Abstract: The introduction of degradable plastic materials into
agricultural sectors has represented a promising alternative to
promote green agriculture and environmental friendly of modern
farming practices. Major challenges of developing degradable
agricultural films are to identify the most feasible types of
degradation mechanisms, composition of degradable polymers and
related processing techniques. The incorrect choice of degradable
mechanisms to be applied during the degradation process will cause
premature losses of mechanical performance and strength. In order to
achieve controlled process of agricultural film degradation, the
compositions of degradable agricultural film also important in order
to stimulate degradation reaction at required interval of time and to
achieve sustainability of the modern agricultural practices. A set of
photodegradable polyethylene based agricultural film was developed
and produced, following the selective optimization of processing
parameters of the agricultural film manufacturing system. Example of
agricultural films application for oil palm seedlings cultivation is
presented.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.