Abstract: Carbon nanotube is one of the most attractive materials
for the potential applications of nanotechnology due to its excellent
mechanical, thermal, electrical and optical properties. In this paper we
report a supercapacitor made of nickel foil electrodes, coated with
multiwall carbon nanotubes (MWCNTs) thin film using
electrophoretic deposition (EPD) method. Chemical vapor deposition
method was used for the growth of MWCNTs and ethanol was used as
a hydrocarbon source. High graphitic multiwall carbon nanotube was
found at 750oC analyzing by Raman spectroscopy. We observed the
electrochemical performance of supercapacitor by cyclic
voltammetry. The electrodes of supercapacitor fabricated from
MWCNTs exhibit considerably small equivalent series resistance
(ESR), and a high specific power density. Electrophoretic deposition
is an easy method in fabricating MWCNT electrodes for high
performance supercapacitor.
Abstract: Hydrogenated amorphous carbon (a-C:H) films have
been synthesized by a radio frequency plasma enhanced chemical
vapor deposition (rf-PECVD) technique with different bias voltage
from 0.0 to -0.5 kV. The Raman spectra displayed the polymer-like
hydrogenated amorphous carbon (PLCH) film with 0.0 to -0.1 and
a-C:H films with -0.2 to -0.5 kV of bias voltages. The surface chemical
information of all films were studied by X-ray photoelectron
spectroscopy (XPS) technique, presented to C-C (sp2 and sp3) and C-O
bonds, and relative carbon (C) and oxygen (O) atomics contents. The
O contamination had affected on structure and optical properties. The
true density of PLCH and a-C:H films were characterized by X-ray
refractivity (XRR) method, showed the result as in the range of
1.16-1.73 g/cm3 that depending on an increasing of bias voltage. The
hardness was proportional to the true density of films. In addition, the
optical properties i.e. refractive index (n) and extinction coefficient (k)
of these films were determined by a spectroscopic ellipsometry (SE)
method that give formation to in 1.62-2.10 (n) and 0.04-0.15 (k)
respectively. These results indicated that the optical properties
confirmed the Raman results as presenting the structure changed with
applied bias voltage increased.
Abstract: Noble metal participation in nanostructured
semiconductor catalysts has drawn much interest because of their
improved properties. Recently, it has been discussed by many
researchers that Ag participation in TiO2, CuO, ZnO semiconductors
showed improved photocatalytic and optical properties. In this
research, Ag/ZnO nanocomposite particles were prepared by
Ultrasonic Spray Pyrolysis(USP) Method. 0.1M silver and zinc
nitrate aqueous solutions were used as precursor solutions. The
Ag:Zn atomic ratio of the solution was selected 1:1. Experiments
were taken place under constant air flow of 400 mL/min at 800°C
furnace temperature. Particles were characterized by X-Ray
Diffraction (XRD), Scanning Electron Microscope (SEM) and
Energy Dispersive Spectroscopy (EDS). The crystallite sizes of Ag
and ZnO in composite particles are 24.6 nm, 19.7 nm respectively.
Although, spherical nanocomposite particles are in a range of 300-
800 nm, these particles are formed by the aggregation of primary
particles which are in a range of 20-60 nm.
Abstract: The use of magnetic and magnetic/gold core/shell
nanoparticles in biotechnology or medicine has shown good promise
due to their hybrid nature which possesses superior magnetic and
optical properties. Some of these potential applications include
hyperthermia treatment, bio-separations, diagnostics, drug delivery
and toxin removal. Synthesis refinement to control geometric and
magnetic/optical properties, and finding functional surfactants for
biomolecular attachment, are requirements to meet application
specifics.
Various high-temperature preparative methods were used for the
synthesis of iron oxide and gold-coated iron oxide nanoparticles.
Different surface functionalities, such as 11-aminoundecanoic and
11-mercaptoundecanoic acid, were introduced on the surface of the
particles to facilitate further attachment of biomolecular functionality
and drug-like molecules. Nanoparticle thermal stability, composition,
state of aggregation, size and morphology were investigated and the
results from techniques such as Fourier Transform-Infra Red
spectroscopy (FT-IR), Ultraviolet visible spectroscopy (UV-vis),
Transmission Electron Microscopy (TEM) and thermal analysis are
discussed.
Abstract: ZnO-SnO2 i.e. Zinc-Tin-Oxide (ZTO) thin films were
deposited on glass substrate with varying concentrations (ZnO:SnO2
- 100:0, 90:10, 70:30 and 50:50 wt.%) at room temperature by flash
evaporation technique. These deposited ZTO film were annealed at
450 0C in vacuum. These films were characterized to study the effect
of annealing on the structural, electrical, and optical properties.
Atomic force microscopy (AFM) and Scanning electron microscopy
(SEM) images manifest the surface morphology of these ZTO thin
films. The apparent growth of surface features revealed the formation
of nanostructure ZTO thin films. The small value of surface
roughness (root mean square RRMS) ensures the usefulness in
optical coatings. The sheet resistance was also found to be decreased
for both types of films with increasing concentration of SnO2. The
optical transmittance found to be decreased however blue shift has
been observed after annealing.
Abstract: In this investigation, anatase TiO2 thin films were
grown by radio frequency magnetron sputtering on glass substrates at
a high sputtering pressure and room temperature. The anatase films
were then annealed at 300-600 °C in air for a period of 1 hour. To
examine the structure and morphology of the films, X-ray diffraction
(XRD) and atomic force microscopy (AFM) methods were used
respectively. From X-ray diffraction patterns of the TiO2 films, it was
found that the as-deposited film showed some differences compared
with the annealed films and the intensities of the peaks of the
crystalline phase increased with the increase of annealing
temperature. From AFM images, the distinct variations in the
morphology of the thin films were also observed. The optical
constants were characterized using the transmission spectra of the
films obtained by UV-VIS-IR spectrophotometer. Besides, optical
thickness of the film deposited at room temperature was calculated
and cross-checked by taking a cross-sectional image through SEM.
The optical band gaps were evaluated through Tauc model. It was
observed that TiO2 films produced at room temperatures exhibited
high visible transmittance and transmittance decreased slightly with
the increase of annealing temperatures. The films were found to be
crystalline having anatase phase. The refractive index of the films
was found from 2.31-2.35 in the visible range. The extinction
coefficient was nearly zero in the visible range and was found to
increase with annealing temperature. The allowed indirect optical
band gap of the films was estimated to be in the range from 3.39 to
3.42 eV which showed a small variation. The allowed direct band
gap was found to increase from 3.67 to 3.72 eV. The porosity was
also found to decrease at a higher annealing temperature making the
film compact and dense.