Abstract: Polymeric composites are being increasingly used as
repair material for repairing critical infrastructures such as building,
bridge, pressure vessel, piping and pipeline. Technique in repairing
damaged pipes is one of the major concerns of pipeline owners.
Considerable researches have been carried out on the repair of
corroded pipes using composite materials. This article attempts a
short review of the subject matter to provide insight into various
techniques used in repairing corroded pipes, focusing on a wide range
of composite repair systems. These systems including pre-cured
layered, flexible wet lay-up, pre-impregnated, split composite sleeve
and flexible tape systems. Both advantages and limitations of these
repair systems were highlighted. Critical technical aspects have been
discussed through the current standards and practices. Research gaps
and future study scopes in achieving more effective design
philosophy are also presented.
Abstract: This experimental study consists of a characterization
of epoxy grout where an amount of 2% of graphene nanoplatelets
particles were added to commercial epoxy resin to evaluate their
behavior regarding neat epoxy resin. Compressive tests, tensile tests
and flexural tests were conducted to study the effect of graphene
nanoplatelets on neat epoxy resin. By comparing graphene-based and
neat epoxy grout, there is no significant increase of strength due to
weak interface in the graphene nanoplatelets/epoxy composites.
From this experiment, the tension and flexural strength of graphenebased
epoxy grouts is slightly lower than ones of neat epoxy grout.
Nevertheless, the addition of graphene has produced more consistent
results according to a smaller standard deviation of strength.
Furthermore, the graphene has also improved the ductility of the
grout, hence reducing its brittle behaviour. This shows that the
performance of graphene-based grout is reliably predictable and able
to minimise sudden rupture. This is important since repair design of
damaged pipeline is of deterministic nature.
Abstract: The main aim of this work is to develop a model of hydrogen sulfide (H2S) separation from natural gas by using membrane separation technology. The model is developed by incorporating three diffusion mechanisms which are Knudsen, viscous and surface diffusion towards membrane selectivity and permeability. The findings from the simulation result shows that the permeability of the gas is dependent toward the pore size of the membrane, operating pressure, operating temperature as well as feed composition. The permeability of methane has the highest value for Poly (1-trimethylsilyl-1-propyne ) PTMSP membrane at pore size of 0.1nm and decreasing toward a minimum peak at pore range 1 to 1.5 nm as pore size increased before it increase again for pore size is greater than 1.5 nm. On the other hand, the permeability of hydrogen sulfide is found to increase almost proportionally with the increase of membrane pore size. Generally, the increase of pressure will increase the permeability of gas since more driving force is provided to the system while increasing of temperature would decrease the permeability due to the surface diffusion drop off effect. A corroboration of the simulation result also showed a good agreement with the experimental data.