Abstract: Aluminium matrix composites with alumina
reinforcements give superior mechanical & physical properties. Their
applications in several fields like automobile, aerospace, defense,
sports, electronics, bio-medical and other industrial purposes are
becoming essential for the last several decades. In the present work,
fabrication of hybrid composite was done by Stir casting technique
using Al 6061 as a matrix with alumina and silicon carbide (SiC) as
reinforcement materials. The weight percentage of alumina is varied
from 2 to 4% and the silicon carbide weight percentage is maintained
constant at 2%. Hardness and wear tests are performed in the as cast
and heat treated conditions. Age hardening treatment was performed
on the specimen with solutionizing at 550°C, aging at two
temperatures (150 and 200°C) for different time durations. Hardness
distribution curves are drawn and peak hardness values are recorded.
Hardness increase was very sensitive with respect to the decrease in
aging temperature. There was an improvement in wear resistance of
the peak aged material when aged at lower temperature. Also
increase in weight percent of alumina, increases wear resistance at
lower temperature but opposite behavior was seen when aged at
higher temperature.