Abstract: Sisal leaves were subjected to enzymatic retting
method to extract the sisal fibre. A portion of the fibre was pretreated
with alkali (NaOH), and further treated with benzoyl chloride
and silane treatment reagents. Both the treated and untreated Sisal
fibre composites were used to fabricate the composite by hand lay-up
technique using unsaturated polyester resin. Tensile, flexural, water
absorption, density, thickness swelling and chemical resistant tests
were conducted and evaluated on the composites. Results obtained
for all the parameters showed an increase in the treated fibre
compared to untreated fibre. FT-IR spectra results ascertained the
inclusion of benzoyl and silane groups on the fibre surface. Scanning
electron microscopy (SEM) result obtained showed variation in the
morphology of the treated and untreated fibre. Chemical modification
was found to improve adhesion of the fibre to the matrix, as well as
physico-mechanical properties of the composites.
Abstract: Emphasis on the advancement of new materials and technology has been there for the past few decades. The global development towards using cheap and durable materials from renewable resources contributes to sustainable development. An experimental investigation of mechanical behaviour of sisal fibre-reinforced concrete is reported for making a suitable building material in terms of reinforcement. Fibre reinforced Composite is one such material, which has reformed the concept of high strength. Sisal fibres are abundantly available in the hot areas. Sisal fibre has emerged as a reinforcing material for concretes, used in civil structures. In this work, properties such as hardness and tensile strength of sisal fibre reinforced cement composites with 6, 12, 18 and 24% by weight of sisal fibres were assessed. Sisal fibre reinforced cement composite slabs with long sisal fibres were manufactured using a cast hand lay up technique. Mechanical response was measured under tension. The high energy absorption capacity of the developed composite system was reflected in high toughness values under tension respectively.