Abstract: The current study aims to investigate the effect of fillers with different geometries and sizes on the interfacial shear properties of PA6 composites with de-sized carbon fiber. The fillers which have been investigated are namely; nano-layer silicates (nanoclay), sub-micro aluminum titanium (ALTi) particles, and multiwall carbon nanotube (MWCNT). By means of X-ray photoelectron spectroscopy (XPS), epoxide group which defined as a sizing agent, has been removed. Sizing removal can reduce the acid parameter of carbon fibers surface promoting bonding strength at the fiber/matrix interface which is a desirable property for the carbon fiber composites. Microdroplet test showed that the interfacial shear strength (IFSS) has been enhanced with the addition of 10wt% ALTi by about 23% comparing with neat PA6. However, with including other types of fillers into PA6, the results did not show enhancement of IFSS.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.
Abstract: Composite material based on Fe3Si micro-particles
and Mn-Zn nano-ferrite was prepared using powder metallurgy
technology. The sol-gel followed by autocombustion process was
used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically
milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano
powder system was homogenized by the Resonant Acoustic Mixing
using ResodynLabRAM Mixer. This non-invasive homogenization
technique was used to preserve spherical morphology of Fe3Si
powder particles. Uniaxial cold pressing in the closed die at pressure
600 MPa was applied to obtain a compact sample. Microwave
sintering of green compact was realized at 800°C, 20 minutes, in air.
Density of the powders and composite was measured by
Hepycnometry. Impulse excitation method was used to measure
elastic properties of sintered composite. Mechanical properties were
evaluated by measurement of transverse rupture strength (TRS) and
Vickers hardness (HV). Resistivity was measured by 4 point probe
method. Ferrite phase distribution in volume of the composite was
documented by metallographic analysis.
It has been found that nano-ferrite particle distributed among
micro- particles of Fe3Si powder alloy led to high relative density
(~93%) and suitable mechanical properties (TRS >100 MPa, HV
~1GPa, E-modulus ~140 GPa) of the composite. High electric
resistivity (R~6.7 ohm.cm) of prepared composite indicate their
potential application as soft magnetic material at medium and high
frequencies.