Abstract: Two Lithium Disilicate (LD) glass ceramics based on
SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting
method. The glass rods were then fabricated into dental crowns via a
hot pressing at 900˚C and 850˚C in order to study the effect of the
pressing temperatures on the phase formation and microstructure of
the glasses. Different samples of as cast glass and heat treated
samples (600˚C and 700˚C) were used to press for investigating the
effect of an initial microstructure on the hot pressing technique. Xray
diffraction (XRD) and scanning electron microscopy (SEM) were
performed to determine the phase formation and microstructure of the
samples, respectively. XRD results show that the main crystalline
structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3,
Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with
different heat treatment temperatures exhibited a difference phase
formations but have less effect during pressing. SEM micrographs
showed the microstructure of Li2Si2O5 as lath-like shape in all
glasses. With increasing the initial heat treatment temperature, the
longer the lath-like crystals of lithium disilicate were increased
especially when using glass heat treatment at 700˚C followed by
pressing at 900˚C. This could be suggested that LD1 heat treatment at
700˚C which pressing at 900˚C presented the best formation by the
hot pressing and compiled microstructure.
Abstract: Calcium phosphate cement (CPC) is one of the most
attractive bioceramics due to its moldable and shape ability to fill
complicated bony cavities or small dental defect positions. In this
study, CPC was produced by using mixture of tetracalcium phosphate
(TTCP, Ca4O(PO4)2) and dicalcium phosphate anhydrous (DCPA,
CaHPO4) in equimolar ratio (1/1) with aqueous solutions of acetic
acid (C2H4O2) and disodium hydrogen phosphate dehydrate
(Na2HPO4.2H2O) in combination with sodium alginate in order to
improve theirs moldable characteristic. The concentration of the
aqueous solutions and sodium alginate were varied to investigate the
effect of different aqueous solutions and alginate on properties of the
cements. The cement paste was prepared by mixing cement powder
(P) with aqueous solution (L) in a P/L ratio of 1.0g/0.35ml. X-ray
diffraction (XRD) was used to analyses phase formation of the
cements. Setting time and compressive strength of the set CPCs were
measured using the Gilmore apparatus and Universal testing
machine, respectively.
The results showed that CPCs could be produced by using both
basic (Na2HPO4.2H2O) and acidic (C2H4O2) solutions. XRD results
show the precipitation of hydroxyapatite in all cement samples. No
change in phase formation among cements using difference
concentrations of Na2HPO4.2H2O solutions. With increasing
concentration of acidic solutions, samples obtained less
hydroxyapatite with a high dicalcium phosphate dehydrate leaded to
a shorter setting time. Samples with sodium alginate exhibited higher
crystallization of hydroxyapatite than that of without alginate as a
result of shorten setting time in a basic solution but a longer setting
time in an acidic solution. The stronger cement was attained from
samples using the acidic solution with sodium alginate; however the
strength was lower than that of using the basic solution.