Abstract: Electrospinning is the most widely utilized method to create nanofibers because of the direct setup, the capacity to mass-deliver consistent nanofibers from different polymers, and the ability to produce ultrathin fibers with controllable diameters. Smooth and much arranged ultrafine Polyacrylonitrile (PAN) nanofibers with diameters going from submicron to nanometer were delivered utilizing Electrospinning technique. PAN powder was used as a precursor to prepare the solution utilized as a part of this process. At the point when the electrostatic repulsion contradicted surface tension, a charged stream of polymer solution was shot out from the head of the spinneret and along these lines ultrathin nonwoven fibers were created. The effect of electrospinning parameter such as applied voltage, feed rate, concentration of polymer solution and tip to collector distance on the morphology of electrospun PAN nanofibers were investigated. The nanofibers were heat treated for carbonization to examine the changes in properties and composition to make for electrical application. Scanning Electron Microscopy (SEM) was performed before and after carbonization to study electrical conductivity and morphological characterization. The SEM images have shown the uniform fiber diameter and no beads formation. The average diameter of the PAN fiber observed 365nm and 280nm for flat plat and rotating drum collector respectively. The four probe strategy was utilized to inspect the electrical conductivity of the nanofibers and the electrical conductivity is significantly improved with increase in oxidation temperature exposed.
Abstract: Nanofibers are defined as fibers with diameters less
than 100 nanometers. In this study, behaviours of activated carbon
nanofiber (ACNF), carbon nanofiber (CNF), polyacrylonitrile/ carbon
nanotube (PAN/CNT), polyvinyl alcohol/nanosilver (PVA/Ag) in
proton exchange membrane (PEM) fuel cells are investigated
experimentally. This material was used as gas diffusion layer (GDL)
in PEM fuel cells. In this study, the electrical conductivities of
nanofiber and nanofiber/nanoparticles have been studied to
understand their effects on PEM fuel cell performance. According to
the experimental results, the maximum electrical conductivity
performance of the fuel cell with nanofiber was found to be at
PVA/Ag (at UConn condition). The electrical conductivities of CNF,
ACNF, PAN/CNT are lower for PEM. The resistance of cell with
PVA/Ag is lower than the resistance of cell with PAN/CNT, ACNF,
CNF.
Abstract: Carbon fibers are fabricated from different materials,
such as special polyacrylonitrile (PAN) fibers, rayon fibers and pitch.
Among these three groups of materials, PAN fibers are the most
widely used precursor for the manufacture of carbon fibers. The
process of fabrication carbon fibers from special PAN fibers includes
two steps; oxidative stabilization at low temperature and
carbonization at high temperatures in an inert atmosphere. Due to the
high price of raw materials (special PAN fibers), carbon fibers are
still expensive.
In the present work the main goal is making carbon fibers from
low price commercial PAN fibers with modified chemical
compositions. The results show that in case of conducting completes
stabilization process, it is possible to produce carbon fibers with
desirable tensile strength from this type of PAN fibers. To this
matter, thermal characteristics of commercial PAN fibers were
investigated and based upon the obtained results, with some changes
in conventional procedure of stabilization in terms of temperature
and time variables; the desirable conditions of complete stabilization
is achieved.
Abstract: In this investigation, types of commercial and special
polyacrylonitrile (PAN) fibers contain sodium 2-methyl-2-
acrylamidopropane sulfonate (SAMPS) and itaconic acid (IA)
comonomers were studied by fourier transform infrared (FT-IR)
spectroscopy. The study of FT-IR spectra of PAN fibers samples
with different comonomers shows that during stabilization of PAN
fibers, the peaks related to C≡N bonds and CH2 are reduced sharply.
These reductions are related to cyclization of nitrile groups and
stabilization procedure. This reduction in PAN fibers contain IA
comonomer is very intense in comparison with PAN fibers contain
SAMPS comonomer. This fact indicates the cycling and stabilization
for sample contain IA comonomer have been conducted more
completely. Therefore the carbon fibers produced from this material
have higher tensile strength due to suitable stabilization.