Abstract: Nanomaterials have many applications in the field of asphalt paving. Two locally produced nanomaterials were used in the asphalt binder modification. The nanomaterials used are Nanosilica (NS), and Nanoclay (NC). The virgin asphalt binder was characterized by the conventional tests. The bitumen was modified by 3%, 5% and 7% of NS and NC. The penetration index (PI), and the retaining penetration (RP) was calculated based on the results of the penetration and the softening point tests. The results show that the RP becomes 95.35% at 5% NS modified bitumen and reaches 97.56% when bitumen is modified with 3% NC. The results show significant improvement in the bitumen stiffness when modified by the two types of nanomaterials, either fresh or aged (stored).
Abstract: In this study, a form-stable composite Paraffin/Nanoclay (PA-NC) has been prepared by absorbing PA into porous particles of NC to be used for low-temperature latent heat thermal energy storage. The leakage test shows that the maximum mass fraction of PA that can be incorporated in NC without leakage is 60 wt.%. Differential scanning calorimetry (DSC) has been used to measure the thermal properties of the PA and PA-NC both before and after incorporation in plasterboard (PL). The mechanical performance of the samples has been evaluated in flexural mode. The thermal energy storage performance has been studied using a small test chamber (100 mm × 100 mm × 100 mm) made from 10 mm thick PL and measuring the temperatures using thermocouples. The flammability of the PL+PL-NC has been discussed using a cone calorimeter. The results indicate that the form composite PA has good potential for use as thermal energy storage materials in building applications.
Abstract: This study investigated the influence of Cloisite-15A nanoclay on the physical, performance, and mechanical properties of bitumen binder. Cloisite-15A was blended in the bitumen in variegated percentages from 1% to 9% with increment of 2%. The blended bitumen was characterized using penetration, softening point, and dynamic viscosity using rotational viscometer, and compared with unmodified bitumen equally penetration grade 60/70. The rheological parameters were investigated using Dynamic Shear Rheometer (DSR), and mechanical properties were investigated by using Marshall Stability test. The results indicated an increase in softening point, dynamic viscosity and decrease in binder penetration. Rheological properties of bitumen increase complex modulus, decrease phase angle and improve rutting resistances as well. There was significant improvement in Marshall Stability, rather marginal improvement in flow value. The best improvement in the modified binder was obtained with 5% Cloisite-15A nanoclay.
Abstract: The current study aims to investigate the effect of fillers with different geometries and sizes on the interfacial shear properties of PA6 composites with de-sized carbon fiber. The fillers which have been investigated are namely; nano-layer silicates (nanoclay), sub-micro aluminum titanium (ALTi) particles, and multiwall carbon nanotube (MWCNT). By means of X-ray photoelectron spectroscopy (XPS), epoxide group which defined as a sizing agent, has been removed. Sizing removal can reduce the acid parameter of carbon fibers surface promoting bonding strength at the fiber/matrix interface which is a desirable property for the carbon fiber composites. Microdroplet test showed that the interfacial shear strength (IFSS) has been enhanced with the addition of 10wt% ALTi by about 23% comparing with neat PA6. However, with including other types of fillers into PA6, the results did not show enhancement of IFSS.
Abstract: Nanocomposites based on polypropylene/polyamide 66 (PP/PA66) nanoblends containing organophilic montmorillonite (OMMT) and maleic anhydride grafted polypropylene (PP-g-MAH) were prepared by melt compounding method followed by injection molding. Two different types of nanoclays were used in this work. DELLITE LVF is the untreated nanoclay and DELLITE 67G is the treated one. The morphology of the nanocomposites was studied using the XR diffraction (XRD). The results indicate that the incorporation of treated nanoclay has a significant effect on the impact strength of PP/PA66 nanocomposites. Furthermore, it was found that XRD results revealed the intercalation, exfoliation of nanaclays of nanocomposites.
Abstract: E-glass-epoxy laminated composites having different fiber volume fractions (40, 50, 60 and 70) were fabricated with and without the addition of nanoclay. Flexural strength and tensile strength of the composite laminates were determined. It was observed that, with increasing the fiber volume fraction (Vf) of fiber from 40 to 60, the ability of nanoclay to enhance the tensile and flexural strength of E-glass-epoxy composites decreases significantly. At 70Vf, the tensile and flexural strength of the nanoclay reinforced E-glass-epoxy were found to be lowest when compared to the E-glass-epoxy composite made without the addition of nanoclay. Based on the obtained data and microstructure of the tested samples, plausible mechanism for the observed trends has been proposed. The enhanced mechanical properties for nanoclay reinforced E-glass-epoxy composites for 40-60 Vf, due to higher interface toughness coupled with strong interfilament bonding may have ensured the homogeneous load distribution across all the glass fibers. Results in the decrease in mechanical properties at 70Vf, may be due to the inability of the matrix to bind the nanoclay and glass-fibers.
Abstract: This work aims to investigate the structure–property
relationship in ternary nanocomposites consisting of polypropylene
as the matrix, polyamide 66 as the minor phase and treated nanoclay
DELLITE 67G as the reinforcement. All PP/PA66/Nanoclay systems
with polypropylene grafted maleic anhydride PP-g-MAH as a
compatibilizer were prepared via melt compounding and
characterized in terms of nanoclay content. Morphological structure
was investigated by scanning electron microscopy. The rheological
behavior of the nanocomposites was determined by various methods,
viz melt flow index (MFI) and parallel plate rheological
measurements. The PP/PP-g-MAH/PA66 nanocomposites showed a homogeneous
morphology supporting the compatibility improvement between PP,
PA66, and nanoclay. SEM results revealed the formation of
nanocomposites as the nanoclay was intercalated and exfoliated. In
the ternary nanocomposites, the rheological behavior showed that, the
complex viscosity is increased with increasing the nanoclay. The results showed that the use of nanoclay affects the variations
of storage modulus (G′), loss modulus (G″) and the melt elasticity.
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.
Abstract: In situ modified cyclohexanone-formaldehyde resins
were prepared by addition of alendronic acid during resin
preparation. Clay nanocomposites in ketonic resins were achieved by
adding clay into the flask at the beginning of the resin preparation.
The prepared resins were used for the synthesis of fire resistant
polyurethanes foam. Both phosphorous containing modifier
compound alendronic acid and nanoclay increases fire resistance of
the cyclohexanone-formaldehyde resin thus polyurethane produced
from these resins. The effect of the concentrations of alendronic acid
and clay on the fire resistance and physical properties of
polyurethanes was studied.
Abstract: Polyethylene (PE), Polypropylene (PP), Polyethylene
(vinyl acetate) (EVA) and PE-ionomer nanocomposite samples were
prepared by mixing of the polymer with organofilized
montmorillonite fillers Cloisite 93A and Dellite 67G. The amount of
each modified montmorillonite (MMT) was fixed to 5% (w/w). The
twin-screw kneader was used for the compounding of polymer matrix
and chosen nanofillers. The level of MMT exfoliation was studied by
the transmission electron microscopy (TEM) observations. The
mechanical properties of prepared materials were evaluated by
dynamical mechanical analysis at 30°C and by the measurement of
tensile properties (stress and strain at break).
Abstract: The Proton Exchange Membranes (PEM) are largely studied because they operate at low temperatures and they are suitable for mobile applications. However, there are some deficiencies in their operation, mainly those that use ethanol as a hydrogen source, that require a certain attention. Therefore, this research aimed to develop Nafion® composite membranes, mixing clay minerals, kaolin and halloysite to the polymer matrix in order to improve the ethanol molecule retentions and, at the same time, to keep the system’s protonic conductivity. The modified Nafion/Kaolin, Nafion/Halloysite composite membranes were prepared in weight proportion of 0.5, 1.0 and 1.5. The membranes obtained were characterized as to their ethanol permeability, protonic conductivity and water absorption. The composite morphology and structure are characterized by SEM and EDX and the thermal behavior is determined by TGA and DSC. The analysis of the results shows ethanol permeability reduction from 48% to 63%. However, the protonic conductivity results are lower in relation to pure Nafion®. As to the thermal behavior, the Nafion® composite membranes were stable up to a temperature of 325ºC.
Abstract: This work was focused in to study the compatibility, dispersion and exfoliation of modified nanoclays in biodegradable polymers and evaluate its effect on the physical, mechanical and thermal properties on the biodegradable matrix used. The formulations have been developed with polylactic acid (PLA) and organically modified montmorillonite-type commercial nanoclays (Cloisite 15, Cloisite 20, and Cloisite 30B) in the presence of a plasticizer agent, specifically Polyethylene Glycol of low molecular weight. Different compositions were evaluated, in order to identify the influence of each nanoclayin the polymeric matrix. The mixtures were characterized by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (DRX), transmission electron microscopy (TEM) and Tensile Test. These tests have allowed understanding the behavior of each of the mixtures developed.
Abstract: Geophagic and cosmetic clays are among potential nanomaterial which occur naturally and are of various forms. The use of these nanoclays is a common practice in both rural and urban areas mostly due to tradition and medicinal reasons. These naturally occurring materials can be valuable sources of nanomaterial by serving as nanocomposites. The need to ascertain the safety of these materials is the motivation for this research. Physical Characterization based on the hue value and microbiological qualities of the nanoclays were carried out. The Microbial analysis of the clay samples showed considerable contamination with both bacteria and fungi with fungal contaminants taking the lead. This observation may not be unlikely due to the ability of fungi species to survive harsher growth conditions than bacteria. ‘Atike pupa’ showed no bacterial growth. The clay with the largest bacterial count was Calabash chalk (Igbanke), while that with the highest fungal count was ‘Eko grey’. The most commonly isolated bacteria in this study were Clostridium spp. and Corynebacterium spp. while fungi included Aspergillus spp. These results are an indication of the need to subject these clay materials to treatments such as heating before consumption or topical usage thereby ascertaining their safety.
Abstract: In the present work, an attempt has been made to
understand the feasibility of using UHF technique for identification
of any corona discharges/ arcing in insulating material due to water
droplets. The sensors of broadband type are useful for identification
of such discharges. It is realised that arcing initiated by liquid droplet
radiates UHF signals in the entire bandwidth up to 2 GHz. The
frequency content of the UHF signal generated due to corona/arcing
is not much varied in epoxy nanocomposites with different weight
percentage of clay content. The exfoliated/intercalated properties
were analysed through TEM studies. It is realized that corona
initiated discharges are of intermittent process. The hydrophobicity
of the material characterized through contact angle measurement. It
is realized that low Wt % of nanoclay content in epoxy resin reduces
the surface carbonization due to arcing/corona discharges. The results
of the study with gamma irradiated specimen indicates that contact
angle, discharge inception time and evaporation time of the liquid are
much lower than the virgin epoxy nanocomposite material.
Abstract: This study has applied the L16 orthogonal array of the
Taguchi method to determine the optimized polymeric
Nanocomposite asphalt binder. Three control factors are defined as
polypropylene plastomer (PP), styrene-butadiene-styrene elastomer
(SBS) and Nanoclay. Four level of concentration contents are
introduced for prepared asphalt binder samples. all samples were
prepared with 4.5% of bitumen 60/70 content. Compressive strength
tests were carried out for defining the optimized sample via
QUALITEK-4 software. SBS with 3%, PP with 5 % and Nanoclay
with 1.5% of concentrations are defined as the optimized
Nanocomposite asphalt binders. The confirmation compressive
strength and also softening point tests showed that modification of
asphalt binders with this method, improved the compressive strength
and softening points of asphalt binders up to 55%.
Abstract: Toughening of polyamide 6 (PA6)/ Nanoclay (NC) nanocomposites with styrene-ethylene/butadiene-styrene copolymer (SEBS) using maleated styrene-ethylene/butadiene-styrene copolymer (mSEBS)/ as a compatibilizer were investigated by blending them in a co-rotating twin-screw extruder. Response surface method of experimental design was used for optimizing the material and processing parameters. Effect of four factors, including SEBS, mSEBS and NC contents as material variables and order of mixing as a processing factor, on toughness of hybrid nanocomposites were studied. All the prepared samples showed ductile behavior and low temperature Izod impact toughness of some of the hybrid nanocomposites demonstrated 900% improvement compared to the PA6 matrix while the modulus showed maximum enhancement of 20% compared to the pristine PA6 resin.
Abstract: Bionanotechnology deals with nanoscopic interactions between nanostructured materials and biological systems. Polymer nanocomposites with optimized biological activity have attracted great attention. Nanoclay is considered as reinforcing nanofiller in manufacturing of high performance nanocomposites. In current study, organomodified-nanoclay with negatively charged silicate layers was incorporated into biomedical grade silicone rubber. Nanoparticle loading has been tailored to enhance cell behavior. Addition of nanoparticles led to improved mechanical properties of substrate with enhanced strength and stiffness while no toxic effects was observed. Results indicated improved viability and proliferation of cells by addition of nanofillers. The improved mechanical properties of the matrix result in proper cell response through adjustment and arrangement of cytoskeletal fibers. Results can be applied in tissue engineering when enhanced substrates are required for improvement of cell behavior for in vivo applications.