Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.