Abstract: High resolution seismic reflection has recently been carried out on Zaria batholith, with the aim of characterizing the granitic Zaria batholiths in terms of its lithology. The geology of the area has revealed that the older granite outcrops in the vicinity of Zaria are exposures of a syntectonics to late-tectonic granite batholiths which intruded a crystalline gneissic basement during the Pan-African Orogeny. During the data acquisition the geophone were placed at interval of 1 m, variable offset of 1 and 10 m was used. The common midpoint (CMP) method with 12 fold coverage was employed for the survey. Analysis of the generated 3D surface of the p wave velocities from different profiles for densities and bulk modulus revealed that the rock material is more consolidated in South East part of the batholith and less consolidated in the North Western part. This was in conformity with earlier identified geology of the area, with the South Eastern part majorly of granitic outcrop, while the North Western part is characterized with the exposure of gneisses and thick overburden cover. The difference in lithology was also confirmed by the difference in seismic sections and Arial satellite photograph. Hence two major lithologies were identified, the granitic and gneisses complex which are characterized by gradational boundaries.
Abstract: Aluminum Matrix Composites reinforced with
nanocrystalline Ni3Al carbon-coated intermetallic particles, were
synthesized by powder metallurgy. Powder mixture of aluminum
with 0.5-volume fraction of reinforcement particles was compacted
by spark plasma sintering (SPS) technique and the compared with
conventional sintering process. The better results for SPS technique
were obtained in 520ºC-5kN-3min.The hardness (70.5±8 HV) and the
elastic modulus (95 GPa) were evaluated in function of sintering
conditions for SPS technique; it was found that the incorporation of
these kind of reinforcement particles in aluminum matrix improve its
mechanical properties. The densities were about 94% and 97% of the
theoretical density. The carbon coating avoided the interfacial
reaction between matrix-particle at high temperature (520°C) without
show composition change either intermetallic dissolution.
Abstract: The microstructure characterization of tempered nanocrystalline bainitic steel is investigated in the present study. It is found that two types of plastic relaxation, dislocation debris and nanotwin, occurs in the displacive transformation due to relatively low transformation temperature and high carbon content. Because most carbon atoms trap in the dislocation, high dislocation density can be sustained during the tempering process. More carbides only can be found in the high tempered temperature due to intense recovery progression.
Abstract: X-ray diffraction is an effective mean for analyzing material properties. This paper developed a new computational software for determining the properties of crystalline materials such as elastic constants, residual stresses, surface hardness, phase components, and etc. The results computed from the X-ray diffraction method were compared to those from the traditional methods and they are in the 95% confidential limits, showing that the newly developed software has high reproducibility, opening a possibility of its commercialization.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: The group of progressive cutting materials can include non-traditional, emerging and less-used materials that can be an efficient use of cutting their lead to a quantum leap in the field of machining. This is essentially a “superhard” materials (STM) based on polycrystalline diamond (PCD) and polycrystalline cubic boron nitride (PCBN) cutting performance ceramics and development is constantly "perfecting" fine coated cemented carbides. The latter cutting materials are broken down by two parameters, toughness and hardness. A variation of alloying elements is always possible to improve only one of each parameter. Reducing the size of the core on the other hand doing achieves "contradictory" properties, namely to increase both hardness and toughness.
Abstract: Nanotechnology has multiple and enormous advantages for all application. Therefore, this research is carried out to synthesize and characterize bimetallic iron with copper nanoparticles. After synthesizing nano zero valent iron by reduction of ferric chloride by sodium borohydride under nitrogen purging environment, bimetallic iron with copper nanoparticles are synthesized by varying different loads of copper chloride. Due to different standard potential (E0) values of copper and iron, copper is coupled with iron at (Cu to Fe ratio of 1:5, 1:6.7, 1:10, 1:20). It is found that the resulted bimetallic Fe/Cu nanoparticles are composing phases of iron and copper. According to the diffraction patterns indicating the state of chemical combination of the bimetallic nanoparticles, the particles are well-combined and crystalline sizes are less than 1000Ao (or 100nm). Specifically, particle sizes of synthesized bimetallic Fe/Cu nanoparticles are ranging from 44.583 nm to 85.149 nm.
Abstract: Floating tablets of Marichyadi Vati were developed with an aim to prolong its gastric residence time and increase the bioavailability of drug. Rapid gastrointestinal transit could result in incomplete drug release from the drug delivery system above the absorption zone leading to diminished efficacy of the administered dose. The tablets were prepared by wet granulation technique, using HPMC E50 LV act as Matrixing agent, Carbopol as floating enhancer, microcrystalline cellulose as binder, Sodium bi carbonate as effervescent agent with other excipients. The simplex lattice design was used for selection of variables for tablets formulation. Formulation was optimized on the basis of floating time and in vitro drug release. The results showed that the floating lag time for optimized formulation was found to be 61 second with about 97.32 % of total drug release within 3 hours. The vitro release profiles of drug from the formulation could be best expressed zero order with highest linearity r2 = 0.9943. It was concluded that the gastroretentive drug delivery system can be developed for Marichyadi Vati containing Piperine to increase the residence time of the drug in the stomach and thereby increasing bioavailability.
Abstract: Polybag and mulch film in agricultural field are used plastics which caused environmental problems after transplantation and planting processes due to the discarded wastes. Thus a degradable polybag was designed in this study to replace non degradable polybag with natural biodegradable resin that is widely available, namely sago starch (SS) and polyvinyl alcohol (PVA). Hybrid blend consists of SS, PVA and linear low density polyethylene (LLDPE) was compounded at different ratios. The thermal and mechanical properties of the blends were investigated. Hybrid films underwent landfill degradation tests for up to 2 months. The films showed gelation and melting transition existed for all three systems with significant melting peaks by LLDPE and PVA. All hybrid blends loses its LLDPE semi crystalline characteristics as PVA and SS systems had disrupted crystallinity and enhanced the amorphosity of the hybrid system. Generally, blending SS with PVA improves the mechanical properties of the SS based materials. Tensile strength of each film was also decreased with the increase of SS contents while its modulus had increased with SS content.
Abstract: Chitosan (CH) material reinforced by bioactive glass (46S6) was fabricated. 46S6 containing 17% wt% CH was studied in vitro and in vivo. Physicochemical techniques, such as Fourier transform infrared spectroscopy (FT-IR), coupled plasma optical emission spectrometry (ICP-OES) analysis were used. The behavior of 46S6CH17 was studied by measuring the in situ pH in a SBF solution. The 46S6CH17 was implanted in the rat femoral condyl. In vitro 46S6CH17 gave an FTIR - spectrum in which three absorption bands with the maxima at 565, 603 and 1039cm-1 after 3 days of soaking in physiological solution. They are assigned to stretching vibrations of PO4^3- group in phosphate crystalline. Moreover, the pH measurement was decreased in the SBF solution. The stability of the calcium phosphate precipitation depended on the pH value. In vivo, a rise in the Ca and phosphate P ions concentrations in the implanted microenvironment was determined.
Abstract: In this study, the phase transition characteristics of flame-synthesized γ-Al2O3 nanoparticles to α-Al2O3 have been investigated. The nanoparticles were synthesized by using a coflow hydrogen diffusion flame. The phase transition and particle characteristics of the Al2O3 nanoparticles were determined by examining the crystalline structure and the shape of the collected nanoparticles before and after the heat treatment. The morphology and crystal structure of the Al2O3 nanoparticles were determined from SEM images and XRD analyses, respectively. The measured specific surface area and averaged particle size were 63.44m2/g and 23.94nm, respectively. Based on the scanning electron microscope images and x-ray diffraction patterns, it is believed that the onset temperature of the phase transition to α-Al2O3 was existed near 1200oC. The averaged diameters of the sintered particles heat treated at 1,260oC were approximately 80nm.
Abstract: Silicon photonics has generated an increasing interest in recent years mainly for optical communications optical interconnects in microelectronic circuits or bio-sensing applications. The development of elementary passive and active components (including detectors and modulators), which are mainly fabricated on the silicon on insulator platform for CMOS-compatible fabrication, has reached such a performance level that the integration challenge of silicon photonics with microelectronic circuits should be addressed. Since crystalline silicon can only be grown from another silicon crystal, making it impossible to deposit in this state, the optical devices are typically limited to a single layer. An alternative approach is to integrate a photonic layer above the CMOS chip using back-end CMOS fabrication process. In this paper, various materials, including silicon nitride, amorphous silicon, and polycrystalline silicon, for this purpose are addressed.
Abstract: The deposition of diamond films on a Si3N4 substrate
is an attractive technique for industrial applications because of the
excellent properties of diamond. Pretreatment of substrate is very
important prior to diamond deposition to promote nucleation and
adhesion between coating and substrate. Deposition of
nanocrystalline diamonds films on silicon nitride substrate have been
carried out by HF-CVD technique using mixture of methane and
hydrogen gases. Different pretreatment of substrate including
chemical etching consists of hot acid etching and basic etching and
mechanical etching were used to study the quality of diamond formed
on the substrate. The structure and morphology of diamond coating
have been studied using X-ray Diffraction (XRD) and Scanning
Electron Microscope (SEM) while diamond film quality has been
characterized using Raman spectroscopy. AFM was used to
investigate the effect of chemical etching and mechanical
pretreatment on the surface roughness of the substrates and the
resultant morphology of nanocrystalline diamond. It was found that
diamond film deposited on as-received, basic etched and grinded
substrate shows the morphology of cauliflower while blasted and
acidic etched substrates produce smooth, continuous diamond film.
However, the Raman investigation did not show any deviation in
quality of diamond film for any pretreatment.
Abstract: The tensile properties of Mg-3%Al nanocrystalline
alloys were investigated at different test environment. Bulk
nanocrystalline samples of these alloy was successfully prepared by
mechanical alloying (MA) followed by cold compaction, sintering,
and hot extrusion process. The crystal size of the consolidated milled
sample was calculated by X-Ray line profile analysis. The
deformation mechanism and microstructural characteristic at
different test condition was discussed extensively. At room
temperature, relatively lower value of activation volume (AV) and
higher value of strain rate sensitivity (SRS) suggests that new rate
controlling mechanism accommodating plastic flow in the present
nanocrystalline sample. The deformation behavior and the
microstructural character of the present samples were discussed in
details.
Abstract: In this study, ZnO nano rods and ZnO ultrafine particles were synthesized by Gel-casting method. The synthesized ZnO powder has a hexagonal zincite structure. The ZnO aggregates with rod-like morphology are typically 1.4 μm in length and 120 nm in diameter, which consist of many small nanocrystals with diameters of 10 nm. Longer wires connected by many hexahedral ZnO nanocrystals were obtained after calcinations at the temperature over 600° C.The crystalline structures and morphologies of the powder have been characterized by X-ray diffraction(XRD) and Scaning electron microscopy (SEM).The result shows that the different preparation conditions such as concentration H2O, calcinations time and calcinations temperature have a lot of influences upon the properties of nano ZnO powders, an increase in the temperature of the calcinations results in an increase of the grain size and also the increase of the calcinations time in high temperature makes the size of the grains bigger. The existences of extra watter prevent nano grains from improving like rod morphology. We have obtained the smallest grain size of ZnO powder by controlling the process conditions. Finally In a suitable condition, a novel nanostructure, namely bi-rod-like ZnO nano rods was found which is different from known ZnO nanostructures.
Abstract: Nylon 6-clay hybrid/neat nylon 6, sheath/core
bicomponent nanocomposite fibers containing 4 wt% of clay in
sheath section were melt spun at different take-up speeds. Their
orientation and crystalline structure were compared to those of neat
nylon 6 fibers. Birefringence measurements showed that the
orientation development in sheath and core parts of bicomponent
fibers was different. Crystallinity results showed that clay did not act
as a nucleating agent for bicomponent fibers. The neat nylon 6 fiber
had a smooth surface while striped pattern was appeared on the
surface of bicomponent fiber containing clay due to thermal
shrinkage of the core part.
Abstract: Environmental decision making, particularly about
hazardous waste management, is inherently exposed to a high
potential conflict, principally because of the trade-off between sociopolitical,
environmental, health and economic factors. The need to
plan complex contexts has led to an increasing request for decision
analytic techniques as support for the decision process. In this work,
alternative systems of asbestos-containing waste management
(ACW) in Puglia (Southern Italy) were explored by a multi-criteria
decision analysis. In particular, through Analytic Hierarchy Process
five alternatives management have been compared and ranked
according to their performance and efficiency, taking into account
environmental, health and socio-economic aspects. A separated
valuation has been performed for different temporal scale. For short
period results showed a narrow deviation between the disposal
alternatives “mono-material landfill in public quarry" and “dedicate
cells in existing landfill", with the best performance of the first one.
While for long period “treatment plant to eliminate hazard from
asbestos-containing waste" was prevalent, although high energy
demand required to achieve the change of crystalline structure. A
comparison with results from a participative approach in valuation
process might be considered as future development of method
application to ACW management.
Abstract: We investigated a modified thermal evaporation
method in the growth process of ZnO nanowires. ZnO nanowires
were fabricated on p-type silicon substrates without using a metal
catalyst. A simple horizontal double-tube system along with
chemical vapor diffusion of the precursor was used to grow the ZnO
nanowires. The substrates were placed in different temperature
zones, and ZnO nanowires with different diameters were obtained for
the different substrate temperatures. In addition to the nanowires,
ZnO microdiscs with different diameters were obtained on another
substrate, which was placed at a lower temperature than the other
substrates. The optical properties and crystalline quality of the ZnO
nanowires and microdiscs were characterized by room temperature
photoluminescence (PL) and Raman spectrometers. The PL and
Raman studies demonstrated that the ZnO nanowires and microdiscs
grown using such set-up had good crystallinity with excellent optical
properties. Rectifying behavior of ZnO/Si heterostructures was
characterized by a simple DC circuit.
Abstract: The nanotechnology based on epitaxial systems
includes single or arranged misfit dislocations. In general, whatever
is the type of dislocation or the geometry of the array formed by the
dislocations; it is important for experimental studies to know exactly
the stress distribution for which there is no analytical expression [1,
2]. This work, using a numerical analysis, deals with relaxation of
epitaxial layers having at their interface a periodic network of edge
misfit dislocations. The stress distribution is estimated by using
isotropic elasticity. The results show that the thickness of the two
sheets is a crucial parameter in the stress distributions and then in the
profile of the two sheets.
A comparative study between the case of single dislocation and
the case of parallel network shows that the layers relaxed better when
the interface is covered by a parallel arrangement of misfit.
Consequently, a single dislocation at the interface produces an
important stress field which can be reduced by inserting a parallel
network of dislocations with suitable periodicity.
Abstract: Copper based composites reinforced with WC and Ti
particles were prepared using planetary ball-mill. The experiment
was designed by using Taguchi technique and milling was carried out
in an air for several hours. The powder was characterized before and
after milling using the SEM, TEM and X-ray for microstructure and
for possible new phases. Microstructures show that milled particles
size and reduction in particle size depend on many parameters. The
distance d between planes of atoms estimated from X-ray powder
diffraction data and TEM image. X-ray diffraction patterns of the
milled powder did not show clearly any new peak or energy shift, but
the TEM images show a significant change in crystalline structure of
corporate on titanium in the composites.