Abstract: Carbon nanotubes (CNTs) are known for having high elastic properties with high surface area that promote them as good candidates for reinforcing polymeric matrices. In composite materials, CNTs lack chemical bonding with the surrounding matrix which decreases the possibility of better stress transfer between the components. In this work, a chemical treatment for activating the surface of the multi-wall carbon nanotubes (MWCNT) was applied and the effect of this functionalization on the elastic properties of the epoxy nanocomposites was studied. Functional amino-groups were added to the surface of the CNTs and it was evaluated to be about 34% of the total weight of the CNTs. Elastic modulus was found to increase by about 40% of the neat epoxy resin at CNTs’ weight fraction of 0.5%. The elastic modulus was found to decrease after reaching a certain concentration of CNTs which was found to be 1% wt. The scanning electron microscopic pictures showed the effect of the CNTs on the crack propagation through the sample by forming stress concentrated spots at the nanocomposite samples.
Abstract: Natural fibers are used in polymer composites to
improve mechanical properties to replace inorganic reinforcing
agents produced by non-renewable resources. The present study
investigates the tensile and flexural behaviors of palm fibers-high
density polyethylene (HDPE) composite as a function of volume
fraction. The surface of the fibers was treated by mercerization
treatments to improve the wetting behavior of the apolar HDPE. The
treatment characterization was obtained by scanning electron
microscopy, X-Ray diffraction and infrared spectroscopy. Results
evidences that a good adhesion interfacial between fibers-matrix
caused an increase strength and modulus flexural as well as tensile
strength in the modified fibers/HDPE composites when compared to
the pure HDPE and untreated fibers reinforced composites.
Abstract: It is an established fact that polymers have several
physical limitations such as low stiffness and low resistance to
impact on loading. Hence, polymers do not usually have requisite
mechanical strength for application in various fields. The
reinforcement by high strength fibers provides the polymer
substantially enhanced mechanical properties and makes them more
suitable for a large number of diverse applications. This research
evaluates the effects of particulate Cow bone and Groundnut shell
additions on the mechanical properties and microstructure of cow
bone and groundnut shell reinforced epoxy composite in order to
assess the possibility of using it as a material for engineering
applications. Cow bone and groundnut shell particles reinforced with
epoxy (CBRPC and GSRPC) was prepared by varying the cow bone
and groundnut shell particles from 0-25 wt% with 5 wt% intervals. A
Hybrid of the Cow bone and Groundnut shell (HGSCB) reinforce
with epoxy was also prepared. The mechanical properties of the
developed composites were investigated. Optical microscopy was
used to examine the microstructure of the composites. The results
revealed that mechanical properties did not increase uniformly with
additions in filler but exhibited maximum properties at specific
percentages of filler additions. From the Microscopic evaluation, it
was discovered that homogeneity decreases with increase in % filler,
this could be due to poor interfacial bonding.
Abstract: This study focuses on a novel method for dispersion
and distribution of reinforcement under high intensive shear stress to
produce metal composites. The polyacrylonitrile (PAN)-based short
carbon fiber (Csf) and Nextel 610 alumina fiber were dispersed under
high intensive shearing at mushy zone in semi-solid of A356 by a
novel method. The bundles and clusters were embedded by
infiltration of slurry into the clusters, thus leading to a uniform
microstructure. The fibers were embedded homogenously into the
aluminum around 576-580°C with around 46% of solid fraction.
Other experiments at 615°C and 568°C which are contained 0% and
90% solid respectively were not successful for dispersion and
infiltration of aluminum into bundles of Csf. The alumina fiber has
been cracked by high shearing load. The morphologies and
crystalline phase were evaluated by SEM and XRD. The adopted
thixo-process effectively improved the adherence and distribution of
Csf into Al that can be developed to produce various composites by
thixomixing.
Abstract: An Australian manufacturer has fabricated an
innovative GFRP sandwich panel made from E-glass fiber skin and a
modified phenolic core for structural applications. Debonding, which
refers to separation of skin from the core material in composite
sandwiches, is one of the most common types of damage in
composites. The presence of debonding is of great concern because it
not only severely affects the stiffness but also modifies the dynamic
behaviour of the structure. Generally it is seen that the majority of
research carried out has been concerned about the delamination of
laminated structures whereas skin-core debonding has received
relatively minor attention. Furthermore it is observed that research
done on composite slabs having multiple skin-core debonding is very
limited. To address this gap, a comprehensive research investigating
dynamic behaviour of composite panels with single and multiple
debonding is presented. The study uses finite-element modelling and
analyses for investigating the influence of debonding on free
vibration behaviour of single and multilayer composite sandwich
panels. A broad parametric investigation has been carried out by
varying debonding locations, debonding sizes and support conditions
of the panels in view of both single and multiple debonding.
Numerical models were developed with Strand7 finite element
package by innovatively selecting the suitable elements to diligently
represent their actual behavior. Three-dimensional finite element
models were employed to simulate the physically real situation as
close as possible, with the use of an experimentally and numerically
validated finite element model. Comparative results and conclusions
based on the analyses are presented. For similar extents and locations
of debonding, the effect of debonding on natural frequencies appears
greatly dependent on the end conditions of the panel, giving greater
decrease in natural frequency when the panels are more restrained.
Some modes are more sensitive to debonding and this sensitivity
seems to be related to their vibration mode shapes. The fundamental
mode seems generally the least sensitive mode to debonding with
respect to the variation in free vibration characteristics. The results
indicate the effectiveness of the developed three dimensional finite
element models in assessing debonding damage in composite
sandwich panels.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: In the present work, the dielectric properties of
Epoxy/MWCNT-muscovite HYBRID and MIXED composites based
on a ratio 30:70 were studied. The multi-wall carbon nanotubes
(MWCNT) were prepared using two methods: (a) MWCNTmuscovite
hybrids were synthesised by chemical vapour deposition
(CVD) and (b) physically mixing muscovite with MWCNT. The
effects of different preparation of the composites and filler loading
were evaluated. It was revealed that the dielectric constants of
HYBRID epoxy composites are slightly higher than MIXED epoxy
composites. It was also indicated that the dielectric constant increased
by increasing the MWCNT filler loading.
Abstract: In the present work, fly ash geopolymer based
composites including polyester (PES) waste were studied. Specimens
of three compositions were prepared: (a) fly ash geopolymer with 5%
PES waste; (b) fly ash geopolymer mortar with 5% PES waste; (c) fly
ash geopolymer mortar with 6.25% PES waste. Compressive and
bending strength measurements, water absorption test and
determination of thermal conductivity coefficient were performed.
The results showed that the addition of sand in a mixture of
geopolymer with 5% PES content led to higher compressive strength,
while it increased water absorption and reduced thermal conductivity
coefficient. The increase of PES addition in geopolymer mortars
resulted in a more dense structure, indicated by the increase of
strength and thermal conductivity and the decrease of water
absorption.
Abstract: Sustainability and eco-friendly requirement of
engineering materials are sort for in recent times, thus giving rise to
the development of bio-composites. However, the natural fibres to
matrix interface interactions remain a key issue in getting the desired
mechanical properties from such composites. Treatment of natural
fibres is essential in improving matrix to filler adhesion, hence
improving its mechanical properties. In this study, investigations
were carried out to determine the effect of sodium hydroxide
treatment on the tensile, flexural, impact and hardness properties of
crushed and uncrushed Luffa cylindrica fibre reinforced recycled low
density polyethylene composites. The LC (Luffa cylindrica) fibres
were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium
hydroxide (NaOH) concentrations for a period of 24 hours under
room temperature conditions. A formulation ratio of 80/20 g (matrix
to reinforcement) was maintained for all developed samples. Analysis
of the results showed that the uncrushed luffa fibre samples gave
better mechanical properties compared with the crushed luffa fibre
samples. The uncrushed luffa fibre composites had a maximum
tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively
corresponding to a young modulus and flexural modulus of 21.08
MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration
respectively. Results obtained in the research showed that NaOH
treatment with the 8% NaOH concentration improved the mechanical
properties of the LC fibre reinforced composites when compared with
other NaOH treatment concentration values.
Abstract: Bio-composites derived from plant fiber and/or bioderived
polymer, are likely more ecofriendly and demonstrate
competitive performance with petroleum based composites. In this
research, the bio phenol-formaldehyde (bio-PF) was used as a matrix
and oil palm empty fruit bunch fiber (EFB) as reinforcement. The
matrix was synthesized via liquefaction and condensation to enhance
the combination of phenol and formaldehyde, during the process.
Then, the bio-PF was mixed with different percentage of EFB (5%,
10%, 15% and 20%) and molded at 180oC. The samples that viewed
under scanning electron microscopy (SEM) showed an excellent
wettability and interaction between EFB and matrix. Samples of 10%
EFB gave the optimum properties of impact and hardness meanwhile
sample 15% of EFB gave the highest reading of flexural modulus
(MOE) and flexural strength (MOR). For thermal stability analysis, it
was found that the weight loss and the activation energy (Ea) of the
bio-composites samples were decreased as the filler content
increased.
Abstract: Burnishing is increasingly used as a finishing operation to improve surface roughness and surface hardness. This can be achieved by applying a hard ball or roller onto metallic surfaces under pressure, in order to achieve many advantages in the metallic surface. In the present work, the feed rate, speed and force have been considered as the basic burnishing parameters to study the surface roughness and surface hardness of metallic matrix composites. The considered metal matrix composites were made from Aluminum-Magnesium-Graphite with five different weight percentage of graphite. Both effects of burnishing parameters mentioned above and the graphite percentage on the surface hardness and surface roughness of the metallic matrix composites were studied. The results of this investigation showed that the surface hardness of the metallic composites increases with the increase of the burnishing force and decreases with the increase in the burnishing feed rate and burnishing speed. The surface roughness of the metallic composites decreases with the increasing of the burnishing force, feed rate, and speed to certain values, then it starts to increase. On the other hand, the increase in the weight percentage of the graphite in the considered composites causes a decrease in the surface hardness and an increase in the surface roughness.
Abstract: Replacement of plastics used in the food industry
seems to be a serious issue to overcome mainly the environmental
problems in recent years. This study investigates the hydrophilicity
and permeability properties of starch biopolymer which ethylene
vinyl alcohol (EVOH) (0-10%) and nanocrystalline cellulose (NCC)
(1-15%) were used to enhance its properties. Starch -EVOH
nanocomposites were prepared by casting method in different
formulations. NCC production by acid hydrolysis was confirmed by
scanning electron microscopy. Solubility, water vapor permeability,
water vapor transmission rate and moisture absorbance were
measured on each of the nanocomposites. The results were analyzed
by SAS software. The lowest moisture absorbance was measured in
pure starch nanocomposite containing 8% NCC. The lowest
permeability to water vapor belongs to starch nanocomposite
containing 8% NCC and the sample containing 7.8% EVOH and 13%
NCC. Also the lowest solubility was observed in the composite
contains the highest amount of EVOH. Applied Process resulted in
production of bio films which have good resistance to water vapor
permeability and solubility in water. The use of NCC and EVOH
leads to reduced moisture absorbance property of the biofilms.
Abstract: PVC foam-fly ash composites (PVC-FA) are
characterized for their structural, morphological, mechanical and
thermal properties. The tensile strength of the composites increased
modestly with higher fly ash loading, while there was a significant
increase in the elastic modulus for the same composites. On the other
hand, a decrease in elongation at UTS was observed upon increasing
fly ash content due to increased rigidity of the composites. Similarly,
the flexural modulus increased as the fly ash loading increased,
where the composites containing 25 phr fly ash showed the highest
flexural strength. Thermal properties of PVC-fly ash composites were
determined by Thermo Gravimetric Analysis (TGA). The
microstructural properties were studied by Scanning Electron
Microscopy (SEM). SEM results confirm that fly ash particles were
mechanically interlocked in PVC matrix with good interfacial
interaction with the matrix. Particle agglomeration and debonding
was observed in samples containing higher amounts of fly ash.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: Aluminum hybrid reinforcement technology is a
response to the dynamic ever increasing service requirements of such
industries as transportation, aerospace, automobile, marine, etc. It is
unique in that it offers a platform of almost unending combinations of
materials to produce various hybrid composites. This article reviews
the studies carried out on various combinations of aluminum hybrid
composite and the effects on mechanical, physical and chemical
properties. It is observed that the extent of enhancement of these
properties of hybrid composites is strongly dependent on the nature
of the reinforcement, its hardness, particle size, volume fraction,
uniformity of dispersion within the matrix and the method of hybrid
production.
Abstract: The influence of three different types of halloysite
nanotubes (HNTs) with different dimensions, namely as camel lake
(CLA), Jarrahdale (JA) and Matauri Bay (MB), on their reinforcing
ability of ethylene propylene dine monomer (EPDM) were
investigated by varying the HNTs loading (from 0-15 phr).
Mechanical properties of the nanocomposites improved with addition
of all three HNTs, but CLA based nanocomposites exhibited a
significant enhancement compared to the other HNTs. For instance,
tensile properties of EPDM nanocomposites increased by 120%,
256% and 340% for MB, JA and CLA, respectively, with addition of
15 phr of HNTs. This could be due to the higher aspect ratio and
higher surface area of CLA compared to others. Scanning electron
microscopy (SEM) of nanocomposites at 15 phr of HNT loadings
showed low amounts of pulled-out nanotubes which confirmed the
presence of more embedded nanotubes inside the EPDM matrix, as
well as aggregates within the fracture surface of EPDM/HNT
nanocomposites
Abstract: Three dimensional non-Interlaced carbon fibre
reinforced silicon carbide (3-D-Cf/SiC) composites with pyrocarbon
interphase were fabricated using isothermal chemical vapor
infiltration (ICVI) combined with polymer impregnation pyrolysis
(PIP) process. Polysilazane (PSZ) is used as a preceramic polymer to
obtain silicon carbide matrix. Thermo gravimetric analysis (TGA),
Infrared spectroscopic analysis (IR) and X-ray diffraction (XRD)
analysis were carried out on PSZ pyrolysed at different temperatures
to understand the pyrolysis and obtaining the optimum pyrolysing
condition to yield β-SiC phase. The density of the composites was
1.94 g cm-3 after the 3-D carbon preform was SiC infiltrated for 280 h
with one intermediate polysilazane pre-ceramic PIP process.
Mechanical properties of the composite materials were investigated
under tensile, flexural, shear and impact loading. The values of
tensile strength were 200 MPa at room temperature (RT) and 195
MPa at 500°C in air. The average RT flexural strength was 243 MPa.
The lower flexural strength of these composites is because of the
porosity. The fracture toughness obtained from single edge notched
beam (SENB) technique was 39 MPa.m1/2. The work of fracture
obtained from the load-displacement curve of SENB test was 22.8
kJ.m-2. The composites exhibited excellent impact resistance and the
dynamic fracture toughness of 44.8 kJ.m-2 is achieved as determined
from instrumented Charpy impact test. The shear strength of the
composite was 93 MPa, which is significantly higher compared 2-D
Cf/SiC composites. Microstructure evaluation of fracture surfaces
revealed the signatures of fracture processes and showed good
support for the higher toughness obtained.
Abstract: In this study was performed in situ consolidation of polypropylene matrix/glass reinforced roving by combining heating systems and roll pressing. The commingled roving during hoop winding was winded on a cylindrical mandrel. The work also presents the advances made in the processing of these materials into composites by conventional technique filament winding. Experimental studies were performed with changing parameters – temperature, pressure and speed. Finally, it describes the investigation of the optimal processing conditions that maximize the mechanical properties of the composites. These properties are good enough for composites to be used as engineering materials in many structural applications.
Abstract: The main advantage of multidirectionally reinforced composites is the freedom to orient selected fiber types and hence derives the benefits of varying fibre volume fractions and there by accommodate the design loads of the final structure of composites. This technology provides the means to produce tailored composites with desired properties. Due to the high level of fibre integrity with through thickness reinforcement those composites are expected to exhibit superior load bearing characteristics with capability to carry load even after noticeable and apparent fracture. However, a survey of published literature indicates inadequacy in the design and test data base for the complete characterization of the multidirectional composites. In this paper the research objective is focused on the development and testing of 4-D orthogonal composites with different preform configurations and resin systems. A preform is the skeleton 4D reinforced composite other than the matrix. In 4-D performs fibre bundles are oriented in three directions at 1200 with respect to each other and they are on orthogonal plane with the fibre in 4th direction. This paper addresses the various types of 4-D composite manufacturing processes and the mechanical test methods followed for the material characterization. A composite analysis is also made, experiments on course and fine woven preforms are conducted and the findings of test results are discussed in this paper. The interpretations of the test results reveal several useful and interesting features. This should pave the way for more widespread use of the perform configurations for allied applications.
Abstract: The outstanding mechanical properties of Carbon
nanotubes (CNTs) have generated great interest for their potential as
reinforcements in high performance cementitious composites. The
main challenge in research is the proper dispersion of carbon
nanotubes in the cement matrix. The present work discusses the role
of dispersion of multiwalled carbon nanotubes (MWCNTs) on the
compressive strength characteristics of hydrated Portland IS 1489
cement paste. Cement-MWCNT composites with different mixing
techniques were prepared by adding 0.2% (by weight) of MWCNTs
to Portland IS 1489 cement. Rectangle specimens of size
approximately 40mm × 40mm ×160mm were prepared and curing of
samples was done for 7, 14, 28 and 35days. An appreciable increase
in compressive strength with both techniques; mixture of MWCNTs
with cement in powder form and mixture of MWCNTs with cement
in hydrated form 7 to 28 days of curing time for all the samples was
observed.