Abstract: The tribological behavior of commercially used Perspex was evaluated under dry and wet sliding condition using a pin-on-disc wear tester with different applied loads ranging from 2.5 to 20 N. Experiments were conducted with varying sliding distance from 0.2 km to 4.6 km, wherein the sliding velocity was kept constant, 0.64 ms-1. The results reveal that the weight loss increases with applied load and the sliding distance. The nature of the wear rate was very similar in both the sliding environments in which initially the wear rate increased very rapidly with increasing sliding distance and then progressed to a slower rate. Moreover, the wear rate in wet sliding environment was significantly lower than that under dry sliding condition. The worn surfaces were characterized by optical microscope and SEM. It is found that surface modification has significant effect on sliding wear performance of Perspex.
Abstract: Nitrogen implantation in aluminum and its alloys is acquainted for the difficulties in obtaining modified layers deeper than 200 nm. The present work addresses a new method to overcome such a problem; although, the coating with nitrogen and oxygen obtained by plasma immersion ion implantation (PIII) into a 7075 aluminum alloy surface was too shallow. This alloy is commonly used for structural parts in aerospace applications. Such a layer was characterized by secondary ion mass spectroscopy, electron microscopy, and nanoindentation experiments reciprocating wear tests. From the results, one can assume that the wear of this aluminum alloy starts presenting severe abrasive wear followed by an additional adhesive mechanism. PIII produced a slight difference, as shown in all characterizations carried out in this work. The results shown here can be used as the scientific basis for further nitrogen PIII experiments in aluminum alloys which have the goal to produce thicker modified layers or to improve their surface properties.
Abstract: Tungsten carbide is widely used as a tool material in metal manufacturing process. Since tungsten is typical rare metal, establishment of recycle process of tungsten carbide tools and restore into cemented carbide material bring great impact to metal manufacturing industry. Recently, recycle process of tungsten carbide has been developed and established gradually. However, the demands for quality of cemented carbide tool are quite severe because hardness, toughness, anti-wear ability, heat resistance, fatigue strength and so on should be guaranteed for precision machining and tool life. Currently, it is hard to restore the recycled tungsten carbide powder entirely as raw material for new processed cemented carbide tool. In this study, to suggest positive use of recycled tungsten carbide powder, we have tried to fabricate a carbon based sintered steel which shows reinforced mechanical properties with recycled tungsten carbide powder. We have made set of newly designed sintered steels. Compression test of sintered specimen in density ratio of 0.85 (which means 15% porosity inside) has been conducted. As results, at least 1.7 times higher in nominal strength in the amount of 7.0 wt.% was shown in recycled WC powder. The strength reached to over 600 MPa for the Fe-WC-Co-Cu sintered alloy. Wear test has been conducted by using ball-on-disk type friction tester using 5 mm diameter ball with normal force of 2 N in the dry conditions. Wear amount after 1,000 m running distance shows that about 1.5 times longer life was shown in designed sintered alloy. Since results of tensile test showed that same tendency in previous testing, it is concluded that designed sintered alloy can be used for several mechanical parts with special strength and anti-wear ability in relatively low cost due to recycled tungsten carbide powder.
Abstract: In this study, the effects of B4C and SiC particle reinforcements on wear properties of magnesium matrix metal composites produced by pressure infiltration method were investigated. AZ91 (9%Al-1%Zn) magnesium alloy was used as a matrix. AZ91 magnesium alloy was melted under an argon atmosphere. The melt was infiltrated to the particles with an appropriate pressure. Wear tests, hardness tests were performed respectively. Microstructure characterizations were examined by light optical (LOM) and scanning electron microscope (SEM). The results showed that uniform particle distributions were achieved in both B4C and SiC reinforced composites. Wear behaviors of magnesium matrix metal composites changed as a function of type of particles. SiC reinforced composite has better wear performance and higher hardness than B4C reinforced composite.
Abstract: Understanding the nature of wheel and rail wear in the railway field is of fundamental importance to the safe and cost effective operation of the railways. Twin disc wear testing is used extensively for studying wear of wheel and rail materials. The University of Huddersfield twin disc rig was used in this paper to examine the effect of surface conditions on wheel and rail wear measurement under a range of wheel/rail contact conditions, with and without contaminants. This work focuses on an investigation of the effect of dry, wet, and lubricated conditions and the effect of contaminants such as sand on wheel and rail wear. The wheel and rail wear measurements were carried out by using a replica material and an optical profilometer that allows measurement of wear in difficult location with high accuracy. The results have demonstrated the rate at which both water and oil reduce wheel and rail wear. Scratches and other damage were seen on the wheel and rail surfaces after the addition of sand and consequently both wheel and rail wear damage rates increased under these conditions. This work introduced the replica material and an optical instrument as effective tools to study the effect of surface conditions on wheel and rail wear.
Abstract: Artificial joint replacements such as total knee and total hip prosthesis have been applied to the patients who affected by osteoarthritis. Although different material combinations are used for these joints, biopolymers are most commonly preferred materials especially for acetabular cup and tibial component of hip and knee joints respectively. The main limitation that shortens the service life of these prostheses is wear. Wear is complicated phenomena and it must be considered with friction and lubrication. In this study, micro wave (MW) induced argon+oxygen plasma surface modification were applied on ultra-high molecular weight polyethylene (UHMWPE) and vitamin E blended UHMWPE (VE-UHMWPE) biopolymer surfaces to improve surface wettability and wear resistance of the surfaces. Contact angel measurement method was used for determination of wettability. Ball-on-disc wear test was applied under 25% bovine serum lubrication conditions. The results show that surface wettability and wear resistance of both material samples were increased by plasma surface modification.
Abstract: This study aimed for improving wear resistance of AM60 magnesium alloy by Ti addition (0, 0.2, 0.5, 1wt%Ti). An electric resistance furnace was used to produce alloys. Pure Mg together with Al, Al-Ti and Al-Mn were melted at 750 0C in a stainless steel crucible under controlled Ar gas atmosphere and then poured into a metal mould preheated at 250 0C. Microstructure characterizations were performed by light optical (LOM) and scanning electron microscope (SEM) after the wear test. Wear rates and friction coefficients were measured with a pin-on-disk type UTS-10 Tribometer test device under a load of 20N. The results showed that Ti addition altered the morphology and the amount of b-Mg17Al12 phase in the microstructure of AM60 alloy. b-Mg17Al12 phases on the grain boundaries were refined with increasing amount of Ti. An improvement in wear resistance of AM60 alloy was observed due to the alteration in the microstructure by Ti addition.
Abstract: The sintering step in powder metallurgy (P/M) processes is very sensitive as it determines to a large extent the properties of the final component produced. Spark plasma sintering over the past decade has been extensively used in consolidating a wide range of materials including metallic alloy powders. This novel, non-conventional sintering method has proven to be advantageous offering full densification of materials, high heating rates, low sintering temperatures, and short sintering cycles over conventional sintering methods. Ti6Al4V has been adjudged the most widely used α+β alloy due to its impressive mechanical performance in service environments, especially in the aerospace and automobile industries being a light metal alloy with the capacity for fuel efficiency needed in these industries. The P/M route has been a promising method for the fabrication of parts made from Ti6Al4V alloy due to its cost and material loss reductions and the ability to produce near net and intricate shapes. However, the use of this alloy has been largely limited owing to its relatively poor hardness and wear properties. The effect of sintering temperature on the densification, hardness, and wear behaviors of spark plasma sintered Ti6Al4V powders was investigated in this present study. Sintering of the alloy powders was performed in the 650–850°C temperature range at a constant heating rate, applied pressure and holding time of 100°C/min, 50 MPa and 5 min, respectively. Density measurements were carried out according to Archimedes’ principle and microhardness tests were performed on sectioned as-polished surfaces at a load of 100gf and dwell time of 15 s. Dry sliding wear tests were performed at varied sliding loads of 5, 15, 25 and 35 N using the ball-on-disc tribometer configuration with WC as the counterface material. Microstructural characterization of the sintered samples and wear tracks were carried out using SEM and EDX techniques. The density and hardness characteristics of sintered samples increased with increasing sintering temperature. Near full densification (99.6% of the theoretical density) and Vickers’ micro-indentation hardness of 360 HV were attained at 850°C. The coefficient of friction (COF) and wear depth improved significantly with increased sintering temperature under all the loading conditions examined, except at 25 N indicating better mechanical properties at high sintering temperatures. Worn surface analyses showed the wear mechanism was a synergy of adhesive and abrasive wears, although the former was prevalent.
Abstract: Partially lubricated sliding wear behaviour of a zinc-based alloy reinforced with 10wt% SiC particles has been studied as a function of applied load and solid lubricant particle size and has been compared with that of matrix alloy and conventionally used grey cast iron. The wear tests were conducted at the sliding velocities of 2.1m/sec in various partial lubricated conditions using pin on disc machine as per ASTM G-99-05. Base oil (SAE 20W-40) or mixture of the base oil with 5wt% graphite of particle sizes (7-10 µm) and (100 µm) were used for creating lubricated conditions. The matrix alloy revealed primary dendrites of a and eutectoid a + h and Î phases in the Inter dendritic regions. Similar microstructure has been depicted by the composite with an additional presence of the dispersoid SiC particles. In the case of cast iron, flakes of graphite were observed in the matrix; the latter comprised of (majority of) pearlite and (limited quantity of) ferrite. Results show a large improvement in wear resistance of the zinc-based alloy after reinforcement with SiC particles. The cast iron shows intermediate response between the matrix alloy and composite. The solid lubrication improved the wear resistance and friction behaviour of both the reinforced and base alloy. Moreover, minimum wear rate is obtained in oil+ 5wt % graphite (7-10 µm) lubricated environment for the matrix alloy and composite while for cast iron addition of solid lubricant increases the wear rate and minimum wear rate is obtained in case of oil lubricated environment. The cast iron experienced higher frictional heating than the matrix alloy and composite in all the cases especially at higher load condition. As far as friction coefficient is concerned, a mixed trend of behaviour was noted. The wear rate and frictional heating increased with load while friction coefficient was affected in an opposite manner. Test duration influenced the frictional heating and friction coefficient of the samples in a mixed manner.
Abstract: Tribological properties that include nanoparticles are an alternative to improve the tribological behaviour of lubricating oil, which has been investigated by many researchers for the past few decades. Various nanostructures can be used as additives for tribological improvement. However, this also depends on the characteristics of the nanoparticles. In this study, tribological investigation was performed to examine the effect of CuO nanoparticles on the tribological behaviour of Syntium 800 SL 10W−30. Three parameters used in the analysis using the wear tester (piston ring) were load, revolutions per minute (rpm), and concentration. The specifications of the nanoparticles, such as size, concentration, hardness, and shape, can affect the tribological behaviour of the lubricant. The friction and wear experiment was conducted using a tribo-tester and the Response Surface Methodology method was used to analyse any improvement of the performance. Therefore, two concentrations of 40 nm nanoparticles were used to conduct the experiments, namely, 0.005 wt % and 0.01 wt % and compared with base oil 0 wt % (control). A water bath sonicator was used to disperse the nanoparticles in base oil, while a tribo-tester was used to measure the coefficient of friction and wear rate. In addition, the thermal properties of the nanolubricant were also measured. The results have shown that the thermal conductivity of the nanolubricant was increased when compared with the base oil. Therefore, the results indicated that CuO nanoparticles had improved the tribological behaviour as well as the thermal properties of the nanolubricant oil.
Abstract: The objective of this study was to synthesize and
characterize the poly(alkenoic acid)s with different molecular
structures, use these polymers to formulate a dental cement
restorative, and study the effect of molecular structures on reaction
kinetics, viscosity, and mechanical strengths of the formed polymers
and cement restoratives. In this study, poly(alkenoic acid)s with
different molecular structures were synthesized. The purified
polymers were formulated with commercial Fuji II LC glass fillers to
form the experimental cement restoratives. The reaction kinetics was
studied via 1HNMR spectroscopy. The formed restoratives were
evaluated using compressive strength, diametral tensile strength,
flexural strength, hardness and wear-resistance tests. Specimens were
conditioned in distilled water at 37oC for 24 h prior to testing. Fuji II
LC restorative was used as control. The results show that the higher
the arm number and initiator concentration, the faster the reaction
was. It was also found that the higher the arm number and branching
that the polymer had, the lower the viscosity of the polymer in water
and the lower the mechanical strengths of the formed restorative. The
experimental restoratives were 31-53% in compressive strength, 37-
55% in compressive modulus, 80-126% in diametral tensile strength,
76-94% in flexural strength, 4-21% in fracture toughness and 53-96%
in hardness higher than Fuji II LC. For wear test, the experimental
restoratives were only 5.4-13% of abrasive and 6.4-12% of attritional
wear depths of Fuji II LC in each wear cycle. The aging study also
showed that all the experimental restoratives increased their strength
continuously during 30 days, unlike Fuji II LC. It is concluded that
polymer molecular structures have significant and positive impact on
mechanical properties of dental cement restoratives.
Abstract: Erosion and abrasion are wear mechanisms reducing
the lifetime of machine elements like valves, pump and pipe systems.
Both wear mechanisms are acting at the same time, causing a
“Synergy” effect, which leads to a rapid damage of the surface.
Different parameters are effective on erosive abrasive wear rate. In
this study effect of particle impact angle on wear rate and wear
mechanism of ductile and brittle materials was investigated. A new
slurry pot was designed for experimental investigation. As abrasive
particle, silica sand was used. Particle size was ranking between 200-
500 μm. All tests were carried out in a sand-water mixture of 20%
concentration for four hours. Impact velocities of the particles were
4.76 m/s. As ductile material steel St 37 with Vickers Hardness
Number (VHN) of 245 and quenched St 37 with 510 VHN was used
as brittle material. After wear tests, morphology of the eroded
surfaces were investigated for better understanding of the wear
mechanisms acting at different impact angles by using Scanning
Electron Microscope. The results indicated that wear rate of ductile
material was higher than brittle material. Maximum wear rate was
observed by ductile material at a particle impact angle of 300 and
decreased further by an increase in attack angle. Maximum wear rate
by brittle materials was by impact angle of 450 and decreased further
up to 900. Ploughing was the dominant wear mechanism by ductile
material. Microcracks on the surface were detected by ductile
materials, which are nucleation centers for crater formation. Number
of craters decreased and depth of craters increased by ductile
materials by attack angle higher than 300. Deformation wear
mechanism was observed by brittle materials. Number and depth of
pits decreased by brittle materials by impact angles higher than 450.
At the end it is concluded that wear rate could not be directly related
to impact angle of particles due to the different reaction of ductile and
brittle materials.
Abstract: The present work is aimed at examining carbon steel
oil pipelines corrosion using three natural extracts (Eruca Sativa,
Rosell and Mango peels) that are used as inhibitors of different
concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds
are used as corrosion mediums. Weight loss method was used for
measuring the corrosion rate of the carbon steel specimens immersed
in technical white oil at 100ºC at various time intervals in absence
and presence of the two sulphur compounds. The corroded specimens
are examined using the chemical wear test, scratch test and hardness
test. The scratch test is carried out using scratch loads from 0.5 Kg to
2.0 Kg. The scratch width is obtained at various scratch load and test
conditions. The Brinell hardness test is carried out and investigated
for both corroded and inhibited specimens. The results showed that
three natural extracts can be used as environmentally friendly
corrosion inhibitors.
Abstract: Aluminium matrix composites with alumina
reinforcements give superior mechanical & physical properties. Their
applications in several fields like automobile, aerospace, defense,
sports, electronics, bio-medical and other industrial purposes are
becoming essential for the last several decades. In the present work,
fabrication of hybrid composite was done by Stir casting technique
using Al 6061 as a matrix with alumina and silicon carbide (SiC) as
reinforcement materials. The weight percentage of alumina is varied
from 2 to 4% and the silicon carbide weight percentage is maintained
constant at 2%. Hardness and wear tests are performed in the as cast
and heat treated conditions. Age hardening treatment was performed
on the specimen with solutionizing at 550°C, aging at two
temperatures (150 and 200°C) for different time durations. Hardness
distribution curves are drawn and peak hardness values are recorded.
Hardness increase was very sensitive with respect to the decrease in
aging temperature. There was an improvement in wear resistance of
the peak aged material when aged at lower temperature. Also
increase in weight percent of alumina, increases wear resistance at
lower temperature but opposite behavior was seen when aged at
higher temperature.
Abstract: Simultaneous measurements of the curves for wear versus distance, wear rate versus distance, and coefficient of friction versus distance were performed in situ to distinguish the transition from severe running-in wear to mild wear. The effects of the initial surface roughness on the severe running-in wear volume were investigated. Disk-on-plate friction and wear tests were carried out with SUS304 austenitic stainless steel in contact with itself under repeated dry sliding conditions at room temperature. The wear volume was dependent on the initial surface roughness. The wear volume when the initial surfaces on the plate and disk had dissimilar roughness was lower than that when these surfaces had similar roughness. For the dissimilar roughness, the wear volume decreased with decreasing initial surface roughness and reached a minimum; it stayed nearly constant as the roughness was less than the mean size of the oxide particles.
Abstract: Composite pins of rubber dust collected from tyre
retreading centres of trucks, cars and buses etc.and epoxy with
weight percentages of 10. 15, and 20 % of rubber (weight fractions of
9, 13 and 17 % respectively) have been prepared in house with the
help of a split wooden mould. The pins were tested in a pin-on-disc
wear monitor to determine the co-efficient of friction and weight
losses with varying speeds, loads and time. The wear volume and
wear rates have also been found out for all these three specimens.. It
is observed that all the specimens have exhibited very low coefficient
of friction and low wear rates under dry sliding condition. Out of the
above three samples tested, the specimen with 10 % rubber dust by
weight has shown lowest wear rates. However a peculiar result i.e
decreasing trend has been obtained with 20% reinforcement of rubber
in epoxy while rubbed against steel at varying speeds. This might
have occurred due to high surface finish of the disc and formation of
a thin transfer layer from the composite
Abstract: The relationship between different types of Molybdenum disulfide greases under extreme pressure loading and different speed situations have been studied using Design of Experiment (DOE) under 1200rpm steady state rotational speed and cyclic frequencies between 2400 and 1200rpm using a Plint machine software to set up the different rotational speed situations.
Research described here is aimed at providing good friction and wear performance while optimizing cyclic frequencies and MoS2 concentration due to the recent concern about grease behavior in extreme pressure applications. Extreme load of 785 Newton was used in conjunction with different cyclic frequencies (2400rpm -3.75min, 1200rpm -7.5min, 2400rpm -3.75min, 1200rpm -7.5min), to examine lithium based grease with and without MoS2 for equal number of revolutions, and a total run of 36000 revolutions; then compared to 1200rpm steady speed for the same total number of revolutions. 4 Ball wear tester was utilized to run large number of experiments randomly selected by the DOE software. The grease was combined with fine grade MoS2 or technical grade then heated to 750C and the wear scar width was collected at the end of each test. DOE model validation results verify that the data were very significant and can be applied to a wide range of extreme pressure applications. Based on simulation results and Scanning Electron images (SEM), it has been found that wear was largely dependent on the cyclic frequency condition. It is believed that technical grade MoS2 greases under faster cyclic speeds perform better and provides antiwear film that can resist extreme pressure loadings. Figures showed reduced wear scars width and improved frictional values.
Abstract: This work presents the results of a study carried out to
determine the sliding wear behavior and its effect on the process
parameters of components manufactured by direct metal laser
sintering (DMLS). A standard procedure and specimen had been used
in the present study to find the wear behavior. Using Taguchi-s
experimental technique, an orthogonal array of modified L8 had been
developed. Sliding wear testing using pin-on-disk machine was
carried out and analysis of variance (ANOVA) technique was used to
investigate the effect of process parameters and to identify the main
process parameter that influences the properties of wear behavior on
the DMLS components. It has been found that part orientation, one
of the selected process parameter had more influence on wear as
compared to other selected process parameters.
Abstract: Tribological behavior and wear regimes of ascast
and heattreted Al-Cu-Mg matrix composites containing SiC
particles were studied using a pin-on-disc wear testing apparatus
against an EN32 steel counterface giving emphasis on wear rate as
a function of applied pressures (0.2, 0.6, 1.0 and 1.4 MPa) at
different sliding distances (1000, 2000, 3000, 4000 and 5000
meters) and at a fixed sliding speed of 3.35m/s. The results showed
that the composite exhibited lower wear rate than that of the matrix
alloy and the wear rate of the composites is noted to be invariant to
the sliding distance and is reducing by heat treatment. Wear
regimes such as low, mild and severe wear were observed as per the
Archard-s wear calculations. It is very interesting to note that the
mild wear is almost constant in all the wear regimes.