Abstract: In this study, Ti-5Al-2.5Fe alloy was prepared by powder metallurgy. The elemental titanium, aluminum, and iron powders were mechanically alloyed for 10 h in a vacuum atmosphere. A stainless steel jar and stainless steel balls were used for mechanical alloying. The alloyed powders were then sintered by vacuum hot pressing at 950 °C for a soaking time of 30 minutes. Pure titanium was also sintered at the same conditions for comparison of mechanical properties and microstructural behavior. The samples were investigated by scanning electron microscopy, XRD analysis, and optical microscopy. Results showed that, after mechanical alloying, a homogeneous distribution of the elements was obtained, and desired a-b structure was determined. Ti-5Al-2.5Fe alloy was successfully produced, and the alloy showed enhanced mechanical properties compared to the commercial pure titanium.
Abstract: The microstructure, mechanical properties and metalgraphic characteristics of Ni plated AlN-Astaloy Cr-M powders were investigated using specimens produced by tube furnace sintering at 1000-1400 °C temperature. A uniform nickel layer on AlN powders was deposited prior to sintering using electroless plating technique. A composite consisting of ternary additions, metallic phase, Ni and ceramic phase AlN within a matrix of Astaloy Cr-M had been prepared under Ar shroud and then tube furnace sintered. The experimental results carried out by using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscope) for composition (10% AlN-Astaloy Cr-M) 10% Ni at 1400 °C suggest that the best properties as 132.45HB and permittivity were obtained at 1400 °C.
Abstract: Intermetallic materials are among advanced
technology materials that have outstanding mechanical and physical
properties for high temperature applications. Especially creep
resistance, low density and high hardness properties stand out in such
intermetallics. The microstructure, mechanical properties of %88Ni-
%10Cr and %2Mn powders were investigated using specimens
produced by tube furnace sintering at 900-1300°C temperature. A
composite consisting of ternary additions, a metallic phase, Fe, Cr
and Mn have been prepared under Ar shroud and then tube furnace
sintered. XRD, SEM (Scanning Electron Microscope), were
investigated to characterize the properties of the specimens.
Experimental results carried out for composition %88Ni-%10Cr and
%2Mn at 1300°C suggest that the best properties as 138,80HV and
6,269/cm3 density were obtained at 1300°C.
Abstract: Aluminum Matrix Composites reinforced with
nanocrystalline Ni3Al carbon-coated intermetallic particles, were
synthesized by powder metallurgy. Powder mixture of aluminum
with 0.5-volume fraction of reinforcement particles was compacted
by spark plasma sintering (SPS) technique and the compared with
conventional sintering process. The better results for SPS technique
were obtained in 520ºC-5kN-3min.The hardness (70.5±8 HV) and the
elastic modulus (95 GPa) were evaluated in function of sintering
conditions for SPS technique; it was found that the incorporation of
these kind of reinforcement particles in aluminum matrix improve its
mechanical properties. The densities were about 94% and 97% of the
theoretical density. The carbon coating avoided the interfacial
reaction between matrix-particle at high temperature (520°C) without
show composition change either intermetallic dissolution.
Abstract: Commercial hydroxyapatite (HA) was reinforced by
adding 2, 5, and 10 wt % of 28.5%CaO-28.5%P2O5-38%Na2 O-
5%CaF2 based glass and then sintered. Although HA shows good
biocompatibility with the human body, its applications are limited to
non load-bearing areas and coatings due to its poor mechanical
properties. These mechanical properties can be improved
substantially with addition of glass ceramics by sintering. In this
study, the effects of sintering hydroxyapatite with above specified
phosphate glass additions are quantified. Each composition was
sintered over a range of temperatures. Scanning electron microscopy
and x-ray diffraction were used to characterize the microstructure and
phases of the composites. The density, microhardness, and
compressive strength were measured using Archimedes Principle,
Vickers Microhardness Tester (at 0.98 N), and Instron Universal
Testing Machine (cross speed of 0.5 mm/min) respectively. These
results were used to indicate which composition provided suitable
material for use in hard tissue replacement. Composites containing 10
wt % glass additions formed dense HA/TCP (tricalcium phosphate)
composite materials possessing good compressive strength and
hardness than HA. In-vitro bioactivity was assessed by evaluating
changes in pH and Ca2+ ion concentration of SBF-simulated body
fluid on immersion of these composites in it for two weeks.