Abstract: New design of a grid for preparation of high density
granules with enhanced mechanical strength by granulation of
dispersed materials is suggested.
A method for hydrodynamic dimensioning of the grid depending
on granulation conditions, hydrodynamic regime of the operation,
dispersity and physicochemical characteristics of the materials to be
granulated was suggested.
The aim of the grid design is to solve the problems arising by the
granulation of disperse materials.
Abstract: A newly designed gas-distributor for granulation of powdery materials in equilibrated fluidized bed and a system for collecting the granules prepared are suggested. The aim of these designs is to solve the problems arising by the granulation of powdery materials in fluidized bed devices. The gasdistributor and the collection system proved to be reliable at operation; they reduce the size of still zones, effectively disperse the binding solution in the bed and ensure the collection of granules of given diameter
Abstract: The crystallization kinetics and phase transformation
of SiO2.Al2O3.0,56P2O5.1,8CaO.0,56CaF2 glass have been
investigated using differential thermal analysis (DTA), x-ray
diffraction (XRD), and scanning electron microscopy (SEM). Glass
samples were obtained by melting the glass mixture at 14500С/120
min. in platinum crucibles. The mixture were prepared from
chemically pure reagents: SiO2, Al(OH)3, H3PO4, CaCO3 and CaF2.
The non-isothermal kinetics of crystallization was studied by
applying the DTA measurements carried out at various heating rates.
The activation energies of crystallization and viscous flow were
measured as 348,4 kJ.mol–1 and 479,7 kJ.mol–1 respectively. Value of
Avrami parameter n ≈ 3 correspond to a three dimensional of crystal
growth mechanism. The major crystalline phase determined by XRD
analysis was fluorapatite (Ca(PO4)3F) and as the minor phases –
fluormargarite (CaAl2(Al2SiO2)10F2) and vitlokite (Ca9P6O24). The
resulting glass-ceramic has a homogeneous microstructure, composed
of prismatic crystals, evenly distributed in glass phase.