Abstract: The crystal orientation is a factor that affects the microscopic material properties. Crystal orientation determines the anisotropy of the polycrystalline material. And it is closely related to the mechanical properties of the material. In this paper, for pure copper polycrystalline material, two different methods; X-Ray Diffraction (XRD) and Electron Backscatter Diffraction (EBSD); and the crystal orientation were analyzed. In the latter method, it is possible that the X-ray beam diameter is thicker as compared to the former, to measure the crystal orientation macroscopically relatively. By measurement of the above, we investigated the change in crystal orientation and internal tissues of pure copper.
Abstract: Because die drawing requires insertion of a die, a plug, or a mandrel, higher precision and efficiency are demanded for drawing equipment for a tube having smaller diameter. Manufacturing of such tubes is also accompanied by problems such as cracking and fracture. We specifically examine dieless drawing, which is less affected by these drawing-related difficulties. This deformation process is governed by a similar principle to that of reduction in diameter when pulling a heated glass tube. We conducted dieless drawing of SUS304 stainless steel microtubes under various conditions with three factor parameters of heating temperature, area reduction, and drawing speed. We used SEM-EBSD to observe the processing condition effects on microstructural elements. As the result of this study, crystallographic orientation of microtube is clear by using SEM-EBSD analysis.
Abstract: To elucidate the material characteristics of single
crystals of pure aluminum and copper, the respective relations between
crystallographic orientations and microstructures were examined,
along with bending and mechanical properties. The texture
distribution was also analysed. Bending tests were performed in a
SEM apparatus while its behaviors were observed. Some analytical
results related to crystal direction maps, inverse pole figures, and
textures were obtained from electron backscatter diffraction (EBSD)
analyses.
Abstract: Using a texture database, a statistical estimation of
spring-back was conducted in this study on the basis of statistical
analysis. Both spring-back in bending deformation and experimental
data related to the crystal orientation show significant dispersion.
Therefore, a probabilistic statistical approach was established for the
proper quantification of these values. Correlation was examined
among the parameters F(x) of spring-back, F(x) of the buildup fraction
to three orientations after 92° bending, and F(x) at an as-received part
on the basis of the three-parameter Weibull distribution. Consequent
spring-back estimation using a texture database yielded excellent
estimates compared with experimental values.
Abstract: To understand the material characteristics of singleand
poly-crystals of pure copper, the respective relationships between
crystallographic orientations and microstructures, and the bending
and mechanical properties were examined. And texture distribution
is also analyzed. A bending test is performed in a SEM apparatus and
while its behaviors are observed in situ. Furthermore, some
analytical results related to crystal direction maps, inverse pole
figures, and textures were obtained from EBSD analyses.
Abstract: To improve the material characteristics of single- and
poly-crystals of pure copper, the respective relationships between crystallographic orientations and microstructures, and the bending and mechanical properties were examined. And texture distribution is also
analyzed. A grain refinement procedure was performed to obtain a
grained structure. Furthermore, some analytical results related to
crystal direction maps, inverse pole figures, and textures were obtained from SEM-EBSD analyses. Results showed that these
grained metallic materials have peculiar springback characteristics with various bending angles.