Preparation and Characterization of Nylon 6-Clay Hybrid/Neat Nylon 6 Bicomponent Nanocomposite Fibers

Nylon 6-clay hybrid/neat nylon 6, sheath/core bicomponent nanocomposite fibers containing 4 wt% of clay in sheath section were melt spun at different take-up speeds. Their orientation and crystalline structure were compared to those of neat nylon 6 fibers. Birefringence measurements showed that the orientation development in sheath and core parts of bicomponent fibers was different. Crystallinity results showed that clay did not act as a nucleating agent for bicomponent fibers. The neat nylon 6 fiber had a smooth surface while striped pattern was appeared on the surface of bicomponent fiber containing clay due to thermal shrinkage of the core part.