Abstract: This paper presents results of an experimental study performed to investigate effect of incorporating silica fume on physico-mechanical properties and durability of resulting fly ash geopolymers. Geopolymer specimens were prepared by activating fly ash incorporated with additional silica fume in the range of 2.5% to 5%, with a mixture of sodium hydroxide and sodium silicate solution having Na2O content of 8%. For studying durability, 10% magnesium sulphate solution was used to immerse the specimens up to a period of 15 weeks during which visual observation, weight changes and strength changes were monitored regularly. Addition of silica fume lowers performance of geopolymer pastes. However, in mortars, addition of silica fume significantly enhanced physico-mechanical properties and durability.
Abstract: This paper presents the findings of an
experimental investigation to study the effect of alkali content
in geopolymer mortar specimens exposed to sulphuric acid.
Geopolymer mortar specimens were manufactured from Class F fly
ash by activation with a mixture of sodium hydroxide and sodium
silicate solution containing 5% to 8% Na2O. Durability of specimens
were assessed by immersing them in 10% sulphuric acid solution and
periodically monitoring surface deterioration and depth of
dealkalization, changes in weight and residual compressive strength
over a period of 24 weeks. Microstructural changes in the specimens
were studied with Scanning electron microscopy (SEM) and EDAX.
Alkali content in the activator solution significantly affects the
durability of fly ash based geopolymer mortars in sulphuric acid.
Specimens manufactured with higher alkali content performed better
than those manufactured with lower alkali content. After 24 weeks in
sulphuric acid, specimen with 8% alkali still recorded a residual
strength as high as 55%.