The Effect of Size, Thickness, and Type of the Bonding Interlayer on Bullet Proof Glass as per EN 1063

This investigation presents preparation of sample and  analysis of results of ballistic impact test as per EN 1063 on the size,  thickness, number, position, and type of the bonding interlayer  Polyvinyl Butyral, Poly Carbonate and Poly Urethane on bullet proof  glass. It was observed that impact energy absorbed by bullet proof  glass increases with the increase of the total thickness from 33mm to  42mm to 51mm for all the three samples respectively. Absorption  impact energy is greater for samples with more number of bonding  interlayers than with the number of glass layers for uniform increase  in total sample thickness. There is no effect on the absorption impact  energy with the change in position of the bonding interlayer. 

Role of Dispersion of Multiwalled Carbon Nanotubes on Compressive Strength of Cement Paste

The outstanding mechanical properties of Carbon  nanotubes (CNTs) have generated great interest for their potential as  reinforcements in high performance cementitious composites. The  main challenge in research is the proper dispersion of carbon  nanotubes in the cement matrix. The present work discusses the role  of dispersion of multiwalled carbon nanotubes (MWCNTs) on the  compressive strength characteristics of hydrated Portland IS 1489  cement paste. Cement-MWCNT composites with different mixing  techniques were prepared by adding 0.2% (by weight) of MWCNTs  to Portland IS 1489 cement. Rectangle specimens of size  approximately 40mm × 40mm ×160mm were prepared and curing of  samples was done for 7, 14, 28 and 35days. An appreciable increase  in compressive strength with both techniques; mixture of MWCNTs  with cement in powder form and mixture of MWCNTs with cement  in hydrated form 7 to 28 days of curing time for all the samples was  observed.