Abstract: Non-crimp three-dimensional (3D) orthogonal carbon fabrics are one of the useful textiles reinforcements in composites. In this paper, flexural and bending properties of a carbon non-crimp 3D orthogonal woven reinforcement are experimentally investigated. The present study is focused on the understanding and measurement of the main bending parameters including flexural stress, strain, and modulus. For this purpose, the three-point bending test method is used and the load-displacement curves are analyzed. The influence of some weave's parameters such as yarn type, geometry of structure, and fiber volume fraction on bending behavior of non-crimp 3D orthogonal carbon fabric is investigated. The obtained results also represent a dataset for the simulation of flexural behavior of non-crimp 3D orthogonal weave carbon composite reinforcement.
Abstract: In order to predict and model wrinkling which is caused by out of plane deformation due to compressive loading in the plane of the material during composite prepregs forming, it is necessary to quantitatively understand the relative magnitude of the bending stiffness. This study aims to examine the bending properties of out-of-autoclave (OOA) thermosetting prepreg under vertical cantilever test condition. A direct method for characterizing the bending behavior of composite prepregs was developed. The results from direct measurement were compared with results derived from an image-processing procedure that analyses the captured image during the vertical bending test. A numerical simulation was performed using ABAQUS to confirm the bending stiffness value.
Abstract: Aim of this work is to determine the theoretical and
experimental properties of filament wound glass fiber/epoxy resin
composite pipes with different winding design subjected under
bending. For determination of bending strength of composite samples
three point bending tests were conducted. Good correlation between
theoretical and experimental results has been obtained, where sample
No4 has shown the highest value of bending strength. All samples
have demonstrated matrix cracking and fiber failure followed by
layers delamination during testing. Also, it was found that smaller
winding angles lead to an increase in bending stress. From presented
results good merger between glass fibers and epoxy resin was
confirmed by SEM analysis.
Abstract: The suitability of Newsprint and Kraft papers for the production of cement bonded ceiling board was investigated. Sample boards were produced from newsprint paper (100%), mixture of newsprint and Kraft paper (50:50) and Kraft paper (100%) at 1:1, 2:1 and 3:1 cement/paper mixing ratio respectively with 3% additive concentration of calcium chloride (CaCl2). Density, flexural and thickness swelling properties of the boards were investigated. The effects of paper type and mixing ratio on the physical and mechanical properties were also examined. The bending properties of the board which include Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) increased linearly with increase in density. Modulus of rupture of boards increased as the density and mixing ratio increased. The thickness swelling property for the two paper types decreased as the board density and mixing ratio increased. Boards made from Kraft paper recorded higher strength values than the ones made from recycled newsprint paper while the mixture of kraft and newsprint papers had the best surface finish. The result of the study will help in managing the large quality of waste from paper converting/carton industry and that the ceiling boards produced could be installed with clout nails or used with suspended ceiling fittings.
Abstract: In order to supplement the brittle property of concrete,
fibers are added into concrete mixtures. Compared to general concrete,
various characteristics such as tensile strength, bending strength,
bending toughness, and resistance to crack are superior, and even
when cracks occur, improvements on toughness as well as resistance
to shock are excellent due to the growth of fracture energy. Increased
function of steel fiber reinforced concrete can be differentiated
depending on the fiber dispersion, and sand percentage can be an
important influence on the fiber dispersion. Therefore, in this research,
experiments were planned on sand percentage in order to apprehend
the influence of sand percentage on the bending properties and direct
tension of SFRC and basic experiments were conducted on bending
and direct tension in order to recognize the properties of bending
properties and direct tension following the size of the aggregates and
sand percentage.