Abstract: Alkylated silicon nanocrystals (C11-SiNCs) were
prepared successfully by galvanostatic etching of p-Si(100) wafers
followed by a thermal hydrosilation reaction of 1-undecene in
refluxing toluene in order to extract C11-SiNCs from porous silicon.
Erbium trichloride was added to alkylated SiNCs using a simple
mixing chemical route. To the best of our knowledge, this is the first
investigation on mixing SiNCs with erbium ions (III) by this
chemical method. The chemical characterization of C11-SiNCs and
their mixtures with Er3+(Er/C11-SiNCs) were carried out using X-ray
photoemission spectroscopy (XPS). The optical properties of C11-
SiNCs and their mixtures with Er3+ were investigated using Raman
spectroscopy and photoluminescence (PL). The erbium mixed
alkylated SiNCs shows an orange PL emission peak at around 595
nm that originates from radiative recombination of Si. Er/C11-SiNCs
mixture also exhibits a weak PL emission peak at 1536 nm that
originates from the intra-4f transition in erbium ions (Er3+). The PL
peak of Si in Er/C11-SiNCs mixture is increased in the intensity up to
three times as compared to pure C11-SiNCs. The collected data
suggest that this chemical mixing route leads instead to a transfer of
energy from erbium ions to alkylated SiNCs.
Abstract: In this paper, extract of papaya leaves are used as a
natural dye and combined by variations of solvent concentration
applied on DSSC (Dye-Sensitized Solar Cell). Indonesian geographic
located on the equator line occasions the magnitude of the potential
to develop organic solar cells made from extracts of chlorophyll as a
substitute for inorganic materials or synthetic dye on DSSC material.
Dye serves as absorbing photons which are then converted into
electrical energy. A conductive coated glass layer called TCO
(Transparent Conductive Oxide) is used as a substrate of electrode.
TiO2 nanoparticles as binding dye molecules, redox couple iodide/
tri-iodide as the electrolyte and carbon as the counter electrode in the
DSSC are used. TiO2 nanoparticles, organic dyes, electrolytes, and
counter electrode are arranged and combined with the layered
structure of the photo-catalyst absorption layer. Dye absorption
measurements using a spectrophotometer at 400-800 nm light
spectrum produces a total amount of chlorophyll 80.076 mg/l. The
test cell at 7 watt LED light with 5000 lux luminescence was
obtained Voc and Isc of 235.5 mV and 14 μA, respectively.
Abstract: The thermal conductivity of a fluid can be
significantly enhanced by dispersing nano-sized particles in it, and
the resultant fluid is termed as "nanofluid". A theoretical model for
estimating the thermal conductivity of a nanofluid has been proposed
here. It is based on the mechanism that evenly dispersed
nanoparticles within a nanofluid undergo Brownian motion in course
of which the nanoparticles repeatedly collide with the heat source.
During each collision a rapid heat transfer occurs owing to the solidsolid
contact. Molecular dynamics (MD) simulation of the collision
of nanoparticles with the heat source has shown that there is a pulselike
pick up of heat by the nanoparticles within 20-100 ps, the extent
of which depends not only on thermal conductivity of the
nanoparticles, but also on the elastic and other physical properties of
the nanoparticle. After the collision the nanoparticles undergo
Brownian motion in the base fluid and release the excess heat to the
surrounding base fluid within 2-10 ms. The Brownian motion and
associated temperature variation of the nanoparticles have been
modeled by stochastic analysis. Repeated occurrence of these events
by the suspended nanoparticles significantly contributes to the
characteristic thermal conductivity of the nanofluids, which has been
estimated by the present model for a ethylene glycol based nanofluid
containing Cu-nanoparticles of size ranging from 8 to 20 nm, with
Gaussian size distribution. The prediction of the present model has
shown a reasonable agreement with the experimental data available
in literature.
Abstract: Liposome plays an important role in medical and
pharmaceutical science as e.g. nano scale drug carriers. Liposomes
are vesicles of varying size consisting of a spherical lipid bilayer and
an aqueous inner compartment. Magnet-driven liposome used for the
targeted delivery of drugs to organs and tissues. These liposome
preparations contain encapsulated drug components and finely
dispersed magnetic particles.
Liposomes are vesicles of varying size consisting of a spherical
lipid bilayer and an aqueous inner compartment that are generated in
vitro. These are useful in terms of biocompatibility, biodegradability,
and low toxicity, and can control biodistribution by changing the size,
lipid composition, and physical characteristics. Furthermore,
liposomes can entrap both hydrophobic and hydrophilic drugs and are
able to continuously release the entrapped substrate, thus being useful
drug carriers. Magnetic liposomes (MLs) are phospholipid vesicles
that encapsulate magneticor paramagnetic nanoparticles. They are
applied as contrast agents for magnetic resonance imaging (MRI).
The biological synthesis of nanoparticles using plant extracts plays
an important role in the field of nanotechnology. Green-synthesized
magnetite nanoparticles-protein hybrid has been produced by treating
Iron (III) / Iron (II) chloride with the leaf extract of Datura inoxia.
The phytochemicals present in the leaf extracts act as a reducing as
well stabilizing agents preventing agglomeration, which include
flavonoids, phenolic compounds, cardiac glycosides, proteins and
sugars.
The magnetite nanoparticles-protein hybrid has been trapped
inside the aqueous core of the liposome prepared by reversed phase
evaporation (REV) method using oleic and linoleic acid which has
been shown to be driven under magnetic field confirming the
formation magnetic liposome (ML). Chemical characterization of
stealth magnetic liposome has been performed by breaking the
liposome and release of magnetic nanoparticles. The presence iron
has been confirmed by colour complex formation with KSCN and
UV-Vis study using spectrophotometer Cary 60, Agilent.
This magnet driven liposome using nanoparticles-protein hybrid
can be a smart vesicles for the targeted drug delivery.
Abstract: In order to manufacture short gap single Si nanowire
(NW) field effect transistor (FET) by imprinting and transferring
method, we introduce the method using Al2O3 sacrificial layer. The
diameters of cylindrical Si NW addressed between Au electrodes by
dielectrophoretic (DEP) alignment method are controlled to 106, 128,
and 148 nm. After imprinting and transfer process, cylindrical Si NW
is embedded in PVP adhesive and dielectric layer. By curing
transferred cylindrical Si NW and Au electrodes on PVP-coated p++ Si
substrate with 200nm-thick SiO2, 3μm gap Si NW FET fabrication
was completed. As the diameter of embedded Si NW increases, the
mobility of FET increases from 80.51 to 121.24 cm2/V·s and the
threshold voltage moves from –7.17 to –2.44 V because the ratio of
surface to volume gets reduced.
Abstract: In this research, waterglass based aerogel powder was
prepared by sol–gel process and ambient pressure drying. Inspired by
limited dust releasing, aerogel powder was introduced to the PET
electrospinning solution in an attempt to create required bulk and
surface structure for the nanofibers to improve their hydrophobic and
insulation properties. The samples evaluation was carried out by
measuring density, porosity, contact angle, heat transfer, FTIR, BET,
and SEM. According to the results, porous silica aerogel powder was
fabricated with mean pore diameter of 24 nm and contact angle of
145.9º. The results indicated the usefulness of the aerogel powder
confined into nanofibers to control surface roughness for
manipulating superhydrophobic nanowebs with water contact angle
of 147º. It can be due to a multi-scale surface roughness which was
created by nanowebs structure itself and nanofibers surface
irregularity in presence of the aerogels while a layer of fluorocarbon
created low surface energy. The wettability of a solid substrate is an
important property that is controlled by both the chemical
composition and geometry of the surface. Also, a decreasing trend in
the heat transfer was observed from 22% for the nanofibers without
any aerogel powder to 8% for the nanofibers with 4% aerogel
powder. The development of thermal insulating materials has become
increasingly more important than ever in view of the fossil energy
depletion and global warming that call for more demanding energysaving
practices.
Abstract: This paper investigates the viability of using carbon
fiber reinforced epoxy composites modified with carbon nanotubes to
strengthening reinforced concrete (RC) columns. Six RC columns
was designed and constructed according to ASCE standards. The
columns were wrapped using carbon fiber sheets impregnated with
either neat epoxy or CNTs modified epoxy. These columns were then
tested under concentric axial loading. Test results show that;
compared to the unwrapped specimens; wrapping concrete columns
with carbon fiber sheet embedded in CNTs modified epoxy resulted
in an increase in its axial load resistance, maximum displacement,
and toughness values by 24%, 109% and 232%, respectively. These
results reveal that adding CNTs into epoxy resin enhanced the
confinement effect, specifically, increased the axial load resistance,
maximum displacement, and toughness values by 11%, 6%, and
19%, respectively compared with columns strengthening with carbon
fiber sheet embedded in neat epoxy.
Abstract: The paper involves a chain of activities from
synthesis, establishment of the methodology for characterization and
testing of novel protective materials through the pilot production and
application on model supports.
It summarizes the results regarding the development of the pilot
production protocol for newly developed self-cleaning materials. The
optimization of the production parameters was completed in order to
improve the most important functional properties (mineralogy
characteristics, particle size, self-cleaning properties and
photocatalytic activity) of the newly designed nanocomposite
material.
Abstract: Rhodamine B (RB) is a toxic dye used extensively in
textile industry, which must be remediated before its drainage to
environment. In the present study, supported gold nanoparticles on
commercially available titania and zincite were successfully prepared
and then their activity on the photodegradation of RB under UV A
light irradiation were evaluated. The synthesized photocatalysts were
characterized by ICP, BET, XRD, and TEM. Kinetic results showed
that Au/TiO2 was an inferior photocatalyst to Au/ZnO. This
observation could be attributed to the strong reflection of UV
irradiation by gold nanoparticles over TiO2 support.
Abstract: Carbon nanotube is one of the most attractive materials
for the potential applications of nanotechnology due to its excellent
mechanical, thermal, electrical and optical properties. In this paper we
report a supercapacitor made of nickel foil electrodes, coated with
multiwall carbon nanotubes (MWCNTs) thin film using
electrophoretic deposition (EPD) method. Chemical vapor deposition
method was used for the growth of MWCNTs and ethanol was used as
a hydrocarbon source. High graphitic multiwall carbon nanotube was
found at 750oC analyzing by Raman spectroscopy. We observed the
electrochemical performance of supercapacitor by cyclic
voltammetry. The electrodes of supercapacitor fabricated from
MWCNTs exhibit considerably small equivalent series resistance
(ESR), and a high specific power density. Electrophoretic deposition
is an easy method in fabricating MWCNT electrodes for high
performance supercapacitor.
Abstract: In this study, epoxy composite specimens reinforced
with multi-walled carbon nanotube filler were fabricated using shear
mixer and ultra-sonication processor. The mechanical and thermal
properties of the fabricated specimens were measured and evaluated.
From the electron microscope images and the results from the
measurements of tensile strengths, the specimens having 0.6 wt%
nanotube content show better dispersion and higher strength than those
of the other specimens. The Young’s moduli of the specimens
increased as the contents of the nanotube filler in the matrix were
increased. The specimen having a 0.6 wt% nanotube filler content
showed higher thermal conductivity than that of the other specimens.
While, in the measurement of thermal expansion, specimens having
0.4 and 0.6 wt% filler contents showed a lower value of thermal
expansion than that of the other specimens. On the basis of the
measured and evaluated properties of the composites, we believe that
the simple and time-saving fabrication process used in this study was
sufficient to obtain improved properties of the specimens.
Abstract: Nanocrystalline powders of the lead-free piezoelectric
material, tantalum-substituted potassium sodium niobate
(K0.5Na0.5)(Nb0.9Ta0.1)O3 (KNNT), were produced using a Retsch
PM100 planetary ball mill by setting the milling time to 15h, 20h,
25h, 30h, 35h and 40h, at a fixed speed of 250rpm. The average
particle size of the milled powders was found to decrease from 12nm
to 3nm as the milling time increases from 15h to 25h, which is in
agreement with the existing theoretical model. An anomalous
increase to 98nm and then a drop to 3nm in the particle size were
observed as the milling time further increases to 30h and 40h
respectively. Various sizes of these starting KNNT powders were
used to investigate the effect of milling time on the microstructure,
dielectric properties, phase transitions and piezoelectric properties of
the resulting KNNT ceramics. The particle size of starting KNNT
was somewhat proportional to the grain size. As the milling time
increases from 15h to 25h, the resulting ceramics exhibit
enhancement in the values of relative density from 94.8% to 95.8%,
room temperature dielectric constant (εRT) from 878 to 1213, and
piezoelectric charge coefficient (d33) from 108pC/N to 128pC/N. For
this range of ceramic samples, grain size refinement suppresses the
maximum dielectric constant (εmax), shifts the Curie temperature (Tc)
to a lower temperature and the orthorhombic-tetragonal phase
transition (Tot) to a higher temperature. Further increase of milling
time from 25h to 40h produces a gradual degradation in the values of
relative density, εRT, and d33 of the resulting ceramics.
Abstract: The main purpose of this work was verify the
influence of the accelerated carbonation in the physical and
mechanical properties of the hybrid composites, reinforced with
micro and nanofibers and composites with microfibers. The
composites were produced by the slurry vacuum dewatering method,
followed by pressing. It was produced using two formulations: 8% of
eucalyptus pulp + 1% of the nanofibrillated cellulose and 9% of
eucalyptus pulp, both were subjected to accelerated carbonation. The
results showed that the accelerated carbonation contributed to
improve the physical and mechanical properties of the hybrid
composites and of the composites reinforced with microfibers
(eucalyptus pulp).
Abstract: This paper illustrates the effect of nano Magnesium
Hydroxide (MH) loading on the thermal properties of Low Density
Polyethylene (LDPE)/Poly (ethylene-co vinyl acetate) (EVA) nano
composite. Thermal studies were conducted, as it understanding is
vital for preliminary development of new polymeric systems.
Thermal analysis of nanocomposite was conducted using thermo
gravimetric analysis (TGA), and differential scanning calorimetry
(DSC). Major finding of TGA indicated two main stages of
degradation process found at (350 ± 25oC) and (480 ± 25oC)
respectively. Nano metal filler expressed better fire resistance as it
stand over high degree of temperature. Furthermore, DSC analysis
provided a stable glass temperature around 51 (±1oC) and captured
double melting point at 84 (±2oC) and 108 (±2oC). This binary
melting point reflects the modification of nano filler to the polymer
matrix forming melting crystals of folded and extended chain. The
percent crystallinity of the samples grew vividly with increasing filler
content. Overall, increasing the filler loading improved the
degradation temperature and weight loss evidently and a better
process and phase stability was captured in DSC.
Abstract: A modeling approach for CMOS gates is presented
based on the use of the equivalent inverter. A new model for the
inverter has been developed using a simplified transistor current
model which incorporates the nanoscale effects for the planar
technology. Parametric expressions for the output voltage are
provided as well as the values of the output and supply current to be
compatible with the CCS technology. The model is parametric
according the input signal slew, output load, transistor widths, supply
voltage, temperature and process. The transistor widths of the
equivalent inverter are determined by HSPICE simulations and
parametric expressions are developed for that using a fitting
procedure. Results for the NAND gate shows that the proposed
approach offers sufficient accuracy with an average error in
propagation delay about 5%.
Abstract: Nanostructured catalysts were successfully prepared
by acidification of diatomite and regeneration of FCC spent catalysts.
The obtained samples were characterized by IR, XRD, SEM, EDX,
MAS-NMR (27Al and 29Si), NH3-TPD and tested in catalytic
pyrolysis of biomass (rice straw). The results showed that the similar
bio-oil yield of 41.4% can be obtained by pyrolysis with catalysts at
450oC as compared to that of the pyrolysis without catalyst at 550oC.
The bio-oil yield reached a maximum of 42.55% at the pyrolysis
temperature of 500oC with catalytic content of 20%. Moreover, by
catalytic pyrolysis, bio-oil quality was better as reflected in higher
ratio of H/C, lower ratio of O/C. This clearly indicated high
application potential of these new nanostructured catalysts in the
production of bio-oil with low oxygenated compounds.
Abstract: The influence of three different types of halloysite
nanotubes (HNTs) with different dimensions, namely as camel lake
(CLA), Jarrahdale (JA) and Matauri Bay (MB), on their reinforcing
ability of ethylene propylene dine monomer (EPDM) were
investigated by varying the HNTs loading (from 0-15 phr).
Mechanical properties of the nanocomposites improved with addition
of all three HNTs, but CLA based nanocomposites exhibited a
significant enhancement compared to the other HNTs. For instance,
tensile properties of EPDM nanocomposites increased by 120%,
256% and 340% for MB, JA and CLA, respectively, with addition of
15 phr of HNTs. This could be due to the higher aspect ratio and
higher surface area of CLA compared to others. Scanning electron
microscopy (SEM) of nanocomposites at 15 phr of HNT loadings
showed low amounts of pulled-out nanotubes which confirmed the
presence of more embedded nanotubes inside the EPDM matrix, as
well as aggregates within the fracture surface of EPDM/HNT
nanocomposites
Abstract: The biosynthesis of nanoparticles by microorganisms,
on the contrary to chemical synthesis, is an environmentally-friendly
process which has low energy requirements. In this investigation, we
used the microorganism Geobacillus wiegelii, strain GWE1, an
aerobic thermophile belonging to genus Geobacillus, isolated from a
drying oven. This microorganism has the ability to reduce selenite
evidenced by the change of color from colorless to red in the culture.
Elemental analysis and composition of the particles were verified
using transmission electron microscopy and energy-dispersive X-ray
analysis. The nanoparticles have a defined spherical shape and a
selenium elemental state. Previous experiments showed that the
presence of the whole microorganism for the reduction of selenite
was not necessary. The results strongly suggested that an intracellular
NADPH/NADH-dependent reductase mediates selenium
nanoparticles synthesis under aerobic conditions. The enzyme was
purified and identified by mass spectroscopy MALDI-TOF TOF
technique. The enzyme is a 1-pyrroline-5-carboxylate dehydrogenase.
Histograms of nanoparticles sizes were obtained. Size distribution
ranged from 40-160 nm, where 70% of nanoparticles have less than
100 nm in size. Spectroscopic analysis showed that the nanoparticles
are composed of elemental selenium. To analyse the effect of pH in
size and morphology of nanoparticles, the synthesis of them was
carried out at different pHs (4.0, 5.0, 6.0, 7.0, 8.0). For
thermostability studies samples were incubated at different
temperatures (60, 80 and 100 ºC) for 1 h and 3 h. The size of all
nanoparticles was less than 100 nm at pH 4.0; over 50% of
nanoparticles have less than 100 nm at pH 5.0; at pH 6.0 and 8.0 over
90% of nanoparticles have less than 100 nm in size. At neutral pH
(7.0) nanoparticles reach a size around 120 nm and only 20% of them
were less than 100 nm. When looking at temperature effect,
nanoparticles did not show a significant difference in size when they
were incubated between 0 and 3 h at 60 ºC. Meanwhile at 80 °C the
nanoparticles suspension lost its homogeneity. A change in size was
observed from 0 h of incubation at 80ºC, observing a size range
between 40-160 nm, with 20% of them over 100 nm. Meanwhile
after 3 h of incubation at size range changed to 60-180 nm with 50%
of them over 100 nm. At 100 °C the nanoparticles aggregate forming
nanorod structures. In conclusion, these results indicate that is
possible to modulate size and shape of biologically synthesized
nanoparticles by modulating pH and temperature.
Abstract: Composites depending on the nature of their
constituents and mode of production are regarded as one of the
advanced materials that drive today’s technology. This paper
attempts a short review of the subject matter with a general aim of
pushing to the next level the frontier of knowledge as it impacts the
technology of nano-particles manufacturing. The objectives entail an
effort to; aggregate recent research efforts in this field, analyse
research findings and observations, streamline research efforts and
support industry in taking decision on areas of fund deployment. It is
envisaged that this work will serve as a quick hand-on compendium
material for researchers in this field and a guide to relevant
government departments wishing to fund a research whose outcomes
have the potential of improving the nation’s GDP.
Abstract: A series of polystyrene (PS) nanoparticles were
prepared by grafting polystyrene from both aggregated silica and
colloidally dispersed silica nanoparticles using atom-transfer radical
polymerisation (ATRP). Cross-linking and macroscopic gelation
were minimised by using a miniemulsion system. The thermal and
mechanical behaviour of the nanocomposites have been examined by
differential scanning calorimetry (DSC) and dynamic mechanical
thermal analysis (DMTA).