Abstract: Nanomaterials have many applications in the field of asphalt paving. Two locally produced nanomaterials were used in the asphalt binder modification. The nanomaterials used are Nanosilica (NS), and Nanoclay (NC). The virgin asphalt binder was characterized by the conventional tests. The bitumen was modified by 3%, 5% and 7% of NS and NC. The penetration index (PI), and the retaining penetration (RP) was calculated based on the results of the penetration and the softening point tests. The results show that the RP becomes 95.35% at 5% NS modified bitumen and reaches 97.56% when bitumen is modified with 3% NC. The results show significant improvement in the bitumen stiffness when modified by the two types of nanomaterials, either fresh or aged (stored).
Abstract: This paper presents a MEMS/NEMS device for fatigue and fracture characterization of nanomaterials. This device can apply static loads, cyclic loads, and their combinations in nanomechanical experiments. It is based on the electromagnetic force induced between paired parallel wires carrying electrical currents. Using this concept, the actuator and sensor parts of the device were designed and analyzed while considering the practical limitations. Since the PWCC device only uses two wires for actuation part and sensing part, its fabrication process is extremely easier than the available MEMS/NEMS devices. The total gain and phase shift of the MEMS/NEMS device were calculated and investigated. Furthermore, the maximum gain and sensitivity of the MEMS/NEMS device were studied to demonstrate the capability and usability of the device for wide range of nanomaterials samples. This device can be readily integrated into SEM/TEM instruments to provide real time study of the mechanical behaviors of nanomaterials as well as their fatigue and fracture properties, softening or hardening behaviors, and initiation and propagation of nanocracks.
Abstract: The fundamental issue in understanding the origin and
growth mechanism of nanomaterials, from a fundamental unit is a big
challenging problem to the scientists. Recently, an immense attention
is generated to the researchers for prediction of exceptionally stable
atomic cluster units as the building units for future smart materials.
The present study is a systematic investigation on the stability and
electronic properties of a series of bimetallic (semiconductor-alkaline
earth) clusters, viz., BxMg3 (x=1-5) is performed, in search for
exceptional and/ or unusual stable motifs. A very popular hybrid
exchange-correlation functional, B3LYP along with a higher basis
set, viz., 6-31+G[d,p] is employed for this purpose under the density
functional formalism. The magic stability among the concerned
clusters is explained using the jellium model. It is evident from the
present study that the magic stability of B4Mg3
cluster arises due to
the jellium shell closure.
Abstract: We present a gas-liquid microfluidic system as a
reactor to obtain magnetite nanoparticles with an excellent degree of
control regarding their crystalline phase, shape and size. Several
types of microflow approaches were selected to prevent nanomaterial
aggregation and to promote homogenous size distribution. The
selected reactor consists of a mixer stage aided by ultrasound waves
and a reaction stage using a N2-liquid segmented flow to prevent
magnetite oxidation to non-magnetic phases. A milli-fluidic reactor
was developed to increase the production rate where a magnetite
throughput close to 450 mg/h in a continuous fashion was obtained.
Abstract: Co metal supported on SiO2 and Al2O3 catalysts with
a metal loading varied from 30 of 70 wt.% were evaluated for
decomposition of methane to COx free hydrogen and carbon
nanomaterials. The catalytic runs were carried out from 550-800oC
under atmospheric pressure using fixed bed vertical flow reactor. The
fresh and spent catalysts were characterized by BET surface area
analyzer, XRD, SEM, TEM and TG analysis. The data showed that
50% Co/Al2O3 catalyst exhibited remarkable higher activity at 800oC
with respect to H2 production compared to rest of the catalysts.
However, the catalytic activity and durability was greatly declined at
higher temperature. The main reason for the catalytic inhibition of Co
containing SiO2 catalysts is the higher reduction temperature of
Co2SiO4. TEM images illustrate that the carbon materials with
various morphologies, carbon nanofibers (CNFs), helical-shaped
CNFs and branched CNFs depending on the catalyst composition and
reaction temperature were obtained.
Abstract: Magnetic and semiconductor nanomaterials exhibit
novel magnetic and optical properties owing to their unique size and
shape-dependent effects. With shrinking the size down to nanoscale
region, various anomalous properties that normally not present in bulk
start to dominate. Ability in harnessing of these anomalous properties
for the design of various advance electronic devices is strictly
dependent on synthetic strategies. Hence, current research has focused
on developing a rational synthetic control to produce high quality
nanocrystals by using organometallic approach to tune both size and
shape of the nanomaterials. In order to elucidate the growth
mechanism, transmission electron microscopy was employed as a
powerful tool in performing real time-resolved morphologies and
structural characterization of magnetic (Fe3O4) and semiconductor
(ZnO) nanocrystals. The current synthetic approach is found able to
produce nanostructures with well-defined shapes. We have found that
oleic acid is an effective capping ligand in preparing oxide-based
nanostructures without any agglomerations, even at high temperature.
The oleate-based precursors and capping ligands are fatty acid
compounds, which are respectively originated from natural palm oil
with low toxicity. In comparison with other synthetic approaches in
producing nanostructures, current synthetic method offers an effective
route to produce oxide-based nanomaterials with well-defined shapes
and good monodispersity. The nanocystals are well-separated with
each other without any stacking effect. In addition, the as-synthesized
nanopellets are stable in terms of chemically and physically if
compared to those nanomaterials that are previous reported. Further
development and extension of current synthetic strategy are being
pursued to combine both of these materials into nanocomposite form
that will be used as “smart magnetic nanophotocatalyst" for industry
waste water treatment.