Abstract: In this study, a nickel film with nano-crystalline grains,
high hardness and smooth surface was electrodeposited using a post
supercritical carbon dioxide (CO2) mixed Watts electrolyte. Although
the hardness was not as high as its Sc-CO2 counterpart, the thin coating
contained significantly less number of nano-sized pinholes. By
measuring the escape concentration of the dissolved CO2 in post
Sc-CO2 mixed electrolyte with the elapsed time, it was believed that
the residue of dissolved CO2 bubbles should closely relate to the
improvement in hardness and surface roughness over its conventional
plating counterpart. Therefore, shortening the duration of
electroplating with the raise of current density up to 0.5 A/cm2 could
effectively retain more post Sc-CO2 mixing effect. This study not only
confirms the roles of dissolved CO2 bubbles in electrolyte but also
provides a potential process to overcome most issues associated with
the cost in building high-pressure chamber for large size products and
continuous plating using supercritical method.
Abstract: Silver nanoparticles were prepared by chemical reduction method. Silver nitrate was taken as the metal precursor and hydrazine hydrate as a reducing agent. The formation of the silver nanoparticles was monitored using UV-Vis absorption spectroscopy. The UV-Vis spectroscopy revealed the formation of silver nanopart├¡cles by exhibing the typical surface plasmon absorption maxima at 418-420 nm from the UV–Vis spectrum. Comparison of theoretical (Mie light scattering theory) and experimental results showed that diameter of silver nanoparticles in colloidal solution is about 60 nm. We have used energy-dispersive spectroscopy (EDX), X-ray diffraction (XRD), transmission electron microscopy (TEM) and, UV–Vis spectroscopy to characterize the nanoparticles obtained. The energy-dispersive spectroscopy (EDX) of the nanoparticles dispersion confirmed the presence of elemental silver signal no peaks of other impurity were detected. The average size and morphology of silver nanoparticles were determined by transmission electron microscopy (TEM). TEM photographs indicate that the nanopowders consist of well dispersed agglomerates of grains with a narrow size distribution (40 and 60 nm), whereas the radius of the individual particles are between 10 and 20 nm. The synthesized nanoparticles have been structurally characterized by X-ray diffraction and transmission high-energy electron diffraction (HEED). The peaks in the XRD pattern are in good agreement with the standard values of the face-centered-cubic form of metallic silver (ICCD-JCPDS card no. 4-0787) and no peaks of other impurity crystalline phases were detected. Additionally, the antibacterial activity of the nanopart├¡culas dispersion was measured by Kirby-Bauer method. The nanoparticles of silver showed high antimicrobial and bactericidal activity against gram positive bacteria such as Escherichia Coli, Pseudimonas aureginosa and staphylococcus aureus which is a highly methicillin resistant strain.
Abstract: Ovshinsky initiated scientific research in the field of
amorphous and disordered materials that continues to this day. The
Ovshinsky Effect where the resistance of thin GST films is
significantly reduced upon the application of low voltage is of
fundamental importance in phase-change - random access memory
(PC-RAM) devices.GST stands for GdSbTe chalcogenide type
glasses.However, the Ovshinsky Effect is not without controversy.
Ovshinsky thought the resistance of GST films is reduced by the
redistribution of charge carriers; whereas, others at that time including
many PC-RAM researchers today argue that the GST resistance
changes because the GST amorphous state is transformed to the
crystalline state by melting, the heat supplied by external heaters. In
this controversy, quantum mechanics (QM) asserts the heat capacity of
GST films vanishes, and therefore melting cannot occur as the heat
supplied cannot be conserved by an increase in GST film
temperature.By precluding melting, QM re-opens the controversy
between the melting and charge carrier mechanisms. Supporting
analysis is presented to show that instead of increasing GST film
temperature, conservation proceeds by the QED induced creation of
photons within the GST film, the QED photons confined by TIR. QED
stands for quantum electrodynamics and TIR for total internal
reflection. The TIR confinement of QED photons is enhanced by the
fact the absorbedheat energy absorbed in the GST film is concentrated
in the TIR mode because of their high surface to volume ratio. The
QED photons having Planck energy beyond the ultraviolet produce
excitons by the photoelectric effect, the electrons and holes of which
reduce the GST film resistance.
Abstract: The complex structure of lignocellulose leads to great
difficulties in converting it to fermentable sugars for the ethanol
production. The major hydrolysis impediments are the crystallinity of
cellulose and the lignin content. To improve the efficiency of
enzymatic hydrolysis, microbial pretreatment of corncob was
investigated using two bacterial strains of Bacillus subtilis A 002 and
Cellulomonas sp. TISTR 784 (expected to break open the crystalline
part of cellulose) and lignin-degrading fungus, Phanerochaete
sordida SK7 (expected to remove lignin from lignocellulose). The
microbial pretreatment was carried out with each strain under its
optimum conditions. The pretreated corncob samples were further
hydrolyzed to produce reducing glucose with low amounts of
commercial cellulase (25 U·g-1 corncob) from Aspergillus niger. The
corncob samples were determined for composition change by X-ray
diffraction (XRD), Fourier transform infrared spectroscopy (FTIR),
and scanning electron microscope (SEM). According to the results,
the microbial pretreatment with fungus, P. sordida SK7 was the most
effective for enhancing enzymatic hydrolysis, approximately, 40%
improvement.
Abstract: Low silica type X (LSX) Zeolite is one of useful
material in many manufacturing due to the advantage properties
including high surface area, stability, microporous crystalline
aluminosilicates and positive ion in an extra–framework. The LSX
was used rice husk silica source which obtained by leaching with
hydrochloric acid and calcination at 500C. To improve the
synthesis method, the LSX was crystallizated in Teflon–lined
autoclave will expedite deceasing of the amorphous particles. The
mixed gel with composition of 5.5 Na2O : 1.65 K2O : Al2O3 : 2.2
SiO2 : 122 H2O was crystallized in different container
(Polypropylene bottom and Teflon–lined autoclave). The obtained
powder was characterized by X–ray diffraction (XRD), X–ray
fluorescence spectrometry, N2 adsorption-desorption analysis BET
surface area Scanning electron microscopy (SEM) and Fourier
transform infrared spectroscopy to justify the quality of zeolite. The
results showed the crystallized zeolite in Teflon lined autoclave has
102.8 nm of crystal size, 286 m2/g of surface area and fewer amounts
of round amorphous particles when compared with the crystallized
zeolite in Polypropylene.
Abstract: The characterisation of agro-wastes fibres for composite applications from Nigeria using X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) has been done. Fibres extracted from groundnut shell, coconut husk, rice husk, palm fruit bunch and palm fruit stalk are processed using two novel cellulose fibre production methods developed by the authors. Cellulose apparent crystallinity calculated using the deconvolution of the diffractometer trace shows that the amorphous portion of cellulose was permeable to hydrolysis yielding high crystallinity after treatment. All diffratograms show typical cellulose structure with well-defined 110, 200 and 040 peaks. Palm fruit fibres had the highest 200 crystalline cellulose peaks compared to others and it is an indication of rich cellulose content. Surface examination of the resulting fibres using SEM indicates the presence of regular cellulose network structure with some agglomerated laminated layer of thin leaves of cellulose microfibrils. The surfaces were relatively smooth indicating the removal of hemicellulose, lignin and pectin.
Abstract: The hydrolysis kinetics of polycrystalline lithium hydride (LiH) in argon at various low humidities was measured by gravimetry and Raman spectroscopy with ambient water concentration ranging from 200 to 1200 ppm. The results showed that LiH hydrolysis curve revealed a paralinear shape, which was attributed to two different reaction stages that forming different products as explained by the 'Layer Diffusion Control' model. Based on the model, a novel two-stage rate equation for LiH hydrolysis reactions was developed and used to fit the experimental data for determination of Li2O steady thickness Hs and the ultimate hydrolysis rate vs. The fitted data presented a rise of Hs as ambient water concentration cw increased. However, in spite of the negative effect imposed by Hs increasing, the upward trend of vs remained, which implied that water concentration, rather than Li2O thickness, played a predominant role in LiH hydrolysis kinetics. In addition, the proportional relationship between vsHs and cw predicted by rate equation and confirmed by gravimetric data validated the model in such conditions.
Abstract: In this paper, we present a vertical nanowire thin film transistor with gate-all-around architecture, fabricated using CMOS compatible processes. A novel method of fabricating polysilicon vertical nanowires of diameter as small as 30 nm using wet-etch is presented. Both n-type and p-type vertical poly-silicon nanowire transistors exhibit superior electrical characteristics as compared to planar devices. On a poly-crystalline nanowire of 30 nm diameter, high Ion/Ioff ratio of 106, low drain-induced barrier lowering (DIBL) of 50 mV/V, and low sub-threshold slope SS~100mV/dec are demonstrated for a device with channel length of 100 nm.
Abstract: Highly ordered arrays of TiO2 nanotubes (TiNTs) were grown vertically on Ti foil by electrochemical anodization. We controlled the lengths of these TiNTs from 2.4 to 26.8 ¶üÇóμm while varying the water contents (1, 3, and 6 wt%) of the electrolyte in ethylene glycol in the presence of 0.5 wt% NH4F with anodization for various applied voltages (20–80 V), periods (10–240 min) and temperatures (10–30 oC). For vertically aligned TiNT arrays, not only the increase in their tube lengths, but also their geometric (wall thickness and surface roughness) and crystalline structure lead to a significant influence on photocatalytic activity. The length optimization for methylene blue (MB) photodegradation was 18 μm. Further extending the TiNT length yielded lower photocatalytic activity presumably related to the limited MB diffusion and light-penetration depth into the TiNT arrays. The results indicated that a maximum MB photodegradation rate was obtained for the discrete anatase TiO2 nanotubes with thick and rough walls.
Abstract: In a state-of-the-art industrial production line of
photovoltaic products the handling and automation processes are of
particular importance and implication. While processing a fully
functional crystalline solar cell an as-cut photovoltaic wafer is subject
to numerous repeated handling steps. With respect to stronger
requirements in productivity and decreasing rejections due to defects
the mechanical stress on the thin wafers has to be reduced to a
minimum as the fragility increases by decreasing wafer thicknesses.
In relation to the increasing wafer fragility, researches at the
Fraunhofer Institutes IPA and CSP showed a negative correlation
between multiple handling processes and the wafer integrity. Recent
work therefore focused on the analysis and optimization of the dry
wafer stack separation process with compressed air. The achievement
of a wafer sensitive process capability and a high production
throughput rate is the basic motivation in this research.
Abstract: Films of pure tin oxide SnO2 and in presence of
antimony atoms (SnO2-Sb) deposited onto glass substrates have
shown a sufficiently high energy gap to be transparent in the visible
region, a high electrical mobility and a carrier concentration which
displays a good electrical conductivity [1]. In this work, the effects of
polycrystalline silicon substrate on the optical properties of pure and
Sb doped tin oxide is investigated.
We used the APCVD (atmospheric pressure chemical vapour
deposition) technique, which is a low-cost and simple technique,
under nitrogen ambient, for growing this material. A series of SnO2
and SnO2-Sb have been deposited onto polycrystalline silicon
substrates with different contents of antimony atoms at the same
conditions of deposition (substrate temperature, flow oxygen,
duration and nitrogen atmosphere of the reactor). The effect of the
substrate in terms of morphology and nonlinear optical properties,
mainly the reflectance, was studied. The reflectance intensity of the
device, compared to the reflectance of tin oxide films deposited
directly on glass substrate, is clearly reduced on the overall
wavelength range. It is obvious that the roughness of the poly-c
silicon plays an important role by improving the reflectance and
hence the optical parameters.
A clear shift in the minimum of the reflectance upon doping level
is observed. This minimum corresponds to strong free carrier
absorption, resulting in different plasma frequency. This effect is
followed by an increase in the reflectance depending of the antimony
doping. Applying the extended Drude theory to the combining
optical and electrical obtained results these effects are discussed.
Abstract: The crystalline quality of the AlGaN/GaN high electron mobility transistor (HEMT) structure grown on a 200 mm silicon substrate has been investigated using UV-visible micro- Raman scattering and photoluminescence (PL). The visible Raman scattering probes the whole nitride stack with the Si substrate and shows the presence of a small component of residual in-plane stress in the thick GaN buffer resulting from a wafer bowing, while the UV micro-Raman indicates a tensile interfacial stress induced at the top GaN/AlGaN/AlN layers. PL shows a good crystal quality GaN channel where the yellow band intensity is very low compared to that of the near-band-edge transition. The uniformity of this sample is shown by measurements from several points across the epiwafer.
Abstract: The governing two-dimensional equations of a heterogeneous material composed of a fluid (allowed to flow in the absence of acoustic excitations) and a crystalline piezoelectric cubic solid stacked one-dimensionally (along the z direction) are derived and special emphasis is given to the discussion of acoustic group velocity for the structure as a function of the wavenumber component perpendicular to the stacking direction (being the x axis). Variations in physical parameters with y are neglected assuming infinite material homogeneity along the y direction and the flow velocity is assumed to be directed along the x direction. In the first part of the paper, the governing set of differential equations are derived as well as the imposed boundary conditions. Solutions are provided using Hamilton-s equations for the wavenumber vs. frequency as a function of the number and thickness of solid layers and fluid layers in cases with and without flow (also the case of a position-dependent flow in the fluid layer is considered). In the first part of the paper, emphasis is given to the small-frequency case. Boundary conditions at the bottom and top parts of the full structure are left unspecified in the general solution but examples are provided for the case where these are subject to rigid-wall conditions (Neumann boundary conditions in the acoustic pressure). In the second part of the paper, emphasis is given to the general case of larger frequencies and wavenumber-frequency bandstructure formation. A wavenumber condition for an arbitrary set of consecutive solid and fluid layers, involving four propagating waves in each solid region, is obtained again using the monodromy matrix method. Case examples are finally discussed.
Abstract: The crystallization kinetics and phase transformation
of SiO2.Al2O3.0,56P2O5.1,8CaO.0,56CaF2 glass have been
investigated using differential thermal analysis (DTA), x-ray
diffraction (XRD), and scanning electron microscopy (SEM). Glass
samples were obtained by melting the glass mixture at 14500С/120
min. in platinum crucibles. The mixture were prepared from
chemically pure reagents: SiO2, Al(OH)3, H3PO4, CaCO3 and CaF2.
The non-isothermal kinetics of crystallization was studied by
applying the DTA measurements carried out at various heating rates.
The activation energies of crystallization and viscous flow were
measured as 348,4 kJ.mol–1 and 479,7 kJ.mol–1 respectively. Value of
Avrami parameter n ≈ 3 correspond to a three dimensional of crystal
growth mechanism. The major crystalline phase determined by XRD
analysis was fluorapatite (Ca(PO4)3F) and as the minor phases –
fluormargarite (CaAl2(Al2SiO2)10F2) and vitlokite (Ca9P6O24). The
resulting glass-ceramic has a homogeneous microstructure, composed
of prismatic crystals, evenly distributed in glass phase.
Abstract: n-CdO/p-Si heterojunction diode was fabricated using
sol-gel spin coating technique which is a low cost and easily scalable
method for preparing of semiconductor films. The structural and
morphological properties of CdO film were investigated. The X-ray
diffraction (XRD) spectra indicated that the film was of
polycrystalline nature. The scanning electron microscopy (SEM)
images indicate that the surface morphology CdO film consists of the
clusters formed with the coming together of the nanoparticles. The
electrical characterization of Au/n-CdO/p–Si/Al heterojunction diode
was investigated by current-voltage. The ideality factor of the diode
was found to be 3.02 for room temperature. The reverse current of
the diode strongly increased with illumination intensity of 100
mWcm-2 and the diode gave a maximum open circuit voltage Voc of
0.04 V and short-circuits current Isc of 9.92×10-9 A.
Abstract: In this investigation, anatase TiO2 thin films were
grown by radio frequency magnetron sputtering on glass substrates at
a high sputtering pressure and room temperature. The anatase films
were then annealed at 300-600 °C in air for a period of 1 hour. To
examine the structure and morphology of the films, X-ray diffraction
(XRD) and atomic force microscopy (AFM) methods were used
respectively. From X-ray diffraction patterns of the TiO2 films, it was
found that the as-deposited film showed some differences compared
with the annealed films and the intensities of the peaks of the
crystalline phase increased with the increase of annealing
temperature. From AFM images, the distinct variations in the
morphology of the thin films were also observed. The optical
constants were characterized using the transmission spectra of the
films obtained by UV-VIS-IR spectrophotometer. Besides, optical
thickness of the film deposited at room temperature was calculated
and cross-checked by taking a cross-sectional image through SEM.
The optical band gaps were evaluated through Tauc model. It was
observed that TiO2 films produced at room temperatures exhibited
high visible transmittance and transmittance decreased slightly with
the increase of annealing temperatures. The films were found to be
crystalline having anatase phase. The refractive index of the films
was found from 2.31-2.35 in the visible range. The extinction
coefficient was nearly zero in the visible range and was found to
increase with annealing temperature. The allowed indirect optical
band gap of the films was estimated to be in the range from 3.39 to
3.42 eV which showed a small variation. The allowed direct band
gap was found to increase from 3.67 to 3.72 eV. The porosity was
also found to decrease at a higher annealing temperature making the
film compact and dense.
Abstract: Considering toxicity of heavy metals and their
accumulation in domestic wastes, immobilization of lead and
cadmium is envisaged inside glass-ceramics. We particularly
focused this work on calcium-rich phases embedded in a
glassy matrix.
Glass-ceramics were synthesized from glasses doped with
12 wt% and 16 wt% of PbO or CdO. They were observed and
analyzed by Electron MicroProbe Analysis (EMPA) and
Analytical Scanning Electron Microscopy (ASEM). Structural
characterization of the samples was performed by powder XRay
Diffraction.
Diopside crystals of CaMgSi2O6 composition are shown to
incorporate significant amounts of cadmium (up to 9 wt% of
CdO). Two new crystalline phases are observed with very
high Cd or Pb contents: about 40 wt% CdO for the cadmiumrich
phase and near 60 wt% PbO for the lead-rich phase. We
present complete chemical and structural characterization of
these phases. They represent a promising way for the
immobilization of toxic elements like Cd or Pb since glass
ceramics are known to propose a “double barrier" protection
(metal-rich crystals embedded in a glass matrix) against metal
release in the environment.
Abstract: The selective wet-etching of amorphous and
crystalline region of Sb20Se80 thin films was carried out using organic
based solution e.g. amines. We report the development of an in situ
real-time method to study the wet chemical etching process of thin
films. Characterization of the structure and surface of films studied
by X-ray diffraction, SEM and EBSD methods has been done and
potential application suggested.
Abstract: Magnesium wastes and scraps, one of the metal wastes, are produced by many industrial activities, all over the world. Their growing size is becoming a future problem for the world. In this study, the use of magnesium wastes as a raw material in the production of the magnesium borate hydrates are aimed. The method used in the experiments is hydrothermal synthesis. The conditions are set to, waste magnesium to B2O3, 1:3 as a molar ratio. Four different reaction times are studied which are 30, 60, 120 and 240 minutes. For the identification analyses X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR) and Raman spectroscopy techniques are used. As a result at all the reaction times magnesium borate hydrates are synthesized and the most crystalline forms are obtained at a reaction time of 120 minutes. The overall yields of the production are found between the values of 65-80 %.
Abstract: To understand the material characteristics of singleand
poly-crystals of pure copper, the respective relationships between
crystallographic orientations and microstructures, and the bending
and mechanical properties were examined. And texture distribution
is also analyzed. A bending test is performed in a SEM apparatus and
while its behaviors are observed in situ. Furthermore, some
analytical results related to crystal direction maps, inverse pole
figures, and textures were obtained from EBSD analyses.