Abstract: At the present work, highly transparent strip type
quasi-solid state dye-sensitized solar cells (DSSCs) were fabricated
through inkjet printing using nanocomposite TiO2 inks as raw
materials and tested under outdoor illumination conditions. The cells,
which can be considered as the structural units of large area modules,
were fully characterized electrically and electrochemically and after
the evaluation of the received results a large area DSSC module was
manufactured. The module design was a sandwich Z-interconnection
where the working electrode is deposited on one conductive glass and
the counter electrode on a second glass. Silver current collective
fingers were printed on the conductive glasses to make the internal
electrical connections and the adjacent cells were connected in series
and finally insulated using a UV curing resin to protect them from the
corrosive (I-/I3-) redox couple of the electrolyte. Finally, outdoor tests
were carried out to the fabricated dye-sensitized solar module and its
performance data were collected and assessed.
Abstract: Transparent nickel doped cobalt sulfide was fabricated
on a SnO2:F electrode and tested as an efficient electrocatalyst and as
an alternative to the expensive platinum counter electrode. In order to
investigate how this electrode could affect the electrical
characteristics of a dye-sensitized solar cell, we manufactured cells
with the same TiO2 photoanode sensitized with dye (N719) and
employing the same quasi-solid electrolyte, altering only the counter
electrode used. The cells were electrically and electrochemically
characterized and it was observed that the ones with the Ni doped
CoS2 outperformed the efficiency of the cells with the Pt counter
electrode (3.76% and 3.44% respectively). Particularly, the higher
efficiency of the cells with the Ni doped CoS2 counter electrode (CE)
is mainly because of the enhanced photocurrent density which is
attributed to the enhanced electrocatalytic ability of the CE and the
low charge transfer resistance at the CE/electrolyte interface.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: Sol-gel method has been used to fabricate
nanocomposite films on glass substrates composed halloysite clay
mineral and nanocrystalline TiO2. The methodology for the synthesis
involves a simple chemistry method utilized nonionic surfactant
molecule as pore directing agent along with the acetic acid-based solgel
route with the absence of water molecules. The thermal treatment
of composite films at 450oC ensures elimination of organic material
and lead to the formation of TiO2 nanoparticles onto the surface of
the halloysite nanotubes. Microscopy techniques and porosimetry
methods used in order to delineate the structural characteristics of the
materials. The nanocomposite films produced have no cracks and
active anatase crystal phase with small crystallite size were deposited
on halloysite nanotubes. The photocatalytic properties for the new
materials were examined for the decomposition of the Basic Blue 41
azo dye in solution. These, nanotechnology based composite films
show high efficiency for dye’s discoloration in spite of different
halloysite quantities and small amount of halloysite/TiO2 catalyst
immobilized onto glass substrates. Moreover, we examined the
modification of the halloysite/TiO2 films with silver particles in order
to improve the photocatalytic properties of the films. Indeed, the
presence of silver nanoparticles enhances the discoloration rate of the
Basic Blue 41 compared to the efficiencies obtained for unmodified
films.