Metallic Coating for Carbon Fiber Reinforced Polymer Matrix Composite Substrate

This paper investigates the application of metallic
coatings on high fiber volume fraction carbon/epoxy polymer matrix
composites. For the grip of the metallic layer, a method of modifying
the surface of the composite by introducing a mixture of copper and
steel powder (filler powders) which can reduce the impact of thermal
spray particles. The powder was introduced to the surface at the time
of the forming. Arc spray was used to project the zinc coating layer.
The substrate was grit blasted to avoid poor adherence. The porosity, microstructure, and morphology of layers are
characterized by optical microscopy, SEM and image analysis. The
samples were studied also in terms of hardness and erosion resistance.
This investigation did not reveal any visible evidence damage to the
substrates. The hardness of zinc layer was about 25.94 MPa and the
porosity was around (∼6.70%). The erosion test showed that the zinc
coating improves the resistance to erosion. Based on the results
obtained, we can conclude that thermal spraying allows the production
of protective coating on PMC. Zinc coating has been identified as a
compatible material with the substrate. The filler powders layer
protects the substrate from the impact of hot particles and allows
avoiding the rupture of brittle carbon fibers.

Authors:

• Amine Rezzoug
• Said Abdi
• Nadjet Bouhelal
• Ismail Daoud

Keywords:

• Arc spray
• coating
• composite
• erosion.

References:

[1] T. J. Reinhart, Engineered Materials Handbook Volume 1: Composites,
ASM International, Metals Park, OH USA, 1987.pp. 39-50
[2] M. Ivosevic, R. Knight, S.R. Kalidindi, G.R. Palmese, J.K. Sutter,’’ Solid
particle erosion resistance of thermally sprayed functionally graded
coatings for polymer matrix composites’’ J. Therm. Spray Technol. 14
(2005) 45.
[3] A. Liu, M. Guo, J. Gao, M. Zhao, ‘’Arc sprayed erosion-resistant coating
for carbon fiber reinforced polymer matrix composite substrates’’Surf.
Coat. Technol. 201 (2006) 2696.
[4] F. Robitaille , M. Yandouzi , S. Hind , B. Jodoin, ‘’Metallic coating of
aerospace carbon/epoxy composites by the pulsed gas dynamic spraying
process’’, Surface & Coatings Technology, (2009).
[5] I. Grimberg, K. Soifer, B. Bouaifi, U. Draugelates, B.Z. Weiss, Tungsten
Carbide Coatings Deposited By High-Velocity Oxy-Fuel Spraying On A
Metallized Polymeric Substrate, Surface And Coatings Technology 90
(1997) Page 82-90
[6] K.Miyoshi, J .K. Sutter, R. A. Horan, S. K. Naik, and R. J.
Cupp’’Assessment of Erosion Resistance of Coated Polymer Matrix
Composites for Propulsion Applications’’ NASA/TM—2004-212911
[7] I.Grimberg, K. Soife, B.Bouaifi, U. Draugelates, B. Z. Weiss’’ Tungsten
carbide coatings deposited by high-velocity oxy-fuel spraying on a
metallized polymeric substrate’’ Surface and Coatings
Technology,(1997)
[8] M. Ivosevic, R. Knight, S. R. Kalidindi, G. R. Palmese, J. K. Sutter,’’
Adhesive/cohesive properties of thermally sprayed functionally graded
coatings for polymer matrix composites’’ Journal of Thermal Spray
Technology,(2005) page 45-51
[9] R. Knight, M. Ivosevic, S. Kalinidi, G. Palmese,’’ Optimal Substrate
Preheating Model for Thermal Spray Deposition of Thermosets Onto
Polymer Matrix Composites’’ International Thermal Spray Conference
and Exposition,(2005)
[10] R.Wang, D.Song, W.Liu, X.He,’’E ffect of arc spraying power on the
microstructure and mechanical properties of Zn–Al coating deposited
onto carbon fiber reinforced epoxy composites’’ Applied Surface Science
257 (2010) 203-209
[11] F. Alonso, I. Fagoaga, P. Oregui,’’ Erosion protection of carbon—epoxy
composites by plasma-sprayed coatings’’ Surface and Coatings
Technology,(1991), page 482-488
[12] R. Lupoi, W. O'Neill,’’ Deposition of metallic coatings on polymer
surfaces using cold spray’’ Surface and Coatings Technology,(2010),page
2167-2173
[13] Engineered Materials Handbook Volume 5: Surface Engineering, ASM
International, Catherine M. Cotell, James A. Sprague, and Fred A. Smidt,
Jr, 1994
[14] American Society for Testing and Materials. Standard test method for
vickers hardness of metallic materials. ASTM E92-82 e2; 2003.
[15] H. K. Pulker, W. Haag, M. Buhler, E. Moll, Proc. 5th Int. Conf. on Ion
Plasma Assisted Techniques (Munich), CEP Consultants Ltd.,
Edinburgh,(1985), pp. 209-306.
[16] ASTM, G76 – 13 Standard Test Method forConducting Erosion Tests by
Solid Particle Impingement Using Gas Jets
[17] Standard ASTM E1920-03, Guide for Metallographic Preparation of
ThermalSprayed Coating
[18] Standard ASTM E2109. Standard test methods for determining area
percentageporosity in thermal sprayed coatings.
[19] Bores Cylinder. "Thermal Spray & Surface Engineering." Advanced
Materials & Processes 39 (2007): 1.