Abstract: The deposition of diamond films on a Si3N4 substrate
is an attractive technique for industrial applications because of the
excellent properties of diamond. Pretreatment of substrate is very
important prior to diamond deposition to promote nucleation and
adhesion between coating and substrate. Deposition of
nanocrystalline diamonds films on silicon nitride substrate have been
carried out by HF-CVD technique using mixture of methane and
hydrogen gases. Different pretreatment of substrate including
chemical etching consists of hot acid etching and basic etching and
mechanical etching were used to study the quality of diamond formed
on the substrate. The structure and morphology of diamond coating
have been studied using X-ray Diffraction (XRD) and Scanning
Electron Microscope (SEM) while diamond film quality has been
characterized using Raman spectroscopy. AFM was used to
investigate the effect of chemical etching and mechanical
pretreatment on the surface roughness of the substrates and the
resultant morphology of nanocrystalline diamond. It was found that
diamond film deposited on as-received, basic etched and grinded
substrate shows the morphology of cauliflower while blasted and
acidic etched substrates produce smooth, continuous diamond film.
However, the Raman investigation did not show any deviation in
quality of diamond film for any pretreatment.
Abstract: Carbon nanotubes (CNTs) with their high mechanical,
electrical, thermal and chemical properties are regarded as promising
materials for many different potential applications. Having unique
properties they can be used in a wide range of fields such as
electronic devices, electrodes, drug delivery systems, hydrogen
storage, textile etc. Catalytic chemical vapor deposition (CCVD) is a
common method for CNT production especially for mass production.
Catalysts impregnated on a suitable substrate are important for
production with chemical vapor deposition (CVD) method. Iron
catalyst and MgO substrate is one of most common catalyst-substrate
combination used for CNT. In this study, CNTs were produced by
CCVD of acetylene (C2H2) on magnesium oxide (MgO) powder
substrate impregnated by iron nitrate (Fe(NO3)3•9H2O) solution. The
CNT synthesis conditions were as follows: at synthesis temperatures
of 500 and 800°C multiwall and single wall CNTs were produced
respectively. Iron (Fe) catalysts were prepared by with Fe:MgO ratio
of 1:100, 5:100 and 10:100. The duration of syntheses were 30 and
60 minutes for all temperatures and catalyst percentages. The
synthesized materials were characterized by thermal gravimetric
analysis (TGA), transmission electron microscopy (TEM) and Raman
spectroscopy.