Abstract: Cemented carbides, owing to their excellent
mechanical properties, have been of immense interest in the field of
hard materials for the past few decades. A number of processing
techniques have been developed to obtain high quality carbide tools,
with a wide range of grain size depending on the application and
requirements. Microwave sintering is one of the heating processes,
which has been used to prepare a wide range of materials including
ceramics. A deep understanding of microwave sintering and its
contribution towards control of grain growth and on deformation of
the resulting carbide materials requires further studies and attention.
In addition, the effect of binder materials and their behavior during
microwave sintering is another area that requires clear understanding.
This review aims to focus on microwave sintering, providing
information of how the process works and what type of materials it is
best suited for. In addition, a closer look at some microwave sintered
Tungsten Carbide-Cobalt samples will be taken and discussed,
highlighting some of the key issues and challenges faced in this
research area.
Abstract: Composite material based on Fe3Si micro-particles
and Mn-Zn nano-ferrite was prepared using powder metallurgy
technology. The sol-gel followed by autocombustion process was
used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically
milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano
powder system was homogenized by the Resonant Acoustic Mixing
using ResodynLabRAM Mixer. This non-invasive homogenization
technique was used to preserve spherical morphology of Fe3Si
powder particles. Uniaxial cold pressing in the closed die at pressure
600 MPa was applied to obtain a compact sample. Microwave
sintering of green compact was realized at 800°C, 20 minutes, in air.
Density of the powders and composite was measured by
Hepycnometry. Impulse excitation method was used to measure
elastic properties of sintered composite. Mechanical properties were
evaluated by measurement of transverse rupture strength (TRS) and
Vickers hardness (HV). Resistivity was measured by 4 point probe
method. Ferrite phase distribution in volume of the composite was
documented by metallographic analysis.
It has been found that nano-ferrite particle distributed among
micro- particles of Fe3Si powder alloy led to high relative density
(~93%) and suitable mechanical properties (TRS >100 MPa, HV
~1GPa, E-modulus ~140 GPa) of the composite. High electric
resistivity (R~6.7 ohm.cm) of prepared composite indicate their
potential application as soft magnetic material at medium and high
frequencies.