Abstract: This paper investigates multiple factors that impact the formation of geopolymers and their compressive strength to be utilized in construction as an environmentally-friendly material. Bentonite and Kaolinite were thermally calcinated at 750 °C to obtain Metabentonite and Metakaolinite with higher reactivity. Both source materials were activated using a solution of sodium hydroxide (NaOH). Thereafter, samples were cured at different temperatures. The samples were analyzed chemically using a host of spectroscopic techniques. The bulk density and compressive strength of the produced geopolymer pastes were studied. Findings indicate that the ratio of NaOH solution to source material affects the compressive strength, being optimal at 0.54. Moreover, controlled heat curing was proven effective to improve compressive strength. The existence of characteristic Fourier Transform Infrared Spectroscopy (FTIR) peaks at approximately 1020 cm-1 and 460 cm-1 which correspond to the asymmetric stretching vibration of Si-O-T and bending vibration of Si-O-Si, hence, confirming the formation of the target geopolymer.
Abstract: Geopolymer mortar is produced by alkaline activation of pozzolanic materials such as fly ground granulated blast-furnace slag (GGBFS) and fly ash (FA). Its unique reaction pathway facilitates rapid strength development in comparison with hydration of ordinary Portland cement (OPC). Geopolymer can be fabricated using various types and dosages of alkali-activator, which effectively gives a wider control over the performance of the final product. The present study investigates the effect of types of precursors and curing conditions on the fresh state and strength development characteristics of geopolymers, thereby comparatively exploring the effect of precursors from various sources of origin. The obtained result showed that the setting time and strength development of the specimens with the identical mix proportion but different precursors displayed significant variations.
Abstract: Fly ash (FA) thanks to the significant presence of SiO2
and Al2O3 as the main components is a potential raw material for
geopolymers production. Mechanical activation is a method for
improving FA reactivity and also the porosity of final mixture; those
parameters can be analysed through sorption properties. They have
direct impact on the durability of fly ash based geopolymer mortars.
In the paper, effect of FA fineness on sorption properties of
geopolymers based on sodium silicate, as well as relationship
between fly ash fineness and apparent density, compressive and
flexural strength of geopolymers are presented. The best results in the
evaluated area reached the sample H1, which contents the highest
portion of particle under 20μm (100% of GFA). The interdependence
of individual tested properties was confirmed for geopolymer
mixtures corresponding to those in the cement based mixtures: higher
is portion of fine particles < 20μm, higher is strength, density and
lower are sorption properties. The compressive strength as well as
sorption parameters of the geopolymer can be reasonably controlled
by grinding process and also ensured by the higher share of fine
particle (to 20μm) in total mass of the material.
Abstract: In the present work, fly ash geopolymer based
composites including polyester (PES) waste were studied. Specimens
of three compositions were prepared: (a) fly ash geopolymer with 5%
PES waste; (b) fly ash geopolymer mortar with 5% PES waste; (c) fly
ash geopolymer mortar with 6.25% PES waste. Compressive and
bending strength measurements, water absorption test and
determination of thermal conductivity coefficient were performed.
The results showed that the addition of sand in a mixture of
geopolymer with 5% PES content led to higher compressive strength,
while it increased water absorption and reduced thermal conductivity
coefficient. The increase of PES addition in geopolymer mortars
resulted in a more dense structure, indicated by the increase of
strength and thermal conductivity and the decrease of water
absorption.
Abstract: This paper presents results of an experimental study performed to investigate effect of incorporating silica fume on physico-mechanical properties and durability of resulting fly ash geopolymers. Geopolymer specimens were prepared by activating fly ash incorporated with additional silica fume in the range of 2.5% to 5%, with a mixture of sodium hydroxide and sodium silicate solution having Na2O content of 8%. For studying durability, 10% magnesium sulphate solution was used to immerse the specimens up to a period of 15 weeks during which visual observation, weight changes and strength changes were monitored regularly. Addition of silica fume lowers performance of geopolymer pastes. However, in mortars, addition of silica fume significantly enhanced physico-mechanical properties and durability.
Abstract: The present paper reports results of an experimental
program conducted to study performance of fly ash based
geopolymer pastes at elevated temperature. Three series of
geopolymer pastes differing in Na2O content (8.5%, 10% and 11.5%)
were manufactured by activating low calcium fly ash with a mixture
of sodium hydroxide and sodium silicate solution. The paste
specimens were subjected to temperatures as high as 900oC and the
behaviour at elevated temperatures were investigated on the basis of
physical appearance, weight losses, residual strength, shrinkage
measurements and sorptivity tests at different temperatures. Scanning
electron microscopy along with EDX and XRD tests were also
conducted to examine microstructure and mineralogical changes
during the thermal exposure. Specimens which were initially grey
turned reddish accompanied by appearance of small cracks as the
temperature increased to 900oC. Loss of weight was more in
specimens manufactured with highest Na2O content. Geopolymer
paste specimen containing minimum Na2O performed better than
those with higher Na2O content in terms of residual compressive
strength.