Abstract: It is an established fact that polymers have several
physical limitations such as low stiffness and low resistance to
impact on loading. Hence, polymers do not usually have requisite
mechanical strength for application in various fields. The
reinforcement by high strength fibers provides the polymer
substantially enhanced mechanical properties and makes them more
suitable for a large number of diverse applications. This research
evaluates the effects of particulate Cow bone and Groundnut shell
additions on the mechanical properties and microstructure of cow
bone and groundnut shell reinforced epoxy composite in order to
assess the possibility of using it as a material for engineering
applications. Cow bone and groundnut shell particles reinforced with
epoxy (CBRPC and GSRPC) was prepared by varying the cow bone
and groundnut shell particles from 0-25 wt% with 5 wt% intervals. A
Hybrid of the Cow bone and Groundnut shell (HGSCB) reinforce
with epoxy was also prepared. The mechanical properties of the
developed composites were investigated. Optical microscopy was
used to examine the microstructure of the composites. The results
revealed that mechanical properties did not increase uniformly with
additions in filler but exhibited maximum properties at specific
percentages of filler additions. From the Microscopic evaluation, it
was discovered that homogeneity decreases with increase in % filler,
this could be due to poor interfacial bonding.
Abstract: A novel method is presented for obtaining the stress
field induced by an edge dislocation in a multilayered composite. To
demonstrate the applications of the obtained solution, we consider the
problem of an interfacial crack in a periodically layered bimaterial
medium. The crack is modelled as a continuous distribution of edge
dislocations and the Distributed Dislocation Technique (DDT) is
utilized to obtain numerical results for the energy release rate (ERR).
The numerical implementation of the dislocation solution in
MATLAB is also provided.
Abstract: In recent years a new method of combination
treatment for cancer has been developed and studied that has led to
significant advancements in the field of cancer therapy. Hyperthermia
is a traditional therapy that, along with a creation of a medically
approved level of heat with the help of an alternating magnetic AC
current, results in the destruction of cancer cells by heat. This paper
gives details regarding the production of the spherical nanocomposite
PVA/γ-Fe2O3 in order to be used for medical purposes such as tumor
treatment by hyperthermia. To reach a suitable and evenly distributed
temperature, the nanocomposite with core-shell morphology and
spherical form within a 100 to 200 nanometer size was created using
phase separation emulsion, in which the magnetic nano-particles γ-
Fe2O3 with an average particle size of 20 nano-meters and with
different percentages of 0.2, 0.4, 0.5 and 0.6 were covered by
polyvinyl alcohol. The main concern in hyperthermia and heat
treatment is achieving desirable specific absorption rate (SAR) and
one of the most critical factors in SAR is particle size. In this project
all attempts has been done to reach minimal size and consequently
maximum SAR. The morphological analysis of the spherical
structure of the nanocomposite PVA/γ-Fe2O3 was achieved by SEM
analyses and the study of the chemical bonds created was made
possible by FTIR analysis. To investigate the manner of magnetic
nanocomposite particle size distribution a DLS experiment was
conducted. Moreover, to determine the magnetic behavior of the γ-
Fe2O3 particle and the nanocomposite PVA/γ-Fe2O3 in different
concentrations a VSM test was conducted. To sum up, creating
magnetic nanocomposites with a spherical morphology that would be
employed for drug loading opens doors to new approaches in
developing nanocomposites that provide efficient heat and a
controlled release of drug simultaneously inside the magnetic field,
which are among their positive characteristics that could significantly
improve the recovery process in patients.
Abstract: We report herein the development and preliminary mechanical characterization of fully-dense multi-wall carbon nanotube (MWCNT)-reinforced ceramics and glasses based on a completely new methodology termed High Shear Compaction (HSC). The tubes are introduced and bound to the matrix grains by aid of polymeric binders to form flexible green bodies which are sintered and densified by spark plasma sintering to unprecedentedly high densities of 100% of the pure-matrix value. The strategy was validated across a PyrexTM glass / MWCNT composite while no identifiable factors limit application to other types of matrices. Nondestructive evaluation, based on ultrasonics, of the dynamic mechanical properties of the materials including elastic, shear and bulk modulus as well as Poisson’s ratio showed optimum property improvement at 0.5 %wt tube loading while evidence of nanoscalespecific energy dissipative characteristics acting complementary to nanotube bridging and pull-out indicate a high potential in a wide range of reinforcing and multifunctional applications.
Abstract: In the present study, response surface methodology has been used to optimize turn-assisted deep cold rolling process of AISI 4140 steel. A regression model is developed to predict surface hardness and surface roughness using response surface methodology and central composite design. In the development of predictive model, deep cold rolling force, ball diameter, initial roughness of the workpiece, and number of tool passes are considered as model variables. The rolling force and the ball diameter are the significant factors on the surface hardness and ball diameter and numbers of tool passes are found to be significant for surface roughness. The predicted surface hardness and surface roughness values and the subsequent verification experiments under the optimal operating conditions confirmed the validity of the predicted model. The absolute average error between the experimental and predicted values at the optimal combination of parameter settings for surface hardness and surface roughness is calculated as 0.16% and 1.58% respectively. Using the optimal processing parameters, the surface hardness is improved from 225 to 306 HV, which resulted in an increase in the near surface hardness by about 36% and the surface roughness is improved from 4.84µm to 0.252 µm, which resulted in decrease in the surface roughness by about 95%. The depth of compression is found to be more than 300µm from the microstructure analysis and this is in correlation with the results obtained from the microhardness measurements. Taylor hobson talysurf tester, micro vickers hardness tester, optical microscopy and X-ray diffractometer are used to characterize the modified surface layer.
Abstract: There is not much effective guideline on development of design parameters selection on spring back for advanced high strength steel sheet metal in U-channel process during cold forming process. This paper presents the development of predictive model for spring back in U-channel process on advanced high strength steel sheet employing Response Surface Methodology (RSM). The experimental was performed on dual phase steel sheet, DP590 in Uchannel forming process while design of experiment (DoE) approach was used to investigates the effects of four factors namely blank holder force (BHF), clearance (C) and punch travel (Tp) and rolling direction (R) were used as input parameters using two level values by applying Full Factorial design (24 ). From a statistical analysis of variant (ANOVA), result showed that blank holder force (BHF), clearance (C) and punch travel (Tp) displayed significant effect on spring back of flange angle (β2 ) and wall opening angle (β1 ), while rolling direction (R) factor is insignificant. The significant parameters are optimized in order to reduce the spring back behavior using Central Composite Design (CCD) in RSM and the optimum parameters were determined. A regression model for spring back was developed. The effect of individual parameters and their response was also evaluated. The results obtained from optimum model are in agreement with the experimental values.
Abstract: Aluminium matrix composites with alumina
reinforcements give superior mechanical & physical properties. Their
applications in several fields like automobile, aerospace, defense,
sports, electronics, bio-medical and other industrial purposes are
becoming essential for the last several decades. In the present work,
fabrication of hybrid composite was done by Stir casting technique
using Al 6061 as a matrix with alumina and silicon carbide (SiC) as
reinforcement materials. The weight percentage of alumina is varied
from 2 to 4% and the silicon carbide weight percentage is maintained
constant at 2%. Hardness and wear tests are performed in the as cast
and heat treated conditions. Age hardening treatment was performed
on the specimen with solutionizing at 550°C, aging at two
temperatures (150 and 200°C) for different time durations. Hardness
distribution curves are drawn and peak hardness values are recorded.
Hardness increase was very sensitive with respect to the decrease in
aging temperature. There was an improvement in wear resistance of
the peak aged material when aged at lower temperature. Also
increase in weight percent of alumina, increases wear resistance at
lower temperature but opposite behavior was seen when aged at
higher temperature.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: This study focuses on a novel method for dispersion
and distribution of reinforcement under high intensive shear stress to
produce metal composites. The polyacrylonitrile (PAN)-based short
carbon fiber (Csf) and Nextel 610 alumina fiber were dispersed under
high intensive shearing at mushy zone in semi-solid of A356 by a
novel method. The bundles and clusters were embedded by
infiltration of slurry into the clusters, thus leading to a uniform
microstructure. The fibers were embedded homogenously into the
aluminum around 576-580°C with around 46% of solid fraction.
Other experiments at 615°C and 568°C which are contained 0% and
90% solid respectively were not successful for dispersion and
infiltration of aluminum into bundles of Csf. The alumina fiber has
been cracked by high shearing load. The morphologies and
crystalline phase were evaluated by SEM and XRD. The adopted
thixo-process effectively improved the adherence and distribution of
Csf into Al that can be developed to produce various composites by
thixomixing.
Abstract: In contrast with literal meaning of nano, researchers
have been achieved mega adventures in this area and every day more
nanomaterials are being introduced to the market. After long time
application of fossil-based plastics, nowadays accumulation of their
waste seems to be a big problem to the environment. On the other
hand, mankind has more attention to safety and living environment.
Replacing common plastic packaging materials with degradable ones
that degrade faster and convert to non-dangerous components like
water and carbon dioxide have more attractions; these new materials
are based on renewable and inexpensive sources of starch and
cellulose. However, the functional properties of them do not suitable
for packaging. At this point, nanotechnology has an important role.
Utilizing of nanomaterials in polymer structure will improve
mechanical and physical properties of them; nanocrystalline cellulose
(NCC) has this ability. This work has employed a chemical method to
produce NCC and starch bio nanocomposite containing NCC. X-Ray
Diffraction technique has characterized the obtained materials.
Results showed that applied method is a suitable one as well as
applicable one to NCC production.
Abstract: This paper presents the results of an experimental
study undertaken to evaluate the local bond stress-slip response of
short embedment of reinforcing bars in normal concrete (NC) and
high performance fiber reinforced cement composites (HPFRCC)
blocks. Long embedment was investigated as well to gain insights on
the distribution of strain, slip, bar stress and bond stress along the bar
especially in post-yield range. A total of 12 specimens were tested,
by means of pull-out of the reinforcing bars from concrete blocks. It
was found that the enhancement of local bond strength can be
reached up to 50% and ductility of the bond behavior was improved
significantly if HPFRCC is used. Also, under a constant strain at
loaded end, HPFRCC has delayed yielding of bars at other location
from the loaded end. Hence, the reduction of bond stress was slower
for HPFRCC in comparison with NC. Due to the same reason, the
total slips at loaded end for HPFRCC was smaller than NC as
expected. Test results indicated that HPFRCC has better bond slip
behavior which makes it a suitable material to be employed in
anchorage zone such as beam-column joints.
Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.
Abstract: Intermetallic materials are among advanced
technology materials that have outstanding mechanical and physical
properties for high temperature applications. Especially creep
resistance, low density and high hardness properties stand out in such
intermetallics. The microstructure, mechanical properties of %88Ni-
%10Cr and %2Mn powders were investigated using specimens
produced by tube furnace sintering at 900-1300°C temperature. A
composite consisting of ternary additions, a metallic phase, Fe, Cr
and Mn have been prepared under Ar shroud and then tube furnace
sintered. XRD, SEM (Scanning Electron Microscope), were
investigated to characterize the properties of the specimens.
Experimental results carried out for composition %88Ni-%10Cr and
%2Mn at 1300°C suggest that the best properties as 138,80HV and
6,269/cm3 density were obtained at 1300°C.
Abstract: Microstructural and electrical properties of
Cu-chromium alloy (Cu-Cr) dispersed with vapor-grown carbon fiber
(VGCF) prepared by powder metallurgy (P/M) process have been
investigated. Cu-0.7 mass% Cr pre-alloyed powder (Cu-Cr) made by
water atomization process was used as raw materials, which contained
solid solute Cr elements in Cu matrix. The alloy powder coated with
un-bundled VGCF by using oil coating process was consolidated at
1223 K in vacuum by spark plasma sintering, and then extruded at
1073 K. The extruded Cu-Cr alloy (monolithic alloy) had 209.3 MPa
YS and 80.4 IACS% conductivity. The extruded Cu-Cr with 0.1
mass% VGCF composites revealed a small decrease of YS compared
to the monolithic Cu-Cr alloy. On the other hand, the composite had a
higher electrical conductivity than that of the monolithic alloy. For
example, Cu-Cr with 0.1 mass% VGCF composite sintered for 5 h
showed 182.7 MPa YS and 89.7 IACS% conductivity. In the case of
Cu-Cr with VGCFs composites, the Cr concentration was observed
around VGCF by SEM-EDS analysis, where Cr23C6 compounds were
detected by TEM observation. The amount of Cr solid solution in the
matrix of the Cu-Cr composites alloy was about 50% compared to the
monolithic Cu-Cr sintered alloy, and resulted in the remarkable
increment of the electrical conductivity.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: Aim of this work is to determine the theoretical and
experimental properties of filament wound glass fiber/epoxy resin
composite pipes with different winding design subjected under
bending. For determination of bending strength of composite samples
three point bending tests were conducted. Good correlation between
theoretical and experimental results has been obtained, where sample
No4 has shown the highest value of bending strength. All samples
have demonstrated matrix cracking and fiber failure followed by
layers delamination during testing. Also, it was found that smaller
winding angles lead to an increase in bending stress. From presented
results good merger between glass fibers and epoxy resin was
confirmed by SEM analysis.
Abstract: Non-crimp 3D orthogonal fabric composite is one of
the textile-based composite materials that are rapidly developing
light-weight engineering materials. The present paper focuses on
geometric and micromechanical modeling of non-crimp 3D
orthogonal carbon fabric and composites reinforced with it for
aerospace applications. In this research meso-finite element (FE)
modeling employs for stress analysis in different load conditions.
Since mechanical testing of expensive textile carbon composites with
specific application isn't affordable, simulation composite in a virtual
environment is a helpful way to investigate its mechanical properties
in different conditions.
Abstract: Al6061 alloy base matrix, reinforced with particles of
silicon carbide (10 wt %) and Graphite powder (1wt%), known as
hybrid composites have been fabricated by liquid metallurgy route
(stir casting technique) and optimized at different parameters like
applied load, sliding speed and sliding distance by taguchi method. A
plan of experiment generated through taguchi technique was used to
perform experiments based on L27 orthogonal array. The developed
ANOVA and regression equations are used to find the optimum
coefficient of friction and wear under the influence of applied load,
sliding speed and sliding distance. On the basis of “smaller the best”
the dry sliding wear resistance was analysed and finally confirmation
tests were carried out to verify the experimental results.
Abstract: The article represents the results of clinical researches
of composite herbal medicinal product based on essential oils of
Sedum plants growing in Kazakhstan in commercial reserves at the
territory of Kazakhstan. The results of comparative analysis are
represented in obstetric-gynecologic practice during combined
therapy for postnatal complications, inflammatory infiltrates in the
area of surgical wounds including wounds after caesarean section.
Abstract: An unconventional composite inorganic ceramic
membrane capable of enhancing carbon dioxide emission decline was
fabricated and tested at laboratory scale in conformism to various
environmental guidelines and also to mitigate the effect of global
warming. A review of the existing membrane technologies for carbon
capture including the relevant gas transport mechanisms is presented.
Single gas permeation experiments using silica modified ceramic
membrane with internal diameter 20mm, outside diameter 25mm and
length of 368mm deposited on a macro porous support was carried
out to investigate individual gas permeation behaviours at different
pressures at room temperature. Membrane fabrication was achieved
using after a dip coating method. Nitrogen, Carbon dioxide, Argon,
Oxygen and Methane pure gases were used to investigate their
individual permeation rates at various pressures. Results show that
the gas flow rate increases with pressure drop. However above a
pressure of 3bar, CO2 permeability ratio to that of the other gases
indicated control of a more selective surface adsorptive transport
mechanism.