Abstract: Cathodic plasma electrolysis (CPE) is used to create surface textures on cast iron samples for improving the tribological properties. Micro craters with confined size distribution were successfully formed by CPE process. These craters can generate extra hydrodynamic pressure that separates two sliding surfaces, increase the oil film thickness and accelerate the transition from boundary to mixed lubrication. It was found that the optimal crater size was 1.7 μm, at which the maximum lubrication efficiency was achieved. The Taguchi method was used to optimize the process parameters (voltage and roughness) for CPE surface texturing. The orthogonal array and the signal-to-noise ratio were employed to study the effect of each process parameter on the coefficient of friction. The results showed that with higher voltage and lower roughness, the lower friction coefficient can be obtained, and thus the lubrication can be more efficiently used for friction reduction.
Abstract: This work aims to investigate the properties and microstructure of diamond-like carbon film deposited by pulsed laser deposition by ablation of a graphite target in a vacuum chamber on a steel substrate. The equipment was mounted to provide one laser beam. The target of high purity graphite and the steel substrate were polished. The mechanical and tribological properties of the film were characterized using Raman spectroscopy, nanoindentation test, scratch test, roughness profile, tribometer, optical microscopy and SEM images. It was concluded that the pulsed laser deposition (PLD) technique associated with the low-pressure chamber and a graphite target provides a good fraction of sp3 bonding, that the process variable as surface polishing and laser parameter have great influence in tribological properties and in adherence tests performance. The optical microscopy images are efficient to identify the metallurgical bond.
Abstract: Nitrogen implantation in aluminum and its alloys is acquainted for the difficulties in obtaining modified layers deeper than 200 nm. The present work addresses a new method to overcome such a problem; although, the coating with nitrogen and oxygen obtained by plasma immersion ion implantation (PIII) into a 7075 aluminum alloy surface was too shallow. This alloy is commonly used for structural parts in aerospace applications. Such a layer was characterized by secondary ion mass spectroscopy, electron microscopy, and nanoindentation experiments reciprocating wear tests. From the results, one can assume that the wear of this aluminum alloy starts presenting severe abrasive wear followed by an additional adhesive mechanism. PIII produced a slight difference, as shown in all characterizations carried out in this work. The results shown here can be used as the scientific basis for further nitrogen PIII experiments in aluminum alloys which have the goal to produce thicker modified layers or to improve their surface properties.
Abstract: The present work aims at contributing to the study of the complex phenomenon of wear of pin on disc contact in dry sliding friction between two material couples (bronze/steel and unsaturated polyester virgin and charged with graphite powder/steel). The work consists of the determination of the coefficient of friction, the study of the influence of the tribological parameters on this coefficient and the determination of the mass loss and the wear rate of the pin. This study is also widened to the highlighting of the influence of the addition of graphite powder on the tribological properties of the polymer constituting the pin. The experiments are carried out on a pin-disc type tribometer that we have designed and manufactured. Tests are conducted according to the standards DIN 50321 and DIN EN 50324. The discs are made of annealed XC48 steel and quenched and tempered XC48 steel. The main results are described here after. The increase of the normal load and the sliding speed causes the increase of the friction coefficient, whereas the increase of the percentage of graphite and the hardness of the disc surface contributes to its reduction. The mass loss also increases with the normal load. The influence of the normal load on the friction coefficient is more significant than that of the sliding speed. The effect of the sliding speed decreases for large speed values. The increase of the amount of graphite powder leads to a decrease of the coefficient of friction, the mass loss and the wear rate. The addition of graphite to the UP resin is beneficial; it plays the role of solid lubricant.
Abstract: Tribological properties that include nanoparticles are an alternative to improve the tribological behaviour of lubricating oil, which has been investigated by many researchers for the past few decades. Various nanostructures can be used as additives for tribological improvement. However, this also depends on the characteristics of the nanoparticles. In this study, tribological investigation was performed to examine the effect of CuO nanoparticles on the tribological behaviour of Syntium 800 SL 10W−30. Three parameters used in the analysis using the wear tester (piston ring) were load, revolutions per minute (rpm), and concentration. The specifications of the nanoparticles, such as size, concentration, hardness, and shape, can affect the tribological behaviour of the lubricant. The friction and wear experiment was conducted using a tribo-tester and the Response Surface Methodology method was used to analyse any improvement of the performance. Therefore, two concentrations of 40 nm nanoparticles were used to conduct the experiments, namely, 0.005 wt % and 0.01 wt % and compared with base oil 0 wt % (control). A water bath sonicator was used to disperse the nanoparticles in base oil, while a tribo-tester was used to measure the coefficient of friction and wear rate. In addition, the thermal properties of the nanolubricant were also measured. The results have shown that the thermal conductivity of the nanolubricant was increased when compared with the base oil. Therefore, the results indicated that CuO nanoparticles had improved the tribological behaviour as well as the thermal properties of the nanolubricant oil.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: The main emphasis of metallurgists has been to process the materials to obtain the balanced mechanical properties for the given application. One of the processing routes to alter the properties is heat treatment. Nearly 90% of the structural applications are related to the medium carbon an alloyed steels and hence are regarded as structural steels. The major requirement in the conventional steel is to improve workability, toughness, hardness and grain refinement. In this view, it is proposed to study the mechanical and tribological properties of unalloyed structural (AISI 1140) steel with different thermal (heat) treatments like annealing, normalizing, tempering and hardening and compared with as brought (cold worked) specimen. All heat treatments are carried out in atmospheric condition. Hardening treatment improves hardness of the material, a marginal decrease in hardness value with improved ductility is observed in tempering. Annealing and normalizing improve ductility of the specimen. Normalized specimen shows ultimate ductility. Hardened specimen shows highest wear resistance in the initial period of slide wear where as above 25KM of sliding distance, as brought steel dominates the hardened specimen. Both mild and severe wear regions are observed. Microstructural analysis shows the existence of pearlitic structure in normalized specimen, lath martensitic structure in hardened, pearlitic, ferritic structure in annealed specimen.
Abstract: The mechanical and tribological properties in WC-Co
coatings are strongly affected by hardness and elasticity
specifications. The results revealed the effect of spraying distance on
microhardness and elasticity modulus of coatings. The metallurgical
studies have been made on coated samples using optical microscopy,
scanning electron microscopy (SEM).
Abstract: The mechanical and tribological properties in WC-Co
coatings are strongly affected by hardness and elasticity
specifications. The results revealed the effect of spraying distance on
microhardness and elasticity modulus of coatings. The metallurgical
studies have been made on coated samples using optical microscopy,
scanning electron microscopy (SEM).
Abstract: In the present work, a comparative study on the
microstructure and mechanical properties of as cast, cast aged and
forged aged A356 alloy has been investigated. The study reveals that
mechanical properties of A356 alloy are highly influenced by melt
treatment and solid state processing. Cast aged alloys achieve highest
strength and hardness compared to as cast and forge aged ones. Ones
treated with combined addition of grain refiners and modifiers
achieve maximum strength and hardness. Cast aged A356 alloy
possesses higher wear resistance compared to as cast and forge aged
ones. Forging improves both strength and ductility of alloys over as
cast ones. However, the improvement in ductility is perceptible only
for properly grain refined and modified alloys. Ones refined with
0.65% Al-3Ti shows highest improvement in ductility while ones
treated with 0.20% Al-10Sr exhibits less improvement in ductility.