Abstract: We present a gas-liquid microfluidic system as a
reactor to obtain magnetite nanoparticles with an excellent degree of
control regarding their crystalline phase, shape and size. Several
types of microflow approaches were selected to prevent nanomaterial
aggregation and to promote homogenous size distribution. The
selected reactor consists of a mixer stage aided by ultrasound waves
and a reaction stage using a N2-liquid segmented flow to prevent
magnetite oxidation to non-magnetic phases. A milli-fluidic reactor
was developed to increase the production rate where a magnetite
throughput close to 450 mg/h in a continuous fashion was obtained.
Abstract: This study focuses on a novel method for dispersion
and distribution of reinforcement under high intensive shear stress to
produce metal composites. The polyacrylonitrile (PAN)-based short
carbon fiber (Csf) and Nextel 610 alumina fiber were dispersed under
high intensive shearing at mushy zone in semi-solid of A356 by a
novel method. The bundles and clusters were embedded by
infiltration of slurry into the clusters, thus leading to a uniform
microstructure. The fibers were embedded homogenously into the
aluminum around 576-580°C with around 46% of solid fraction.
Other experiments at 615°C and 568°C which are contained 0% and
90% solid respectively were not successful for dispersion and
infiltration of aluminum into bundles of Csf. The alumina fiber has
been cracked by high shearing load. The morphologies and
crystalline phase were evaluated by SEM and XRD. The adopted
thixo-process effectively improved the adherence and distribution of
Csf into Al that can be developed to produce various composites by
thixomixing.
Abstract: In contrast with literal meaning of nano, researchers
have been achieved mega adventures in this area and every day more
nanomaterials are being introduced to the market. After long time
application of fossil-based plastics, nowadays accumulation of their
waste seems to be a big problem to the environment. On the other
hand, mankind has more attention to safety and living environment.
Replacing common plastic packaging materials with degradable ones
that degrade faster and convert to non-dangerous components like
water and carbon dioxide have more attractions; these new materials
are based on renewable and inexpensive sources of starch and
cellulose. However, the functional properties of them do not suitable
for packaging. At this point, nanotechnology has an important role.
Utilizing of nanomaterials in polymer structure will improve
mechanical and physical properties of them; nanocrystalline cellulose
(NCC) has this ability. This work has employed a chemical method to
produce NCC and starch bio nanocomposite containing NCC. X-Ray
Diffraction technique has characterized the obtained materials.
Results showed that applied method is a suitable one as well as
applicable one to NCC production.
Abstract: Dielectric ceramic samples in the BaO-Re2O3-TiO2
ternary system were synthesized with structural formula Ba2-
xRe4+2x/3Ti8O24 where Re= rare earth metal and Re= Sm and La where
x varies from 0.0 to 0.6 with step size 0.1. Polycrystalline samples
were prepared by the conventional solid state reaction technique. The
dielectric, electrical and impedance analysis of all the samples in the
frequency range 1KHz- 1MHz at room temperature (25°C) have been
done to get the understanding of electrical conduction and dielectric
relaxation and their correlation. Dielectric response of the samples at
lower frequencies shows dielectric dispersion while at higher
frequencies it shows dielectric relaxation. The ac conductivity is well
fitted by the Jonscher law. The spectroscopic data in the impedance
plane confirms the existence of grain contribution to the relaxation.
All the properties are found out to be function of frequency as well as
the amount of substitution.
Abstract: The effect of N2 pretreatment on the catalytic activity
of tungsten-based catalysts was investigated in the metathesis of
ethylene and trans-2-butene at 450oC and atmospheric pressure. The
presence of tungsten active species was confirmed by UV-Vis and
Raman spectroscopy. Compared to the WO3-based catalysts treated
in air, higher amount of WO4 2-tetrahedral species and lower amount
of WO3 crystalline species were observed on the N2-treated ones.
These contribute to the higher conversion of 2-butene and propylene
selectivity during 10 h time-on-stream. Moreover, N2 treatment led to
lower amount of coke formation as revealed by TPO of the spent
catalysts.
Abstract: A chromium-loaded ash originating from incineration of tannery sludge under anoxic conditions was mixed with low grade soda-lime glass powder coming from commercial glass bottles. The relative weight proportions of ash over glass powder tested were 30/70, 40/60 and 50/50. The solid mixtures, formed in green state compacts, were sintered at the temperature range of 800o C up to 1200o C. The resulting products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDXS) and micro-indentation. The above methods were employed to characterize the various phases, microstructure and hardness of the produced materials. Thermal treatment at 800o C and 1000o C produced opaque ceramic products composed of a variety of chromium-containing and chromium-free crystalline phases. Thermal treatment at 1200o C gave rise to composite products, where only chromium-containing crystalline phases were detected. Hardness results suggest that specific products are serious candidates for structural applications.
Abstract: It is well known that in recent years magnetic
materials have received increased attention due to their properties.
For this reason a significant number of patents that were published
during the last decade are oriented towards synthesis and study of
such materials. The aim of this work is to create and study ferrite
nanocrystalline materials with spinel structure, using sol-gel
technology with participation of auto-combustion. This method is
perspective in that it is a cheap and low-temperature technique that
allows for the fine control on the product’s chemical composition.
Abstract: A nanocrystalline thin film of ZnSe was successfully
electrodeposited on copper substrate using a non-aqueous solution
and subsequently annealed in air at 400°C. XRD analysis indicates
the polycrystalline deposit of (111) plane in both the cases. The
sharpness of the peak increases due to annealing of the film and
average grain size increases to 20 nm to 27nm. SEM photograph
indicate that grains are uniform and densely distributed over the
surface. Annealing increases the average grain size by 20%. The EDS
spectroscopy shows the ratio of Zn & Se is 1.1 in case of annealed
film. AFM analysis indicates the average roughness of the film
reduces from 181nm to 165nm due to annealing of the film. The
bandgap also decreases from 2.71eV to 2.62eV.
Abstract: Thin ZnO films are deposited on glass substrates via
sol–gel method and dip-coating. The films are prepared from zinc
acetate dehydrate as a starting reagent. After that the as-prepared
ZnO sol is aged for different periods (0, 1, 3, 5, 10, 15 and 30 days).
Nanocrystalline thin films are deposited from various sols. The
effect ZnO sols aging time on the structural and photocatalytic
properties of the films is studied. The films surface is studied by
Scanning Electron Microscopy. The effect of the aging time of the
starting solution is studied in the photocatalytic degradation of
Reactive Black 5 (RB5) by UV-vis spectroscopy. The experiments
are conducted upon UV-light illumination and in complete darkness.
The variation of the absorption spectra shows the degradation of RB5
dissolved in water, as a result of the reaction, occurring on the surface
of the films and promoted by UV irradiation. The initial
concentrations of dye (5, 10 and 20 ppm) and the effect of the aging
time are varied during the experiments. The results show, that the
increasing aging time of starting solution with respect to ZnO
generally promotes photocatalytic activity. The thin films obtained
from ZnO sol, which is aged 30 days have best photocatalytic
degradation of the dye (97,22%) in comparison with the freshly
prepared ones (65,92%). The samples and photocatalytic
experimental results are reproducible. Nevertheless, all films exhibit
a substantial activity in both UV light and darkness, which is
promising for the development of new ZnO photocatalysts by sol-gel
method.
Abstract: The current study investigated the influence of milling
time and ball-to-powder (BPR) weight ratio on the microstructural
constituents and mechanical properties of bulk nanocrystalline Al;
Al-10%Cu; and Al-10%Cu-5%Ti alloys. Powder consolidation was
carried out using a high frequency induction heat sintering where the
processed metal powders were sintered into a dense and strong bulk
material. The powders and the bulk samples were characterized using
XRD and FEGSEM techniques. The mechanical properties were
evaluated at various temperatures of 25°C, 100°C, 200°C, 300°C and
400°C to study the thermal stability of the processed alloys. The
processed bulk nanocrystalline alloys displayed extremely high
hardness values even at elevated temperatures. The Al-10%Cu-5%Ti
alloy displayed the highest hardness values at room and elevated
temperatures which are related to the presence of Ti-containing
phases such as Al3Ti and AlCu2Ti. These phases are thermally stable
and retain the high hardness values at elevated temperatures up to
400ºC.
Abstract: Replacement of plastics used in the food industry
seems to be a serious issue to overcome mainly the environmental
problems in recent years. This study investigates the hydrophilicity
and permeability properties of starch biopolymer which ethylene
vinyl alcohol (EVOH) (0-10%) and nanocrystalline cellulose (NCC)
(1-15%) were used to enhance its properties. Starch -EVOH
nanocomposites were prepared by casting method in different
formulations. NCC production by acid hydrolysis was confirmed by
scanning electron microscopy. Solubility, water vapor permeability,
water vapor transmission rate and moisture absorbance were
measured on each of the nanocomposites. The results were analyzed
by SAS software. The lowest moisture absorbance was measured in
pure starch nanocomposite containing 8% NCC. The lowest
permeability to water vapor belongs to starch nanocomposite
containing 8% NCC and the sample containing 7.8% EVOH and 13%
NCC. Also the lowest solubility was observed in the composite
contains the highest amount of EVOH. Applied Process resulted in
production of bio films which have good resistance to water vapor
permeability and solubility in water. The use of NCC and EVOH
leads to reduced moisture absorbance property of the biofilms.
Abstract: TiO2 thin films have been prepared by the sol-gel dipcoating
technique in order to elaborate antireflective thin films for
monocrystalline silicon (mono-Si). The titanium isopropoxyde was
chosen as a precursor with hydrochloric acid as a catalyser for
preparing a stable solution. The optical properties have been tailored
with varying the solution concentration, the withdrawn speed, and the
heat-treatment. We showed that using a TiO2 single layer with 64.5
nm in thickness, heat-treated at 450°C or 300°C reduces the mono-Si
reflection at a level lower than 3% over the broadband spectral
domains [669-834] nm and [786-1006] nm respectively. Those latter
performances are similar to the ones obtained with double layers of
low and high refractive index glasses respectively.
Abstract: Nanocrystalline powders of the lead-free piezoelectric
material, tantalum-substituted potassium sodium niobate
(K0.5Na0.5)(Nb0.9Ta0.1)O3 (KNNT), were produced using a Retsch
PM100 planetary ball mill by setting the milling time to 15h, 20h,
25h, 30h, 35h and 40h, at a fixed speed of 250rpm. The average
particle size of the milled powders was found to decrease from 12nm
to 3nm as the milling time increases from 15h to 25h, which is in
agreement with the existing theoretical model. An anomalous
increase to 98nm and then a drop to 3nm in the particle size were
observed as the milling time further increases to 30h and 40h
respectively. Various sizes of these starting KNNT powders were
used to investigate the effect of milling time on the microstructure,
dielectric properties, phase transitions and piezoelectric properties of
the resulting KNNT ceramics. The particle size of starting KNNT
was somewhat proportional to the grain size. As the milling time
increases from 15h to 25h, the resulting ceramics exhibit
enhancement in the values of relative density from 94.8% to 95.8%,
room temperature dielectric constant (εRT) from 878 to 1213, and
piezoelectric charge coefficient (d33) from 108pC/N to 128pC/N. For
this range of ceramic samples, grain size refinement suppresses the
maximum dielectric constant (εmax), shifts the Curie temperature (Tc)
to a lower temperature and the orthorhombic-tetragonal phase
transition (Tot) to a higher temperature. Further increase of milling
time from 25h to 40h produces a gradual degradation in the values of
relative density, εRT, and d33 of the resulting ceramics.
Abstract: In this study, microcrystalline cellulose (MCC) was
extracted from oil palm empty fruit bunch (EFB) cellulose which was
earlier isolated from oil palm EFB fibre. In order to isolate the
cellulose, the chlorination method was carried out. Then, the MCC
was prepared by simultaneous ultrasonic and alkali treatment from
the isolated α-cellulose. Based on mass balance calculation, the yields
for MCC obtained from EFB was 44%. For fiber characterization, it
is observed that the chemical composition of the hemicellulose and
lignin for all samples decreased while composition for cellulose
increased. The structural property of the MCC was studied by X-ray
diffraction (XRD) method and the result shows that the MCC
produced is a cellulose-I polymorph, with 73% crystallinity.
Abstract: Two Lithium Disilicate (LD) glass ceramics based on
SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting
method. The glass rods were then fabricated into dental crowns via a
hot pressing at 900˚C and 850˚C in order to study the effect of the
pressing temperatures on the phase formation and microstructure of
the glasses. Different samples of as cast glass and heat treated
samples (600˚C and 700˚C) were used to press for investigating the
effect of an initial microstructure on the hot pressing technique. Xray
diffraction (XRD) and scanning electron microscopy (SEM) were
performed to determine the phase formation and microstructure of the
samples, respectively. XRD results show that the main crystalline
structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3,
Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with
different heat treatment temperatures exhibited a difference phase
formations but have less effect during pressing. SEM micrographs
showed the microstructure of Li2Si2O5 as lath-like shape in all
glasses. With increasing the initial heat treatment temperature, the
longer the lath-like crystals of lithium disilicate were increased
especially when using glass heat treatment at 700˚C followed by
pressing at 900˚C. This could be suggested that LD1 heat treatment at
700˚C which pressing at 900˚C presented the best formation by the
hot pressing and compiled microstructure.
Abstract: Yttrium oxide (Y2O3) films have been successfully
deposited with yttrium-ethylenediamine tetraacetic acid (EDTA·Y·H)
complexes prepared by various milling techniques. The effects of the
properties of the EDTA·Y·H complex on the properties of the
deposited Y2O3 films have been analyzed. Seven different types of the
raw EDTA·Y·H complexes were prepared by various commercial
milling techniques such as ball milling, hammer milling, commercial
milling, and mortar milling. The milled EDTA·Y·H complexes
exhibited various particle sizes and distributions, depending on the
milling method. Furthermore, we analyzed the crystal structure,
morphology and elemental distribution profile of the metal oxide films
deposited on stainless steel substrate with the milled EDTA·Y·H
complexes. Depending on the milling technique, the flow properties of
the raw powders differed. The X-ray diffraction pattern of all the
samples revealed the formation of Y2O3 crystalline phase, irrespective
of the milling technique. Of all the different milling techniques, the
hammer milling technique is considered suitable for fabricating dense
Y2O3 films.
Abstract: Violet Sr–Al–O:Eu2+ phosphor particles were
synthesized from a metal–ethylenediaminetetraacetic acid (EDTA)
solution of Sr, Al, Eu, and particulate alumina via spray drying and
sintering in a reducing atmosphere. The crystal structures and emission
properties at 85–300 K were investigated. The composition of the
violet Sr–Al–O:Eu2+ phosphor particles was determined from various
Sr–Al–O:Eu2+ phosphors by their emission properties’ dependence
on temperature. The highly crystalline SrAl12O19:Eu2+ emission phases
were confirmed by their crystallite sizes and the activation energies for
the 4f5d–8S7/2 transition of the Eu2+ ion. These results showed that the
material identification for the violet Sr–Al–O:Eu2+ phosphor was
accomplished by the low-temperature luminescence measurements.
Abstract: Metal-enhanced Luminescence of silicon nanocrystals
(SiNCs) was determined using two different particle sizes of silver
nanoparticles (AgNPs). SiNCs have been characterized by scanning
electron microscopy (SEM), high resolution transmission electron
microscopy (HRTEM), Fourier transform infrared spectroscopy
(FTIR) and X-ray photoelectron spectroscopy (XPS). It is found that
the SiNCs are crystalline with an average diameter of 65 nm and FCC
lattice. AgNPs were synthesized using photochemical reduction of
AgNO3 with sodium dodecyl sulphate (SDS). The enhanced
luminescence of SiNCs by AgNPs was evaluated by confocal Raman
microspectroscopy. Enhancement up to x9 and x3 times were
observed for SiNCs that mixed with AgNPs which have an average
particle size of 100 nm and 30 nm, respectively. Silver NPs-enhanced
luminescence of SiNCs occurs as a result of the coupling between the
excitation laser light and the plasmon bands of AgNPs; thus this
intense field at AgNPs surface couples strongly to SiNCs.
Abstract: Partial shadowing is one of the problems that are always faced in terrestrial applications of solar photovoltaic (PV). The effects of partial shadow on the energy yield of conventional mono-crystalline and multi-crystalline PV modules have been researched for a long time. With deployment of new thin-film solar PV modules in the market, it is important to understand the performance of new PV modules operating under the partial shadow in the tropical zone. This paper addresses the impacts of different partial shadowing on the operating characteristics of four different types of solar PV modules that include multi-crystalline, amorphous thin-film, CdTe thin-film and CIGS thin-film PV modules.
Abstract: With growth of PV market in tropical region, it is necessary to investigate the performance of different types of PV technology under the tropical weather conditions. Singapore Polytechnic was funded by Economic Development Board (EDB) to set up a solar PV test-bed for the research on performance of different types of PV modules in the country. The PV test-bed installed the nine different types of PV systems that are integrated to power utility grid for monitoring and analyzing their operating performances. This paper presents the 12 months operational data of nine different PV systems and analyses on performances of installed PV systems using energy yield and performance ratio. The nine types of PV systems under test have shown their energy yields ranging from 2.67 to 3.36 kWh/kWp and their performance ratios (PRs) ranging from 70% to 88%.