Abstract: A dip-coating process has been used to form an
asymmetric silica membrane with improved membrane performance
and reproducibility. First, we deposited repeatedly silica on top of a
commercial alumina membrane support to improve its structural
make up. The membrane is further processed under clean room
conditions to avoid dust impurity and subsequent drying in an oven
for high thermal, chemical and physical stability. The resulting
asymmetric membrane exhibits a gradual change in the membrane
layer thickness. Compared to the support, the dual-layer process
improves the gas flow rates. For the scientific applications for natural
gas purification, CO2, CH4 and H2 gas flow rates were. In addition,
the membrane selectively separated hydrogen.
Abstract: Atmospheric carbon dioxide emissions are considered
as the greatest environmental challenge the world is facing today.
The tasks to control the emissions include the recovery of CO2 from
flue gas. This concern has been improved due to recent advances in
materials process engineering resulting in the development of
inorganic gas separation membranes with excellent thermal and
mechanical stability required for most gas separations. This paper,
therefore, evaluates the performance of a highly selective inorganic
membrane for CO2 recovery applications. Analysis of results
obtained is in agreement with experimental literature data. Further
results show the prediction performance of the membranes for gas
separation and the future direction of research. The materials
selection and the membrane preparation techniques are discussed.
Method of improving the interface defects in the membrane and its
effect on the separation performance has also been reviewed and in
addition advances to totally exploit the potential usage of this
innovative membrane.
Abstract: An unconventional composite inorganic ceramic
membrane capable of enhancing carbon dioxide emission decline was
fabricated and tested at laboratory scale in conformism to various
environmental guidelines and also to mitigate the effect of global
warming. A review of the existing membrane technologies for carbon
capture including the relevant gas transport mechanisms is presented.
Single gas permeation experiments using silica modified ceramic
membrane with internal diameter 20mm, outside diameter 25mm and
length of 368mm deposited on a macro porous support was carried
out to investigate individual gas permeation behaviours at different
pressures at room temperature. Membrane fabrication was achieved
using after a dip coating method. Nitrogen, Carbon dioxide, Argon,
Oxygen and Methane pure gases were used to investigate their
individual permeation rates at various pressures. Results show that
the gas flow rate increases with pressure drop. However above a
pressure of 3bar, CO2 permeability ratio to that of the other gases
indicated control of a more selective surface adsorptive transport
mechanism.