Abstract: Many sustainable approaches to generate electric energy have emerged in the last few decades; one of them is through solar cells. Yet, this also has the disadvantage of highly polluting inorganic semiconductor manufacturing processes. Therefore, the use of molecular semiconductors must be considered. In this work, allene compounds C24H26O4 and C24H26O5 were used as dopants to manufacture semiconductor films based on PbPc by high-vacuum evaporation technique. IR spectroscopy was carried out to determine the phase and any significant chemical changes which may occur during the thermal evaporation. According to UV-visible spectroscopy and Tauc’s model, the deposition process generated thin films with an activation energy range of 1.47 eV to 1.55 eV for direct transitions and 1.29 eV to 1.33 eV for indirect transitions. These values place the manufactured films within the range of low bandgap semiconductors. The flexible devices were manufactured: polyethylene terephthalate (PET), Indium tin oxide (ITO)/organic semiconductor/Cubic Close Packed (CCP). The characterization of the devices was carried out by evaluating electrical conductivity using the four-probe collinear method. I-V curves were obtained under different lighting conditions at room temperature. OS1 (PbPc/C24H26O4) showed an Ohmic behavior, while OS2 (PbPc/C24H26O5) reached higher current values at lower voltages. The results obtained show that the semiconductor devices doped with allene compounds can be used in the manufacture of optoelectronic devices.
Abstract: A core/trunk exoskeleton design has been produced that is aimed to assist the raise to stand motion. A 3D model was produced to examine the use of additive manufacturing as a core method for producing structural components for the exoskeleton presented. The two materials that were modelled for this simulation work were Polylatic acid (PLA) and polyethylene terephthalate with carbon (PET-C), and the central spinal cord of the design being Nitrile rubber. The aim of this study was to examine the use of 3D printed materials as the main skeletal structure to support the core of a human when moving raising from a resting position. The objective in this work was to identify if the 3D printable materials could be offered as an equivalent alternative to conventional more expensive materials, thus allow for greater access for production for home maintenance. A maximum load of lift force was calculated, and this was incrementally reduced to study the effects on the material. The results showed a total number of 8 simulations were run to study the core in conditions with no muscular support through to 90% of operational support. The study presents work in the form of a core/trunk exoskeleton that presents 3D printing as a possible alternative to conventional manufacturing.
Abstract: Manufacturing a composite material from post-consumer bottles is an interesting outlet since Madagascar is still facing the challenges of managing plastic waste on the one hand and appropriate waste treatment facilities are not yet developed on the other hand. New waste management options are needed to divert End-Of-Life (EOL) soft plastic wastes from landfills and incineration. Waste polyethylene terephthalate (PET) bottles might be considered as a valuable resource and recovered into polymer concrete. The methodology is easy to implement and appropriate to the local context in Madagascar. This approach will contribute to the production of ecological building materials that might be profitable for the environment and the construction sector. This work aims to study the feasibility of using the post-consumer PET bottles as an alternative binding agent instead of the conventional Portland cement and water. Then, the mechanical and physical properties of the materials were evaluated.
Abstract: The main objective of this paper is to evaluate the use of plastic waste as a low cost asphalt binder modifier. For this purpose Marshall mix design procedure was used. Marshall mix design procedure seeks to select the Optimum Binder Content (OBC) to be added to a specific aggregate blend resulting in a mixture that satisfies the desired properties of strength and durability. In order to evaluate the plastic waste modified (PWM) asphalt mixtures, the OBC for the conventional asphalt mix was first identified, and then different percentages of crushed plastic waste by weight of the identified OBC were tested. Marshall test results for the modified asphalt mixtures were analyzed to find the optimum PWM content. Finally, the static indirect tensile strength (IDT) was determined for all mixtures using the splitting tensile test. It was found that PWM content of 7.43% by weight of OBC is recommended as the optimum PWM content needed for enhancing the performance of asphalt mixtures. It enhanced stability by 42.56%, flow by 89.91% and strength by 13.54%. This would lead to a more durable pavement by improving the pavement resistance to fatigue cracking and rutting.
Abstract: This paper reports the effects of laser energy on the characteristics of bubbles generated in the weld zone and the formation of new chemical bonds at the Polyethylene Terephthalate (PET)/Ti joint interface in laser joining of PET to Ti. The samples were produced by using different laser energies ranging from 1.5 J – 6 J in steps of 1.5 J, while all other joining parameters remained unchanged. The types of chemical bonding at the joint interface were analysed by the x-ray photoelectron spectroscopy (XPS) depth-profiling method. The results show that the characteristics of the bubbles and the thickness of the chemically bonded interface, which contains the laser generated bonds of Ti–C and Ti–O, increase markedly with increasing laser energy input. The tensile failure load of the joint depends on the combined effect of the amount and distribution of the bubbles formed and the chemical bonding intensity of the joint interface.
Abstract: Concrete is strong in compression however weak in
tension. The tensile strength as well as ductile property of concrete
could be improved by addition of short dispersed fibers. Polyethylene
terephthalate (PET) fiber obtained from hand cutting or mechanical
slitting of plastic sheets generally used as discrete reinforcement in
substitution of steel fiber. PET fiber obtained from the former process
is in the form of straight slit sheet pattern that impart weaker
mechanical bonding behavior in the concrete matrix. To improve the
limitation of straight slit sheet fiber the present study considered two
additional geometry of fiber namely (a) flattened end slit sheet and
(b) deformed slit sheet. The mix for plain concrete was design for a
compressive strength of 25 MPa at 28 days curing time with a watercement
ratio of 0.5. Cylindrical and beam specimens with 0.5% fibers
volume fraction and without fibers were cast to investigate the
influence of geometry on the mechanical properties of concrete. The
performance parameters mainly studied include flexural strength,
splitting tensile strength, compressive strength and ultrasonic pulse
velocity (UPV). Test results show that geometry of fiber has a
marginal effect on the workability of concrete. However, it plays a
significant role in achieving a good compressive and tensile strength
of concrete. Further, significant improvement in term of flexural and
energy dissipation capacity were observed from other fibers as
compared to the straight slit sheet pattern. Also, the inclusion of PET
fiber improved the ability in absorbing energy in the post-cracking
state of the specimen as well as no significant porous structures.
Abstract: This study investigates the suitability of using plastic,
such as polyethylene terephthalate (PET), as a partial replacement of
natural coarse and fine aggregates (for example, brick chips and
natural sand) to produce lightweight concrete for load bearing
structural members. The plastic coarse aggregate (PCA) and plastic
fine aggregate (PFA) were produced from melted polyethylene
terephthalate (PET) bottles. Tests were conducted using three
different water–cement (w/c) ratios, such as 0.42, 0.48, and 0.57,
where PCA and PFA were used as 50% replacement of coarse and
fine aggregate respectively. Fresh and hardened properties of
concrete have been compared for natural aggregate concrete (NAC),
PCA concrete (PCC) and PFA concrete (PFC). The compressive
strength of concrete at 28 days varied with the water–cement ratio for
both the PCC and PFC. Between PCC and PFC, PFA concrete
showed the highest compressive strength (23.7 MPa) at 0.42 w/c ratio
and also the lowest compressive strength (13.7 MPa) at 0.57 w/c
ratio. Significant reduction in concrete density was mostly observed
for PCC samples, ranging between 1977–1924 kg/m³. With the
increase in water–cement ratio PCC achieved higher workability
compare to both NAC and PFC. It was found that both the PCA and
PFA contained concrete achieved the required compressive strength
to be used for structural purpose as partial replacement of the natural
aggregate; but to obtain the desired lower density as lightweight
concrete the PCA is most suited.
Abstract: A high thermal dissipation performance polyethylene terephthalate heat pipe has been fabricated and tested in this research. Polyethylene terephthalate (PET) is used as the container material instead of copper. Copper mesh and methanol are sealed in the middle of two PET films as the wick structure and working fluid. Although the thermal conductivity of PET (0.15-0.24 W/m·K) is much smaller than copper (401 W/m·K), the experiment results reveal that the PET heat pipe can reach a minimum thermal resistance of 0.146 (oC/W) and maximum effective thermal conductivity of 18,310 (W/m·K) with 36.9 vol% at 26 W input power. However, when the input power is larger than 30 W, the laminated PET will debond due to the high vapor pressure of methanol.
Abstract: In this study tree types of multilayer gas barrier plastic packaging films were compared using life cycle assessment as a tool for resource efficient and environmentally low-impact materials selection. The first type of multilayer packaging film (PET-AlOx/LDPE) consists of polyethylene terephthalate with barrier layer AlOx (PET-AlOx) and low density polyethylene (LDPE). The second type of polymer film (PET/PE-EVOH-PE) is made of polyethylene terephthalate (PET) and co-extrusion film PE-EVOH-PE as barrier layer. And the third one type of multilayer packaging film (PET-PVOH/LDPE) is formed from polyethylene terephthalate with barrier layer PVOH (PET-PVOH) and low density polyethylene (LDPE).
All of analyzed packaging has significant impact to resource depletion, because of raw materials extraction and energy use and production of different kind of plastics. Nevertheless the impact generated during life cycle of functional unit of II type of packaging (PET/PE-EVOH-PE) was about 25% lower than impact generated by I type (PET-AlOx/LDPE) and III type (PET-PVOH/LDPE) of packaging.
Result revealed that the contribution of different gas barrier type to the overall environmental problem of packaging is not significant. The impact are mostly generated by using energy and materials during raw material extraction and production of different plastic materials as plastic polymers material as PE, LDPE and PET, but not gas barrier materials as AlOx, PVOH and EVOH.
The LCA results could be useful in different decision-making processes, for selecting resource efficient and environmentally low-impact materials.
Abstract: In this paper, an automated system is presented for
identification and separation of plastic resins based on near infrared
(NIR) reflectance spectroscopy. For identification and separation
among resins, a "Two-Filter" identification method is proposed that
is capable to distinguish among polyethylene terephthalate (PET),
high density polyethylene (HDPE), polyvinyl chloride (PVC),
polypropylene (PP) and polystyrene (PS). Through surveying effects
of parameters such as surface contamination, sample thickness, label
and cap existence, it was obvious that the "Two-Filter" method has a
high efficiency in identification of resins. It is shown that accurate
identification and separation of five major resins can be obtained
through calculating the relative reflectance at two wavelengths in the
NIR region.
Abstract: Utilization of waste material in asphalt pavement
would be beneficial in order to find an alternative solution to increase
service life of asphalt pavement and reduce environmental pollution
as well. One of these waste materials is Polyethylene Terephthalate
(PET) which is a type of polyester material and is produced in a large
extent. This research program is investigating the effects of adding
waste PET particles into the asphalt mixture with a maximum size of
2.36 mm. Different percentages of PET were added into the mixture
during dry process. Gap-graded mixture (SMA 14) and PG 80-100
asphalt binder have been used for this study. To evaluate PET
reinforced asphalt mixture different laboratory investigations have
been conducted on specimens. Marshall Stability test was carried
out. Besides, stiffness modulus test and indirect tensile fatigue test
were conducted on specimens at optimum asphalt content. It was
observed that in many cases PET reinforced SMA mixture had better
mechanical properties in comparison with control mixture.
Abstract: Bottle water is getting very popular all through the
world; especially in the gulf countries as the main source of drinking
water. However, concerns over leaching of toxic chemicals are
increasing. In this study, a health risk assessment was conducted in
accordance with the guidelines indicated by United States
Environmental Protection Agency (USEPA). It is conducted based on
leaching of Diethyl Phthalate (DEP) from Polyethylene terephthalate
(PET). The toxicity and exposure assessment of diethyl phthalate was
conducted to characterize its risk on human health. Risk management
is also discussed.
Abstract: We succeeded to produce a high performance and flexible graphene/Manganese dioxide (G/MnO2) electrode coated on flexible polyethylene terephthalate (PET) substrate. The graphene film is initially synthesized by drop-casting the graphene oxide (GO) solution on the PET substrate, followed by simultaneous reduction and patterning of the dried film using carbon dioxide (CO2) laser beam with power of 1.8 W. Potentiostatic Anodic Deposition method was used to deposit thin film of MnO2 with different loading mass 10 – 50 and 100 μg.cm-2 on the pre-prepared graphene film. The electrodes were fully characterized in terms of structure, morphology, and electrochemical performance. A maximum specific capacitance of 973 F.g-1 was attributed when depositing 50μg.cm-2 MnO2 on the laser reduced graphene oxide rGO (or G/50MnO2) and over 92% of its initial capacitance was retained after 1000 cycles. The good electrochemical performance and long-term cycling stability make our proposed approach a promising candidate in the supercapacitor applications.
Abstract: Thermo-chemical treatment (TCT) such as pyrolysis
is getting recognized as a valid route for (i) materials and valuable
products and petrochemicals recovery; (ii) waste recycling; and (iii)
elemental characterization. Pyrolysis is also receiving renewed
attention for its operational, economical and environmental
advantages. In this study, samples of polyethylene terephthalate
(PET) and polystyrene (PS) were pyrolysed in a microthermobalance
reactor (using a thermogravimetric-TGA setup). Both
polymers were prepared and conditioned prior to experimentation.
The main objective was to determine the kinetic parameters of the
depolymerization reactions that occur within the thermal degradation
process. Overall kinetic rate constants (ko) and activation energies
(Eo) were determined using the general kinetics theory (GKT)
method previously used by a number of authors. Fitted correlations
were found and validated using the GKT, errors were within ± 5%.
This study represents a fundamental step to pave the way towards the
development of scaling relationship for the investigation of larger
scale reactors relevant to industry.