Abstract: Nanomaterials have many applications in the field of asphalt paving. Two locally produced nanomaterials were used in the asphalt binder modification. The nanomaterials used are Nanosilica (NS), and Nanoclay (NC). The virgin asphalt binder was characterized by the conventional tests. The bitumen was modified by 3%, 5% and 7% of NS and NC. The penetration index (PI), and the retaining penetration (RP) was calculated based on the results of the penetration and the softening point tests. The results show that the RP becomes 95.35% at 5% NS modified bitumen and reaches 97.56% when bitumen is modified with 3% NC. The results show significant improvement in the bitumen stiffness when modified by the two types of nanomaterials, either fresh or aged (stored).
Abstract: The main objective of this paper is to evaluate the use of plastic waste as a low cost asphalt binder modifier. For this purpose Marshall mix design procedure was used. Marshall mix design procedure seeks to select the Optimum Binder Content (OBC) to be added to a specific aggregate blend resulting in a mixture that satisfies the desired properties of strength and durability. In order to evaluate the plastic waste modified (PWM) asphalt mixtures, the OBC for the conventional asphalt mix was first identified, and then different percentages of crushed plastic waste by weight of the identified OBC were tested. Marshall test results for the modified asphalt mixtures were analyzed to find the optimum PWM content. Finally, the static indirect tensile strength (IDT) was determined for all mixtures using the splitting tensile test. It was found that PWM content of 7.43% by weight of OBC is recommended as the optimum PWM content needed for enhancing the performance of asphalt mixtures. It enhanced stability by 42.56%, flow by 89.91% and strength by 13.54%. This would lead to a more durable pavement by improving the pavement resistance to fatigue cracking and rutting.
Abstract: Modification of asphalt is a fundamental method around the world mainly on the purpose of providing more durable pavements which lead to diminish repairing cost during the lifetime of highways. Various polymers such as styrene-butadiene-styrene (SBS) and ethylene vinyl acetate (EVA) make up the greater parts of the all-over asphalt modifiers generally providing better physical properties of asphalt by decreasing temperature dependency which eventually diminishes permanent deformation on highways such as rutting. However, some waste and low-cost materials such as recycled plastics and ground rubber tire have been attempted to utilize in asphalt as modifier instead of manufactured polymer modifiers due to decreasing the eventual highway cost. On the other hand, the usage of recycled plastics has become a worldwide requirement and awareness in order to decrease the pollution made by waste plastics. Hence, finding an area in which recycling plastics could be utilized has been targeted by many research teams so as to reduce polymer manufacturing and plastic pollution. To this end, in this paper, thermoplastic dynamic vulcanizate (TDV) obtained from recycled post-consumer polyethylene and ground tire rubber (GTR) were used to provide an efficient modifier for asphalt which decreases the production cost as well and finally might provide an ecological solution by decreasing polymer disposal problems. TDV was synthesized by the chemists in the research group by means of the abovementioned components that are considered as compatible physical characteristic of asphalt materials. TDV modified asphalt samples having different rate of proportions of 3, 4, 5, 6, 7 wt.% TDV modifier were prepared. Conventional tests, such as penetration, softening point and roll thin film oven (RTFO) tests were performed to obtain fundamental physical and aging properties of the base and modified binders. The high temperature performance grade (PG) of binders was determined by Superpave tests conducted on original and aged binders. The multiple stress creep and recovery (MSCR) test which is relatively up-to-date method for classifying asphalts taking account of their elasticity abilities was carried out to evaluate PG plus grades of binders. The results obtained from performance grading, and MSCR tests were also evaluated together so as to make a comparison between the methods both aiming to determine rheological parameters of asphalt. The test results revealed that TDV modification leads to a decrease in penetration, an increase in softening point, which proves an increasing stiffness of asphalt. DSR results indicate an improvement in PG for modified binders compared to base asphalt. On the other hand, MSCR results that are compatible with DSR results also indicate an enhancement on rheological properties of asphalt. However, according to the results, the improvement is not as distinct as observed in DSR results since elastic properties are fundamental in MSCR. At the end of the testing program, it can be concluded that TDV can be used as modifier which provides better rheological properties for asphalt and might diminish plastic waste pollution since the material is 100% recycled.
Abstract: This paper presents the results of the development of asphalt nanocomposites containing carbon nanotubes (CNTs) with high resistance to permanent deformation, aiming to increase the performance of asphalt surfaces in relation to the rutting problem. Asphalt nanocomposites were prepared with the addition of different proportions of CNTs (1%, 2% and 3%) in relation to the weight of asphalt binder. The base binder used was a conventional binder (50-70 penetration) classified as PG 58-22. The optimum percentage of CNT addition in the asphalt binder (base) was determined through the evaluation of the rheological and empirical characteristics of the nanocomposites produced. In order to evaluate the contribution and the effects of the nanocomposite (optimized) in relation to the rutting, the conventional and nanomodified asphalt mixtures were tested in a French traffic simulator (Orniéreur). The results obtained demonstrate the efficient contribution of the asphalt nanocomposite containing CNTs to the resistance to permanent deformation of the asphalt mixture.
Abstract: Fibers are extensively used in civil engineering applications for many years. In this study, empty fruit bunch of date palm trees were used to produce cellulose fiber that were used as additives in the asphalt binder. Two sizes (coarse and fine) of cellulose fibers were pre-blended in PG64-22 binder with various contents of 1.5%, 3%, 4.5%, 6%, and 7.5% by weight of asphalt binder. The physical and rheological properties of fiber modified asphalt binders were tested by using conventional tests such as penetration, softening point and viscosity; and SHRP test such as dynamic shear rheometer. The results indicated that the fiber modified asphalt binders were higher in softening point, viscosity, and complex shear modulus, and lower in penetration compared to pure asphalt. The fiber modified binders showed an improvement in rheological properties since it was possible to raise the control binder (pure asphalt) PG from 64 to 70 by adding 6% (by weight) of either fine or coarse fibers. Such improvement in stiffness of fiber modified binder is expected to improve pavement resistance to rutting.
Abstract: Flexible pavement made with neat asphalt binder is not enough to resist heavy traffic loads as well as harsh environmental condition found in Riyadh region. Therefore, there is a need to modify asphalt binder with polymers to satisfy such conditions. There are several types of polymers that are used to modify asphalt binder. The objective of this paper is to compare the rheological properties of six polymer modified asphalt binders (Lucolast7010, Anglomak2144, Paveflex140, SBS KTR401, EE-2 and Crumb rubber) obtained from asphalt manufacturer plants. The rheological properties of polymer modified asphalt binders were tested using conventional tests such as penetration, softening point and viscosity; and SHRP tests such as dynamic shear rheometer and bending beam rheometer. The results have indicated that the polymer modified asphalt binders have lower penetration and higher softening point than neat asphalt indicating an improvement in stiffness of asphalt binder, and as a result, more resistant to rutting. Moreover, the dynamic shear rheometer results have shown that all modifiers used in this study improved the binder properties and satisfied the Superpave specifications except SBS KTR401 which failed to satisfy the rutting parameter (G*/sinδ).
Abstract: Asphalt pavement itself is a mixture made up of mainly aggregates, binders, and fillers that acts as a composition used for pavement construction. An experimental program was setup to determine the fatigue performance test of Asphalt with three different grades of conventional binders. Asphalt specimen has achieved the maximum optimum bulk density and air voids with a consistent bulk density of 2.3 t/m3, with an air void of 5% ± 0.5, before loading into the Asphalt Mixture Performance Tested (AMPT) for fatigue test. The number of cycles is defined as the point where phase angle drops, which is caused by the formation of cracks due to the increasing micro cracks when asphalt is undergoing repeated cycles of loading. Thus, the data collected are analyzed using the drop of phase angle as failure criteria. Based in the data analyzed, it is evident that the fatigue life of asphalt lies on the grade of binder. The result obtained shows that all specimens do experience a drop in phase angle due to macro cracks in the asphalt specimen.
Abstract: Asphalt concrete pavements have a short life cycle,
failing mainly due to temperature changes, traffic loading and ageing.
Modified asphalt mixtures provide the technology to produce a
bituminous binder with improved viscoelastic properties, which
remain in balance over a wider temperature range and loading
conditions. In this research, 60/70 penetration grade asphalt binder
was modified by adding 2, 4, 6, 8 and 10 percent by weight of asphalt
binder following the wet process and the mineral aggregate was
modified by adding 1, 2, 3, 4 and 5 percent crumb rubber by volume
of the mineral aggregate following the dry process. The LDPE
modified asphalt binder rheological properties were evaluated. The
laboratory results showed an increase in viscosity, softening point
and stiffness of the binder. The modified asphalt was then used in
preparing asphalt mixtures by Marshall Mix design procedure. The
Marshall Stability values for mixes containing 2% crumb rubber and
4% LDPE were found to be 30% higher than the conventional asphalt
concrete mix.
Abstract: Utilization of waste material in asphalt pavement
would be beneficial in order to find an alternative solution to increase
service life of asphalt pavement and reduce environmental pollution
as well. One of these waste materials is Polyethylene Terephthalate
(PET) which is a type of polyester material and is produced in a large
extent. This research program is investigating the effects of adding
waste PET particles into the asphalt mixture with a maximum size of
2.36 mm. Different percentages of PET were added into the mixture
during dry process. Gap-graded mixture (SMA 14) and PG 80-100
asphalt binder have been used for this study. To evaluate PET
reinforced asphalt mixture different laboratory investigations have
been conducted on specimens. Marshall Stability test was carried
out. Besides, stiffness modulus test and indirect tensile fatigue test
were conducted on specimens at optimum asphalt content. It was
observed that in many cases PET reinforced SMA mixture had better
mechanical properties in comparison with control mixture.
Abstract: This study has applied the L16 orthogonal array of the
Taguchi method to determine the optimized polymeric
Nanocomposite asphalt binder. Three control factors are defined as
polypropylene plastomer (PP), styrene-butadiene-styrene elastomer
(SBS) and Nanoclay. Four level of concentration contents are
introduced for prepared asphalt binder samples. all samples were
prepared with 4.5% of bitumen 60/70 content. Compressive strength
tests were carried out for defining the optimized sample via
QUALITEK-4 software. SBS with 3%, PP with 5 % and Nanoclay
with 1.5% of concentrations are defined as the optimized
Nanocomposite asphalt binders. The confirmation compressive
strength and also softening point tests showed that modification of
asphalt binders with this method, improved the compressive strength
and softening points of asphalt binders up to 55%.
Abstract: This paper characterizes the effects of artificial short
term aging in the laboratory on the rheological properties of virgin
80/100 penetration grade asphalt binder. After several years in
service, asphalt mixture started to deteriorate due to aging. Aging is a
complex physico-chemical phenomenon that influences asphalt
binder rheological properties causing a deterioration in asphalt
mixture performance. To ascertain asphalt binder aging effects, the
virgin, artificially aged and extracted asphalt binder were tested via
the Rolling Thin film Oven (RTFO), Dynamic Shear Rheometer
(DSR) and Rotational Viscometer (RV). A comparative study
between laboratory and field aging conditions were also carried out.
The results showed that the specimens conditioned for 85 minutes
inside the RTFO was insufficient to simulate the actual short term
aging caused that took place in the field under Malaysian field
conditions
Abstract: One of the important factors of cracks on the asphalt
pavements is bitumen aging that associated with the loss of volatile
components and oxidation of asphalt binder. This paper is about
effect of Styrene-Butadiene-Styrene (SBS) polymer on asphalt aging
In order to decrease asphalt aging effects. For this purpose samples of
base bitumen and SBS modified bitumen aged according to the
rolling thin film oven test (RTFOT) and pressure aging vessel (PAV),
respectively. Properties of each sample were evaluated using Fourier
Transform Infrared (FTIR) spectroscopy, n-heptane precipitation,
viscosity test, softening point test and penetration test. FT-IR
Analysis, showed lower oxidation of SBS modified bitumen than
base bitumen, after aging.