Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.