Abstract: Asphalt pavement itself is a mixture made up of mainly aggregates, binders, and fillers that acts as a composition used for pavement construction. An experimental program was setup to determine the fatigue performance test of Asphalt with three different grades of conventional binders. Asphalt specimen has achieved the maximum optimum bulk density and air voids with a consistent bulk density of 2.3 t/m3, with an air void of 5% ± 0.5, before loading into the Asphalt Mixture Performance Tested (AMPT) for fatigue test. The number of cycles is defined as the point where phase angle drops, which is caused by the formation of cracks due to the increasing micro cracks when asphalt is undergoing repeated cycles of loading. Thus, the data collected are analyzed using the drop of phase angle as failure criteria. Based in the data analyzed, it is evident that the fatigue life of asphalt lies on the grade of binder. The result obtained shows that all specimens do experience a drop in phase angle due to macro cracks in the asphalt specimen.
Abstract: This paper investigates the application of metallic
coatings on high fiber volume fraction carbon/epoxy polymer matrix
composites. For the grip of the metallic layer, a method of modifying
the surface of the composite by introducing a mixture of copper and
steel powder (filler powders) which can reduce the impact of thermal
spray particles. The powder was introduced to the surface at the time
of the forming. Arc spray was used to project the zinc coating layer.
The substrate was grit blasted to avoid poor adherence. The porosity, microstructure, and morphology of layers are
characterized by optical microscopy, SEM and image analysis. The
samples were studied also in terms of hardness and erosion resistance.
This investigation did not reveal any visible evidence damage to the
substrates. The hardness of zinc layer was about 25.94 MPa and the
porosity was around (∼6.70%). The erosion test showed that the zinc
coating improves the resistance to erosion. Based on the results
obtained, we can conclude that thermal spraying allows the production
of protective coating on PMC. Zinc coating has been identified as a
compatible material with the substrate. The filler powders layer
protects the substrate from the impact of hot particles and allows
avoiding the rupture of brittle carbon fibers.
Abstract: This paper describes the development of new class of
epoxy based rice husk filled jute reinforced composites. Rice husk
flour is added in 0%, 1%, 3%, 5% by weight. Epoxy resin and
triethylenetetramine (T.E.T.A) is used as matrix and hardener
respectively. It investigates the mechanical properties of the
composites and a comparison is done for monolithic jute composite
and the filled ones. The specimens are prepared according to the
ASTM standards and experimentation is carried out using INSTRON
8801. The result shows that with the increase of filler percentage the
tensile properties increases but compressive and flexural properties
decreases.
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.
Abstract: The objective of this study was to synthesize and
characterize the poly(alkenoic acid)s with different molecular
structures, use these polymers to formulate a dental cement
restorative, and study the effect of molecular structures on reaction
kinetics, viscosity, and mechanical strengths of the formed polymers
and cement restoratives. In this study, poly(alkenoic acid)s with
different molecular structures were synthesized. The purified
polymers were formulated with commercial Fuji II LC glass fillers to
form the experimental cement restoratives. The reaction kinetics was
studied via 1HNMR spectroscopy. The formed restoratives were
evaluated using compressive strength, diametral tensile strength,
flexural strength, hardness and wear-resistance tests. Specimens were
conditioned in distilled water at 37oC for 24 h prior to testing. Fuji II
LC restorative was used as control. The results show that the higher
the arm number and initiator concentration, the faster the reaction
was. It was also found that the higher the arm number and branching
that the polymer had, the lower the viscosity of the polymer in water
and the lower the mechanical strengths of the formed restorative. The
experimental restoratives were 31-53% in compressive strength, 37-
55% in compressive modulus, 80-126% in diametral tensile strength,
76-94% in flexural strength, 4-21% in fracture toughness and 53-96%
in hardness higher than Fuji II LC. For wear test, the experimental
restoratives were only 5.4-13% of abrasive and 6.4-12% of attritional
wear depths of Fuji II LC in each wear cycle. The aging study also
showed that all the experimental restoratives increased their strength
continuously during 30 days, unlike Fuji II LC. It is concluded that
polymer molecular structures have significant and positive impact on
mechanical properties of dental cement restoratives.
Abstract: This study aims at developing a novel cold asphalt
concrete binder course mixture by using Ordinary Portland Cement
(OPC) as a replacement for conventional mineral filler (0%-100%)
with new by-product material (LJMU-A2) used as a supplementary
cementitious material. With this purpose, cold asphalt concrete binder
course mixtures with cationic emulsions were studied by means of
stiffness modulus whereas water sensitivity was assessed by
measuring the stiffness modulus ratio before and after sample
conditioning.
The results indicate that a substantial enhancement in the stiffness
modulus and a considerable improvement of water sensitivity
resistance is achieved by adding LJMU-A2 to the cold asphalt
mixtures as a supplementary cementitious material. Moreover, the
addition of LJMU-A2 to those mixtures leads to a stiffness modulus
after 2-day curing compared to that obtained with Portland cement,
which occurs after 7-day curing.
Abstract: It is an established fact that polymers have several
physical limitations such as low stiffness and low resistance to
impact on loading. Hence, polymers do not usually have requisite
mechanical strength for application in various fields. The
reinforcement by high strength fibers provides the polymer
substantially enhanced mechanical properties and makes them more
suitable for a large number of diverse applications. This research
evaluates the effects of particulate Cow bone and Groundnut shell
additions on the mechanical properties and microstructure of cow
bone and groundnut shell reinforced epoxy composite in order to
assess the possibility of using it as a material for engineering
applications. Cow bone and groundnut shell particles reinforced with
epoxy (CBRPC and GSRPC) was prepared by varying the cow bone
and groundnut shell particles from 0-25 wt% with 5 wt% intervals. A
Hybrid of the Cow bone and Groundnut shell (HGSCB) reinforce
with epoxy was also prepared. The mechanical properties of the
developed composites were investigated. Optical microscopy was
used to examine the microstructure of the composites. The results
revealed that mechanical properties did not increase uniformly with
additions in filler but exhibited maximum properties at specific
percentages of filler additions. From the Microscopic evaluation, it
was discovered that homogeneity decreases with increase in % filler,
this could be due to poor interfacial bonding.
Abstract: An experimental and analytical research on shear
buckling of a comparably large polymer composite I-section is
presented. It is known that shear buckling load of a large span
composite beam is difficult to determine experimentally. In order to
sensitively detect shear buckling of the tested I-section, twenty strain
rosettes and eight displacement sensors were applied and attached on
the web and flange surfaces. The tested specimen was a pultruded
composite beam made of vinylester resin, E-glass, carbon fibers and
micro-fillers. Various coupon tests were performed before the shear
buckling test to obtain fundamental material properties of the Isection.
An asymmetric four-point bending loading scheme was
utilized for the shear test. The loading scheme resulted in a high shear
and almost zero moment condition at the center of the web panel. The
shear buckling load was successfully determined after analyzing the
obtained test data from strain rosettes and displacement sensors. An
analytical approach was also performed to verify the experimental
results and to support the discussed experimental program.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: In the present work, the dielectric properties of
Epoxy/MWCNT-muscovite HYBRID and MIXED composites based
on a ratio 30:70 were studied. The multi-wall carbon nanotubes
(MWCNT) were prepared using two methods: (a) MWCNTmuscovite
hybrids were synthesised by chemical vapour deposition
(CVD) and (b) physically mixing muscovite with MWCNT. The
effects of different preparation of the composites and filler loading
were evaluated. It was revealed that the dielectric constants of
HYBRID epoxy composites are slightly higher than MIXED epoxy
composites. It was also indicated that the dielectric constant increased
by increasing the MWCNT filler loading.
Abstract: The dissimilar joint between aluminum/titanium
alloys (Al 6082 and Ti G2) were successfully achieved by CO2 laser
welding with a single pass and without filler material using the
overlap joint design. Laser welding parameters ranges combinations
were experimentally determined using Taguchi approach with the
objective of producing welded joint with acceptable welding profile
and high quality of mechanical properties. In this study a joining of
dissimilar Al 6082 / Ti G2 was resulted in three distinct regions
fusion area in the weldment. These regions are studied in terms of its
microstructural characteristics and microhardness which are directly
affecting the welding quality.
The weld metal was mainly composed of martensite alpha prime.
In two different metals in the two different sides of joint HAZ, grain
growth was detected. The microhardness of the joint distribution also
has shown microhardness increasing in the HAZ of two base metals
and a varying microhardness in fusion zone.
Abstract: Thin-walled elements with a matrix set on a base of
high-valuable Portland cement with dispersed reinforcement from
alkali-resistant glass fibres are used in a range of applications as
claddings of buildings and infrastructure constructions as well as
various architectural elements of residential buildings.
Even though their elementary thickness and therefore total weight
is quite low, architects and building companies demand on even
further decreasing of the bulk density of these fibre-cement elements
for the reason of loading elimination of connected superstructures
and easier assembling in demand conditions.
By the means of various kinds of light-weight aggregates it is
possible to achieve light-weighing of these composite elements.
From the range of possible fillers with different material properties
granulated expanded glass worked the best.
By the means of laboratory testing an effect of two fillers based on
expanded glass on the fibre reinforced cement composite was
verified.
Practical applicability was tested in the production of commonly
manufactured glass fibre reinforced concrete elements, such as
channels for electrical cable deposition, products for urban equipment
and especially various cladding elements.
Even though these are not structural elements, it is necessary to
evaluate also strength characteristics and resistance to environment
for their durability in certain applications.
Abstract: Sustainability and eco-friendly requirement of
engineering materials are sort for in recent times, thus giving rise to
the development of bio-composites. However, the natural fibres to
matrix interface interactions remain a key issue in getting the desired
mechanical properties from such composites. Treatment of natural
fibres is essential in improving matrix to filler adhesion, hence
improving its mechanical properties. In this study, investigations
were carried out to determine the effect of sodium hydroxide
treatment on the tensile, flexural, impact and hardness properties of
crushed and uncrushed Luffa cylindrica fibre reinforced recycled low
density polyethylene composites. The LC (Luffa cylindrica) fibres
were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium
hydroxide (NaOH) concentrations for a period of 24 hours under
room temperature conditions. A formulation ratio of 80/20 g (matrix
to reinforcement) was maintained for all developed samples. Analysis
of the results showed that the uncrushed luffa fibre samples gave
better mechanical properties compared with the crushed luffa fibre
samples. The uncrushed luffa fibre composites had a maximum
tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively
corresponding to a young modulus and flexural modulus of 21.08
MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration
respectively. Results obtained in the research showed that NaOH
treatment with the 8% NaOH concentration improved the mechanical
properties of the LC fibre reinforced composites when compared with
other NaOH treatment concentration values.
Abstract: This study was developed to compare the behavior
and the ability of polymer foam composites towards sound absorption
test of Shorea leprosula wood (SL) of acid hydrolysis treatment with
particle size
Abstract: Waste silicon carbide (waste SiC) filled high-density
polyethylene (HDPE) with and without surface modifiers were
studied. Two types of surface modifiers namely; high-density
polyethylene-grafted-maleic anhydride (HDPE-g-MA) and 3-aminopropyltriethoxysilane have been used in this study. The
composites were produced using a two roll mill, extruder and shaped
in a hydraulic compression molding machine. The mechanical
properties of polymer composites such as flexural strength and
modulus, impact strength, tensile strength, stiffness and hardness
were investigated over a range of compositions. It was found that,
flexural strength and modulus, tensile modulus and hardness
increased, whereas impact strength and tensile strength decreased
with the increasing in filler contents, compared to the neat HDPE. At
similar filler content, the effect of both surface modifiers increased
flexural modulus, impact strength, tensile strength and stiffness but
reduced the flexural strength. Morphological investigation using
SEM revealed that the improvement in mechanical properties was
due to enhancement of the interfacial adhesion between waste SiC
and HDPE.
Abstract: Bio-composites derived from plant fiber and/or bioderived
polymer, are likely more ecofriendly and demonstrate
competitive performance with petroleum based composites. In this
research, the bio phenol-formaldehyde (bio-PF) was used as a matrix
and oil palm empty fruit bunch fiber (EFB) as reinforcement. The
matrix was synthesized via liquefaction and condensation to enhance
the combination of phenol and formaldehyde, during the process.
Then, the bio-PF was mixed with different percentage of EFB (5%,
10%, 15% and 20%) and molded at 180oC. The samples that viewed
under scanning electron microscopy (SEM) showed an excellent
wettability and interaction between EFB and matrix. Samples of 10%
EFB gave the optimum properties of impact and hardness meanwhile
sample 15% of EFB gave the highest reading of flexural modulus
(MOE) and flexural strength (MOR). For thermal stability analysis, it
was found that the weight loss and the activation energy (Ea) of the
bio-composites samples were decreased as the filler content
increased.
Abstract: In this paper, the electromagnetic shielding
characteristics of an up-to-date typical carbon filler material, carbon
fiber used with a metal mesh were investigated. Carbon fiber
12k-prepregs, where carbon fibers were impregnated with epoxy, were
laminated with wire meshes, vacuum bag-molded and hardened to
manufacture hybrid-type specimens, with which an electromagnetic
shield test was performed in accordance with ASTM D4935-10,
through which was known as the most excellent reproducibility is
obtainable among electromagnetic shield tests. In addition, glass fiber
prepregs whose electromagnetic shielding effect were known as
insignificant were laminated and formed with wire meshes to verify
the validity of the electromagnetic shield effect of wire meshes in
order to confirm the electromagnetic shielding effect of metal meshes
corresponding existing carbon fiber 12k-prepregs. By grafting carbon
fibers, on which studies are being actively underway in the
environmental aspects and electromagnetic shielding effect, with
hybrid-type wire meshes that were analysed through the tests, in this
study, the applicability and possibility are proposed.
Abstract: In this study, epoxy composite specimens reinforced
with multi-walled carbon nanotube filler were fabricated using shear
mixer and ultra-sonication processor. The mechanical and thermal
properties of the fabricated specimens were measured and evaluated.
From the electron microscope images and the results from the
measurements of tensile strengths, the specimens having 0.6 wt%
nanotube content show better dispersion and higher strength than those
of the other specimens. The Young’s moduli of the specimens
increased as the contents of the nanotube filler in the matrix were
increased. The specimen having a 0.6 wt% nanotube filler content
showed higher thermal conductivity than that of the other specimens.
While, in the measurement of thermal expansion, specimens having
0.4 and 0.6 wt% filler contents showed a lower value of thermal
expansion than that of the other specimens. On the basis of the
measured and evaluated properties of the composites, we believe that
the simple and time-saving fabrication process used in this study was
sufficient to obtain improved properties of the specimens.
Abstract: This paper illustrates the effect of nano Magnesium
Hydroxide (MH) loading on the thermal properties of Low Density
Polyethylene (LDPE)/Poly (ethylene-co vinyl acetate) (EVA) nano
composite. Thermal studies were conducted, as it understanding is
vital for preliminary development of new polymeric systems.
Thermal analysis of nanocomposite was conducted using thermo
gravimetric analysis (TGA), and differential scanning calorimetry
(DSC). Major finding of TGA indicated two main stages of
degradation process found at (350 ± 25oC) and (480 ± 25oC)
respectively. Nano metal filler expressed better fire resistance as it
stand over high degree of temperature. Furthermore, DSC analysis
provided a stable glass temperature around 51 (±1oC) and captured
double melting point at 84 (±2oC) and 108 (±2oC). This binary
melting point reflects the modification of nano filler to the polymer
matrix forming melting crystals of folded and extended chain. The
percent crystallinity of the samples grew vividly with increasing filler
content. Overall, increasing the filler loading improved the
degradation temperature and weight loss evidently and a better
process and phase stability was captured in DSC.
Abstract: Laser beam welding for the dissimilar Titanium and
Aluminium thin sheets is an emerging area which is having wider
applications in aerospace, aircraft, automotive, electronics and in
other industries due to its high speed, non-contact, precision with low
heat effects, least welding distortion, low labor costs and convenient
operation. Laser beam welding of dissimilar metal combinations are
increasingly demanded due to high energy densities with small fusion
and heat affected zones. Furthermore, no filler or electrode material is
required and contamination of weld is also very small. The present
study is to reviews the influence of different parameters like laser
power, welding speed, power density, beam diameter, focusing
distance and type of shielding gas on the mechanical properties of
dissimilar metal combinations like SS/Al, Cu/Al and Ti/Al focusing
on aluminum to other materials. Research findings reveal that Ti/Al
combination gives better metallurgical and mechanical properties
than other combinations such as SS/Al and Cu/Al.