Abstract: Cemented carbides, owing to their excellent
mechanical properties, have been of immense interest in the field of
hard materials for the past few decades. A number of processing
techniques have been developed to obtain high quality carbide tools,
with a wide range of grain size depending on the application and
requirements. Microwave sintering is one of the heating processes,
which has been used to prepare a wide range of materials including
ceramics. A deep understanding of microwave sintering and its
contribution towards control of grain growth and on deformation of
the resulting carbide materials requires further studies and attention.
In addition, the effect of binder materials and their behavior during
microwave sintering is another area that requires clear understanding.
This review aims to focus on microwave sintering, providing
information of how the process works and what type of materials it is
best suited for. In addition, a closer look at some microwave sintered
Tungsten Carbide-Cobalt samples will be taken and discussed,
highlighting some of the key issues and challenges faced in this
research area.
Abstract: The group of progressive cutting materials can include non-traditional, emerging and less-used materials that can be an efficient use of cutting their lead to a quantum leap in the field of machining. This is essentially a “superhard” materials (STM) based on polycrystalline diamond (PCD) and polycrystalline cubic boron nitride (PCBN) cutting performance ceramics and development is constantly "perfecting" fine coated cemented carbides. The latter cutting materials are broken down by two parameters, toughness and hardness. A variation of alloying elements is always possible to improve only one of each parameter. Reducing the size of the core on the other hand doing achieves "contradictory" properties, namely to increase both hardness and toughness.
Abstract: In this study, WC-Ni-based cemented carbides having different nickel contents were used as the substrate for cutting tool materials. Hardened steel was turned by a (Ti,W,Si)N-coated WC-Ni-based cemented carbide tool, and the tool wear was experimentally investigated. The following results were obtained: (1) In the (Ti,W,Si)N-coated WC-Ni-based cemented carbide, the hardness of the coating film was not much different from the content of the binding material, Ni, and the adhesion strength increased with a decrease in Ni content. (2) There is little difference between the wear progress of the (Ti,W,Si)N-coated WC-7%Ni-based cemented carbide tool and that of the (Ti,W,Si)N-coated WC-6%Co-based cemented carbide tool. (3) The wear progress of the (Ti,W,Si)N-coated WC-Ni-based cemented carbide became slower with a decrease in Ni content.
From the above, it is has become clear that WC-Ni-based cemented carbide can be used as a substrate for cutting tool materials.