Abstract: In this study, precipitated calcium carbonate lime waste (LW) from sugar beet process was recycled as the raw material for the preparation of composite materials. Epoxidized soybean oil (ESO) was used as a co-matrix in 50 wt% with DGEBA type epoxy resin (ER). XRD was used for characterization of composites. Effects of ESO and LW filler amounts on mechanical properties of neat ER were investigated. Modification of ER with ESO remarkably enhanced plasticity of ER.
Abstract: Partially lubricated sliding wear behaviour of a zinc-based alloy reinforced with 10wt% SiC particles has been studied as a function of applied load and solid lubricant particle size and has been compared with that of matrix alloy and conventionally used grey cast iron. The wear tests were conducted at the sliding velocities of 2.1m/sec in various partial lubricated conditions using pin on disc machine as per ASTM G-99-05. Base oil (SAE 20W-40) or mixture of the base oil with 5wt% graphite of particle sizes (7-10 µm) and (100 µm) were used for creating lubricated conditions. The matrix alloy revealed primary dendrites of a and eutectoid a + h and Î phases in the Inter dendritic regions. Similar microstructure has been depicted by the composite with an additional presence of the dispersoid SiC particles. In the case of cast iron, flakes of graphite were observed in the matrix; the latter comprised of (majority of) pearlite and (limited quantity of) ferrite. Results show a large improvement in wear resistance of the zinc-based alloy after reinforcement with SiC particles. The cast iron shows intermediate response between the matrix alloy and composite. The solid lubrication improved the wear resistance and friction behaviour of both the reinforced and base alloy. Moreover, minimum wear rate is obtained in oil+ 5wt % graphite (7-10 µm) lubricated environment for the matrix alloy and composite while for cast iron addition of solid lubricant increases the wear rate and minimum wear rate is obtained in case of oil lubricated environment. The cast iron experienced higher frictional heating than the matrix alloy and composite in all the cases especially at higher load condition. As far as friction coefficient is concerned, a mixed trend of behaviour was noted. The wear rate and frictional heating increased with load while friction coefficient was affected in an opposite manner. Test duration influenced the frictional heating and friction coefficient of the samples in a mixed manner.
Abstract: Shell wastes represent a considerable quantity of byproducts in the shellfish aquaculture. From the viewpoint of ecofriendly and economical disposal, it is highly desirable to convert these residues into high value-added products for industrial applications. So far, the utilization of shell wastes was confined at relatively lower levels, e.g. wastewater decontaminant, soil conditioner, fertilizer constituent, feed additive and liming agent. Shell wastes consist of calcium carbonate and organic matrices, with the former accounting for 95-99% by weight. Being the richest source of biogenic CaCO3, shell wastes are suitable to prepare high purity CaCO3 powders, which have been extensively applied in various industrial products, such as paper, rubber, paints and pharmaceuticals. Furthermore, the shell waste could be further processed to be the filler of polymer composites. This paper presents a study on the potential use of mussel shell waste as biofiller to produce the composite materials with different epoxy matrices, such as bisphenol-A type, CTBN modified and polyurethane modified epoxy resins. Morphology and mechanical properties of shell particles reinforced epoxy composites were evaluated to assess the possibility of using it as a new material. The effects of shell particle content on the mechanical properties of the composites were investigated. It was shown that in all composites, the tensile strength and Young’s modulus values increase with the increase of mussel shell particles content from 10 wt% to 50 wt%, while the elongation at break decreased, compared to pure epoxy resin. The highest Young’s modulus values were determined for bisphenol-A type epoxy composites.
Abstract: The disposal of waste plastics has become a major worldwide environmental problem. Pyrolysis of waste plastics is one of the routes to waste minimization and recycling that has been gaining interest. In pyrolysis, the pyrolysed material is separated into gas, liquid (both are fuel) and solid (char) products. All fractions have utilities and economical value depending upon their characteristics. The first objective of this study is to determine the co-pyrolysis product fractions of waste HDPE- (high density polyethylene) and LDPE (low density polyethylene)-olive pomace (OP) and to determine the qualities of the solid product char. Chars obtained at 700 °C pyrolysis were used in biocomposite preparation as additive. As the second objective, the effects of char on biocomposite quality were investigated. Pyrolysis runs were performed at temperature 700 °C with heating rates of 5 °C/min. Biocomposites were prepared by mixing of chars with bisphenol-F type epoxy resin in various wt%. Biocomposite properties were determined by measuring electrical conductivity, surface hardness, Young’s modulus and tensile strength of the composites. The best electrical conductivity results were obtained with HDPE-OP char. For HDPE-OP char and LDPE-OP char, compared to neat epoxy, the tensile strength values of the composites increased by 102% and 78%, respectively, at 10% char dose. The hardness measurements showed similar results to the tensile tests, since there is a correlation between the hardness and the tensile strength.
Abstract: Nanocomposites based on polypropylene/polyamide 66 (PP/PA66) nanoblends containing organophilic montmorillonite (OMMT) and maleic anhydride grafted polypropylene (PP-g-MAH) were prepared by melt compounding method followed by injection molding. Two different types of nanoclays were used in this work. DELLITE LVF is the untreated nanoclay and DELLITE 67G is the treated one. The morphology of the nanocomposites was studied using the XR diffraction (XRD). The results indicate that the incorporation of treated nanoclay has a significant effect on the impact strength of PP/PA66 nanocomposites. Furthermore, it was found that XRD results revealed the intercalation, exfoliation of nanaclays of nanocomposites.
Abstract: Space Radiation has become one of the major factors in successful long duration space exploration. Exposure to space radiation not only can affect the health of astronauts but also can disrupt or damage materials and electronics. Hazards to materials include degradation of properties, such as, modulus, strength, or glass transition temperature. Electronics may experience single event effects, gate rupture, burnout of field effect transistors and noise. Presently aluminum is the major component in most of the space structures due to its lightweight and good structural properties. However, aluminum is ineffective at blocking space radiation. Therefore, most of the past research involved studying at polymers which contain large amounts of hydrogen. Again, these materials are not structural materials and would require large amounts of material to achieve the structural properties needed. One of the materials to alleviate this problem is polymeric composite materials, which has good structural properties and use polymers that contained large amounts of hydrogen. This paper presents steps involved in fabrication of multi-functional hybrid sandwich panels that can provide beneficial radiation shielding as well as structural strength. Multifunctional hybrid sandwich panels were manufactured using vacuum assisted resin transfer molding process and were subjected to radiation treatment. Study indicates that various nanoparticles including Boron Nano powder, Boron Carbide and Gadolinium nanoparticles can be successfully used to block the space radiation without sacrificing the structural integrity.
Abstract: Composites materials of Poly (vinyl alcohol) (PVA)/Chitosan (CS) have been synthesized and characterized successfully. HNTs have been added to composites to enhance the mechanical and degradation properties by hydrogen bonding interactions, compatibility, and chemical crosslink between HNTs and PVA. PVA/CS/HNTs composites prepared with different concentration ratio. SEM micrographs of composites surface showed that more agglomeration with more chitosan ratio. Mechanical and degradation properties were characterized and the result indicates that Mechanical and degradation of 80%PVA/5%Chitosan/15%HNTs higher than the others PVA/CS/HNTs composites.
Abstract: This study attempts to understand the effect of different UV irradiation methods on the intercalation of LDPE/MMT nanocomposites, and its molecular behavior at certain isothermal crystallization temperature. Three different methods of UV exposure were employed using single composition of LDPE/MMT nanocomposites. All samples were annealed for 5 hours at a crystallization temperature of 100oC. The crystallization temperature was chosen to be at large supercooling temperature to ensure quick and complete crystallization. The raw material of LDPE consisted of two stable monoclinic and orthorhombic phases according to XRD results. The thermal behavior of both phases acted differently when UV exposure method was changed. The monoclinic phase was more dependent on the method used compared to the orthorhombic phase. The intercalation of clay, as well as, the non-isothermal crystallization temperature, has also shown a clear dependency on the type of UV exposure. A third phase that is thermally less stable was also observed. Its respond to UV irradiation was greater since it contains low molecular weight entities which make it more vulnerable to any UV exposure.
Abstract: Effective treatment of ground instability is essential when managing the impacts associated with historic mining. A field trial was undertaken by the Coal Authority to investigate the geotechnical performance and potential use of composite materials comprising resin and fill or stone to safely treat surface collapses, such as crown-holes, associated with shallow mining. Test pits were loosely filled with various granular fill materials. The fill material was injected with commercially available silicate and polyurethane resin foam products. In situ and laboratory testing was undertaken to assess the geotechnical properties of the resultant composite materials. The test pits were subsequently excavated to assess resin permeation. Drilling and resin injection was easiest through clean limestone fill materials. Recycled building waste fill material proved difficult to inject with resin; this material is thus considered unsuitable for use in resin composites. Incomplete resin permeation in several of the test pits created irregular ‘blocks’ of composite. Injected resin foams significantly improve the stiffness and resistance (strength) of the un-compacted fill material. The stiffness of the treated fill material appears to be a function of the stone particle size, its associated compaction characteristics (under loose tipping) and the proportion of resin foam matrix. The type of fill material is more critical than the type of resin to the geotechnical properties of the composite materials. Resin composites can effectively support typical design imposed loads. Compared to other traditional treatment options, such as cement grouting, the use of resin composites is potentially less disruptive, particularly for sites with limited access, and thus likely to achieve significant reinstatement cost savings. The use of resin composites is considered a suitable option for the future treatment of shallow mining collapses.
Abstract: The present study is based on the three-dimensional digital analysis by the finite elements method of the mechanical loading effect on the delamination of unidirectional and multidirectional stratified composites. The aim of this work is the determination of the release energy rate G in mode I and the Von Mises equivalent constraint distribution along the damaged area under the influence of several parameters such as the applied load and the delamination size. The results obtained in this study show that the unidirectional composite laminates have better mechanical resistance one the loading line than the multidirectional composite laminates.
Abstract: The combination of the properties of graphene oxide
(OG) and PVDF homopolymer makes their combined composite
materials as multifunctional systems with great potential. Knowledge
of the molecular structure is essential for better use. In this work, the
degradation of PVDF polymer exposed to gamma irradiation in
oxygen atmosphere in high dose rate has been studied and compared
to degradation of PVDF/OG composites. The samples were irradiated
with a Co-60 source at constant dose rate, with doses ranging from
100 kGy to 1,000 kGy. In FTIR data shown that the formation of
oxidation products was at the both samples with formation of
carbonyl and hydroxyl groups amongst the most prevalent products
in the pure PVDF samples. In the other hand, the composites samples
exhibit less presence of degradation products with predominant
formation of carbonyl groups, these results also seen in the UV-Vis
analysis. The results show that the samples of composites may have
greater resistance to the irradiation process, since they have less
degradation products than pure PVDF samples seen by spectroscopic
techniques.
Abstract: Sisal leaves were subjected to enzymatic retting
method to extract the sisal fibre. A portion of the fibre was pretreated
with alkali (NaOH), and further treated with benzoyl chloride
and silane treatment reagents. Both the treated and untreated Sisal
fibre composites were used to fabricate the composite by hand lay-up
technique using unsaturated polyester resin. Tensile, flexural, water
absorption, density, thickness swelling and chemical resistant tests
were conducted and evaluated on the composites. Results obtained
for all the parameters showed an increase in the treated fibre
compared to untreated fibre. FT-IR spectra results ascertained the
inclusion of benzoyl and silane groups on the fibre surface. Scanning
electron microscopy (SEM) result obtained showed variation in the
morphology of the treated and untreated fibre. Chemical modification
was found to improve adhesion of the fibre to the matrix, as well as
physico-mechanical properties of the composites.
Abstract: The combination of multi–walled carbon nanotubes
(MWCNTs) with polymers offers an attractive route to reinforce the
macromolecular compounds as well as the introduction of new
properties based on morphological modifications or electronic
interactions between the two constituents. As they are only a few
nanometers in dimension, it offers ultra-large interfacial area per
volume between the nano-element and polymer matrix. Nevertheless,
the use of MWCNTs as a rough material in different applications has
been largely limited by their poor processability, insolubility, and
infusibility. Studies concerning the nanofiller reinforced polymer
composites are justified in an attempt to overcome these limitations.
This work presents one preliminary study of MWCNTs dispersion
into the PVDF homopolymer. For preparation, the composite
components were diluted in n,n-dimethylacetamide (DMAc) with
mechanical agitation assistance. After complete dilution, followed by
slow evaporation of the solvent at 60°C, the samples were dried.
Films of about 80 μm were obtained. FTIR and UV-Vis
spectroscopic techniques were used to characterize the
nanocomposites. The appearance of absorption bands in the FTIR
spectra of nanofilled samples, when compared to the spectrum of
pristine PVDF samples, are discussed and compared with the UV-Vis
measurements.
Abstract: This paper investigates the application of metallic
coatings on high fiber volume fraction carbon/epoxy polymer matrix
composites. For the grip of the metallic layer, a method of modifying
the surface of the composite by introducing a mixture of copper and
steel powder (filler powders) which can reduce the impact of thermal
spray particles. The powder was introduced to the surface at the time
of the forming. Arc spray was used to project the zinc coating layer.
The substrate was grit blasted to avoid poor adherence. The porosity, microstructure, and morphology of layers are
characterized by optical microscopy, SEM and image analysis. The
samples were studied also in terms of hardness and erosion resistance.
This investigation did not reveal any visible evidence damage to the
substrates. The hardness of zinc layer was about 25.94 MPa and the
porosity was around (∼6.70%). The erosion test showed that the zinc
coating improves the resistance to erosion. Based on the results
obtained, we can conclude that thermal spraying allows the production
of protective coating on PMC. Zinc coating has been identified as a
compatible material with the substrate. The filler powders layer
protects the substrate from the impact of hot particles and allows
avoiding the rupture of brittle carbon fibers.
Abstract: Nanofibers are defined as fibers with diameters less
than 100 nanometers. In this study, behaviours of activated carbon
nanofiber (ACNF), carbon nanofiber (CNF), polyacrylonitrile/ carbon
nanotube (PAN/CNT), polyvinyl alcohol/nanosilver (PVA/Ag) in
proton exchange membrane (PEM) fuel cells are investigated
experimentally. This material was used as gas diffusion layer (GDL)
in PEM fuel cells. In this study, the electrical conductivities of
nanofiber and nanofiber/nanoparticles have been studied to
understand their effects on PEM fuel cell performance. According to
the experimental results, the maximum electrical conductivity
performance of the fuel cell with nanofiber was found to be at
PVA/Ag (at UConn condition). The electrical conductivities of CNF,
ACNF, PAN/CNT are lower for PEM. The resistance of cell with
PVA/Ag is lower than the resistance of cell with PAN/CNT, ACNF,
CNF.
Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.
Abstract: Lightweight and efficient structures have the aim to
enhance the efficiency of the components in various industries.
Toward this end, composites are one of the most widely used
materials because of durability, high strength and modulus, and low
weight. One type of the advanced composites is grid-stiffened
composite (GSC) structures, which have been extensively considered
in aerospace, automotive, and aircraft industries. They are one of the
top candidates for replacing some of the traditional components,
which are used here. Although there are a good number of published
surveys on the design aspects and fabrication of GSC structures, little
systematic work has been reported on their material modification to
improve their properties, to our knowledge. Matrix modification
using nanoparticles is an effective method to enhance the flexural
properties of the fibrous composites. In the present study, a silanecoupling
agent (3-glycidoxypropyltrimethoxysilane/3-GPTS) was
introduced onto the silica (SiO2) nanoparticle surface and its effects
on the three-point flexural response of isogrid E-glass/epoxy
composites were assessed. Based on the Fourier Transform Infrared
Spectrometer (FTIR) spectra, it was inferred that the 3-GPTS
coupling agent was successfully grafted onto the surface of SiO2
nanoparticles after modification. Flexural test revealed an
improvement of 16%, 14%, and 36% in stiffness, maximum load and
energy absorption of the isogrid specimen filled with 3 wt.% 3-
GPTS/SiO2 compared to the neat one. It would be worth mentioning
that in these structures, considerable energy absorption was observed
after the primary failure related to the load peak. In addition, 3-
GPTMS functionalization had a positive effect on the flexural
behavior of the multiscale isogrid composites. In conclusion, this
study suggests that the addition of modified silica nanoparticles is a
promising method to improve the flexural properties of the gridstiffened
fibrous composite structures.
Abstract: This experimental study consists of a characterization
of epoxy grout where an amount of 2% of graphene nanoplatelets
particles were added to commercial epoxy resin to evaluate their
behavior regarding neat epoxy resin. Compressive tests, tensile tests
and flexural tests were conducted to study the effect of graphene
nanoplatelets on neat epoxy resin. By comparing graphene-based and
neat epoxy grout, there is no significant increase of strength due to
weak interface in the graphene nanoplatelets/epoxy composites.
From this experiment, the tension and flexural strength of graphenebased
epoxy grouts is slightly lower than ones of neat epoxy grout.
Nevertheless, the addition of graphene has produced more consistent
results according to a smaller standard deviation of strength.
Furthermore, the graphene has also improved the ductility of the
grout, hence reducing its brittle behaviour. This shows that the
performance of graphene-based grout is reliably predictable and able
to minimise sudden rupture. This is important since repair design of
damaged pipeline is of deterministic nature.
Abstract: This paper describes the development of new class of
epoxy based rice husk filled jute reinforced composites. Rice husk
flour is added in 0%, 1%, 3%, 5% by weight. Epoxy resin and
triethylenetetramine (T.E.T.A) is used as matrix and hardener
respectively. It investigates the mechanical properties of the
composites and a comparison is done for monolithic jute composite
and the filled ones. The specimens are prepared according to the
ASTM standards and experimentation is carried out using INSTRON
8801. The result shows that with the increase of filler percentage the
tensile properties increases but compressive and flexural properties
decreases.
Abstract: In the present study we have investigated axial
buckling characteristics of nanocomposite beams reinforced by
single-walled carbon nanotubes (SWCNTs). Various types of beam
theories including Euler-Bernoulli beam theory, Timoshenko beam
theory and Reddy beam theory were used to analyze the buckling
behavior of carbon nanotube-reinforced composite beams.
Generalized differential quadrature (GDQ) method was utilized to
discretize the governing differential equations along with four
commonly used boundary conditions. The material properties of the
nanocomposite beams were obtained using molecular dynamic (MD)
simulation corresponding to both short-(10,10) SWCNT and long-
(10,10) SWCNT composites which were embedded by amorphous
polyethylene matrix. Then the results obtained directly from MD
simulations were matched with those calculated by the mixture rule
to extract appropriate values of carbon nanotube efficiency
parameters accounting for the scale-dependent material properties.
The selected numerical results were presented to indicate the
influences of nanotube volume fractions and end supports on the
critical axial buckling loads of nanocomposite beams relevant to
long- and short-nanotube composites.