Abstract: Nanofibers are defined as fibers with diameters less
than 100 nanometers. In this study, behaviours of activated carbon
nanofiber (ACNF), carbon nanofiber (CNF), polyacrylonitrile/ carbon
nanotube (PAN/CNT), polyvinyl alcohol/nanosilver (PVA/Ag) in
proton exchange membrane (PEM) fuel cells are investigated
experimentally. This material was used as gas diffusion layer (GDL)
in PEM fuel cells. In this study, the electrical conductivities of
nanofiber and nanofiber/nanoparticles have been studied to
understand their effects on PEM fuel cell performance. According to
the experimental results, the maximum electrical conductivity
performance of the fuel cell with nanofiber was found to be at
PVA/Ag (at UConn condition). The electrical conductivities of CNF,
ACNF, PAN/CNT are lower for PEM. The resistance of cell with
PVA/Ag is lower than the resistance of cell with PAN/CNT, ACNF,
CNF.
Abstract: In this experimental study, performance of a counter
flow Ranque-Hilsch vortex tube (RHVT) with threads cut on its inner
surface was investigated experimentally (pitch is 1 and 2 mm). The
inner diameter of the vortex tube used was D=9 mm and the ratio of
the tube’s length to diameter was L/D=12. The experimental system
was a thermodynamic open system. Flow was controlled by a valve
on the hot outlet side, where the valve was changed from a nearly
closed position to its nearly open position. Fraction of cold flow (ξ) =
0.1-0.9, was determined under 300 and 350 kPa pressurized air. All
experimental data were compared with each other, the maximum
heating performance of the RHVT system was found to be 38.2 oC
and the maximum cooling performance of the RHVT in this study
was found to be -30.9 oC at pitch 1 mm.