Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: Sol-gel method has been used to fabricate
nanocomposite films on glass substrates composed halloysite clay
mineral and nanocrystalline TiO2. The methodology for the synthesis
involves a simple chemistry method utilized nonionic surfactant
molecule as pore directing agent along with the acetic acid-based solgel
route with the absence of water molecules. The thermal treatment
of composite films at 450oC ensures elimination of organic material
and lead to the formation of TiO2 nanoparticles onto the surface of
the halloysite nanotubes. Microscopy techniques and porosimetry
methods used in order to delineate the structural characteristics of the
materials. The nanocomposite films produced have no cracks and
active anatase crystal phase with small crystallite size were deposited
on halloysite nanotubes. The photocatalytic properties for the new
materials were examined for the decomposition of the Basic Blue 41
azo dye in solution. These, nanotechnology based composite films
show high efficiency for dye’s discoloration in spite of different
halloysite quantities and small amount of halloysite/TiO2 catalyst
immobilized onto glass substrates. Moreover, we examined the
modification of the halloysite/TiO2 films with silver particles in order
to improve the photocatalytic properties of the films. Indeed, the
presence of silver nanoparticles enhances the discoloration rate of the
Basic Blue 41 compared to the efficiencies obtained for unmodified
films.