Abstract: n-CdO/p-Si heterojunction diode was fabricated using
sol-gel spin coating technique which is a low cost and easily scalable
method for preparing of semiconductor films. The structural and
morphological properties of CdO film were investigated. The X-ray
diffraction (XRD) spectra indicated that the film was of
polycrystalline nature. The scanning electron microscopy (SEM)
images indicate that the surface morphology CdO film consists of the
clusters formed with the coming together of the nanoparticles. The
electrical characterization of Au/n-CdO/p–Si/Al heterojunction diode
was investigated by current-voltage. The ideality factor of the diode
was found to be 3.02 for room temperature. The reverse current of
the diode strongly increased with illumination intensity of 100
mWcm-2 and the diode gave a maximum open circuit voltage Voc of
0.04 V and short-circuits current Isc of 9.92×10-9 A.
Abstract: In this investigation, anatase TiO2 thin films were
grown by radio frequency magnetron sputtering on glass substrates at
a high sputtering pressure and room temperature. The anatase films
were then annealed at 300-600 °C in air for a period of 1 hour. To
examine the structure and morphology of the films, X-ray diffraction
(XRD) and atomic force microscopy (AFM) methods were used
respectively. From X-ray diffraction patterns of the TiO2 films, it was
found that the as-deposited film showed some differences compared
with the annealed films and the intensities of the peaks of the
crystalline phase increased with the increase of annealing
temperature. From AFM images, the distinct variations in the
morphology of the thin films were also observed. The optical
constants were characterized using the transmission spectra of the
films obtained by UV-VIS-IR spectrophotometer. Besides, optical
thickness of the film deposited at room temperature was calculated
and cross-checked by taking a cross-sectional image through SEM.
The optical band gaps were evaluated through Tauc model. It was
observed that TiO2 films produced at room temperatures exhibited
high visible transmittance and transmittance decreased slightly with
the increase of annealing temperatures. The films were found to be
crystalline having anatase phase. The refractive index of the films
was found from 2.31-2.35 in the visible range. The extinction
coefficient was nearly zero in the visible range and was found to
increase with annealing temperature. The allowed indirect optical
band gap of the films was estimated to be in the range from 3.39 to
3.42 eV which showed a small variation. The allowed direct band
gap was found to increase from 3.67 to 3.72 eV. The porosity was
also found to decrease at a higher annealing temperature making the
film compact and dense.
Abstract: Commercial nanocomposite food packaging type nano-silver containers were characterised using scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). The presence of nanoparticles consistent with the incorporation of 1% nano-silver (Ag) and 0.1% titanium dioxide (TiO2) nanoparticle into polymeric materials formed into food containers was confirmed. Both nanomaterials used in this type of packaging appear to be embedded in a layered configuration within the bulk polymer. The dimensions of the incorporated nanoparticles were investigated using X-ray diffraction (XRD) and determined by calculation using the Scherrer Formula; these were consistent with Ag and TiO2 nanoparticles in the size range 20-70nm both were spherical shape nanoparticles. Antimicrobial assessment of the nanocomposite container has also been performed and the results confirm the antimicrobial activity of Ag and TiO2 nanoparticles in food packaging containers. Migration assessments were performed in a wide range of food matrices to determine the migration of nanoparticles from the packages. The analysis was based upon the relevant European safety Directives and involved the application of inductively coupled plasma mass spectrometry (ICP-MS) to identify the range of migration risk. The data pertain to insignificance levels of migration of Ag and TiO2 nanoparticles into the selected food matrices.
Abstract: Adsorption of Toluidine blue dye from aqueous solutions onto Neem Leaf Powder (NLP) has been investigated. The surface characterization of this natural material was examined by Particle size analysis, Scanning Electron Microscopy (SEM), Fourier Transform Infrared (FTIR) spectroscopy and X-Ray Diffraction (XRD). The effects of process parameters such as initial concentration, pH, temperature and contact duration on the adsorption capacities have been evaluated, in which pH has been found to be most effective parameter among all. The data were analyzed using the Langmuir and Freundlich for explaining the equilibrium characteristics of adsorption. And kinetic models like pseudo first- order, second-order model and Elovich equation were utilized to describe the kinetic data. The experimental data were well fitted with Langmuir adsorption isotherm model and pseudo second order kinetic model. The thermodynamic parameters, such as Free energy of adsorption (AG"), enthalpy change (AH') and entropy change (AS°) were also determined and evaluated.
Abstract: Commercial hydroxyapatite (HA) was reinforced by
adding 2, 5, and 10 wt % of 28.5%CaO-28.5%P2O5-38%Na2 O-
5%CaF2 based glass and then sintered. Although HA shows good
biocompatibility with the human body, its applications are limited to
non load-bearing areas and coatings due to its poor mechanical
properties. These mechanical properties can be improved
substantially with addition of glass ceramics by sintering. In this
study, the effects of sintering hydroxyapatite with above specified
phosphate glass additions are quantified. Each composition was
sintered over a range of temperatures. Scanning electron microscopy
and x-ray diffraction were used to characterize the microstructure and
phases of the composites. The density, microhardness, and
compressive strength were measured using Archimedes Principle,
Vickers Microhardness Tester (at 0.98 N), and Instron Universal
Testing Machine (cross speed of 0.5 mm/min) respectively. These
results were used to indicate which composition provided suitable
material for use in hard tissue replacement. Composites containing 10
wt % glass additions formed dense HA/TCP (tricalcium phosphate)
composite materials possessing good compressive strength and
hardness than HA. In-vitro bioactivity was assessed by evaluating
changes in pH and Ca2+ ion concentration of SBF-simulated body
fluid on immersion of these composites in it for two weeks.
Abstract: In this study, hydroxyapatite (HA) composites are
prepared on addition of 30%CaO-30%P2O5-40%Na2 O based glass to
pure HA, in proportion of 2, 5, and 10 wt %. Each composition was
sintered over a range of temperatures. The quantitative phase
analysis was carried out using XRD and the microstructures were
studied using SEM. The density, microhardness, and compressive
strength have shown increase with the increasing amount of glass
addition. The resulting composites have chemical compositions that
are similar to the inorganic constituent of the mineral part of bone,
and constitutes trace elements like Na. X-ray diffraction showed no
decomposition of HA to secondary phases, however, the glass
reinforced-HA composites contained a HA phase and variable
amounts of tricalcium phosphate phase, depending on the amount of
bioglass added. The HA-composite material exhibited higher
compressive strength compared to sintered HA. The HA composite
reinforced with 10 wt % bioglass showed highest bioactivity level.
Abstract: Considering toxicity of heavy metals and their
accumulation in domestic wastes, immobilization of lead and
cadmium is envisaged inside glass-ceramics. We particularly
focused this work on calcium-rich phases embedded in a
glassy matrix.
Glass-ceramics were synthesized from glasses doped with
12 wt% and 16 wt% of PbO or CdO. They were observed and
analyzed by Electron MicroProbe Analysis (EMPA) and
Analytical Scanning Electron Microscopy (ASEM). Structural
characterization of the samples was performed by powder XRay
Diffraction.
Diopside crystals of CaMgSi2O6 composition are shown to
incorporate significant amounts of cadmium (up to 9 wt% of
CdO). Two new crystalline phases are observed with very
high Cd or Pb contents: about 40 wt% CdO for the cadmiumrich
phase and near 60 wt% PbO for the lead-rich phase. We
present complete chemical and structural characterization of
these phases. They represent a promising way for the
immobilization of toxic elements like Cd or Pb since glass
ceramics are known to propose a “double barrier" protection
(metal-rich crystals embedded in a glass matrix) against metal
release in the environment.
Abstract: Mung bean starches were subjected to heat-moisture treatment (HMT) by different moisture contents (15%, 20%, 25%, 30% and 35%) at 120Ôäâ for 12h. The impact on the yields of resistant starch (RS), microstructure, physicochemical and functional properties was investigated. Compared to native starch, the RS content of heat-moisture treated starches increased significantly. The RS level of HMT-20 was the highest of all the starches. Birefringence was displayed clear at the center of native starch. For HMT starches, pronounced birefringence was exhibited on the periphery of starch granules; however, birefringence disappeared at the centre of some starch granules. The shape of HMT starches hadn-t been changed and the integrity of starch granules was preserved for all the conditions. Concavity could be observed on HMT starches under scanning electronic microscopy. After HMT, apparent amylose contents were increased and starch macromolecule was degraded in comparison with those of native starch. There was a reduction in swelling power on HMT starches, but the solubility of HMT starches was higher than that of native starch. Both of native and HMT starches showed A-type X-ray diffraction pattern. Furthermore, there is a higher intensity at the peak of 15.0 and 22.9 Å than those of native starch.
Abstract: This paper presents a experiment to estimate the
influences of cutting conditions in microstructure changes of
machining austenitic 304 stainless steel, especially for wear insert. The
wear insert were prefabricated with a width of 0.5 mm. And the forces,
temperature distribution, RS, and microstructure changes were
measured by force dynamometer, infrared thermal camera, X-ray
diffraction, XRD, SEM, respectively. The results told that the different
combinations of machining condition have a significant influence on
machined surface microstructure changes. In addition to that, the
ANOVA and AOMwere used to tell the different influences of cutting
speed, feed rate, and wear insert.
Abstract: Copper sulfide nanoparticles (CuS) were successfully synthesized by the pulsed plasma in liquid method, using two copper rod electrodes submerged in molten sulfur. Low electrical energy and no high temperature were applied for synthesis. Obtained CuS nanoparticles were then analyzed by means of X-ray diffraction, Low and High Resolution Transmission Electron Microscopy, Electron Diffraction, X-ray Photoelectron, Raman Spectroscopies and Field Emission Scanning Electron Microscopy. XRD analysis revealed peaks for CuS with hexagonal phase composition. TEM and HRTEM studies showed that sizes of CuS nanoparticles ranged between 10-60 nm, with the average size of about 20 nm. Copper sulfide nanoparticles have short nanorod-like structure. Raman spectroscopy found peak for CuS at 474.2cm-1of Raman region.
Abstract: The selective wet-etching of amorphous and
crystalline region of Sb20Se80 thin films was carried out using organic
based solution e.g. amines. We report the development of an in situ
real-time method to study the wet chemical etching process of thin
films. Characterization of the structure and surface of films studied
by X-ray diffraction, SEM and EBSD methods has been done and
potential application suggested.
Abstract: The production of glass, ceramic materials and many non-ferrous metals (Zn, Cu, Pb, etc.), ferrous metals (pig iron) and others is connected with the use of a considerable number of initial solid raw materials. Before carrying out the basic technological processes (oxidized roasting, melting, agglomeration, baking) it is necessary to mix and homogenize the raw materials that have different chemical and phase content, granulometry and humidity. For this purpose zinc sulfide concentrates differing in origin are studied for their more complete characteristics using chemical, X-ray diffraction analyses, DTA and TGA as well as Mössbauer spectroscopy. The phases established in most concentrates are: β-ZnS, mZnS.nFeS, FeS2, CuFeS2, PbS, SiO2 (α-quartz). With the help of the developed by us a Web-based information system for a continued period of time different mix proportions from zinc concentrates are calculated and used in practice (roasting in fluidized bed reactor), which have to conform to the technological requirements of the zinc hydrometallurgical technological scheme.
Abstract: Magnesium wastes and scraps, one of the metal wastes, are produced by many industrial activities, all over the world. Their growing size is becoming a future problem for the world. In this study, the use of magnesium wastes as a raw material in the production of the magnesium borate hydrates are aimed. The method used in the experiments is hydrothermal synthesis. The conditions are set to, waste magnesium to B2O3, 1:3 as a molar ratio. Four different reaction times are studied which are 30, 60, 120 and 240 minutes. For the identification analyses X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR) and Raman spectroscopy techniques are used. As a result at all the reaction times magnesium borate hydrates are synthesized and the most crystalline forms are obtained at a reaction time of 120 minutes. The overall yields of the production are found between the values of 65-80 %.
Abstract: This study reports the preparation of soft magnetic ribbons of Fe-based amorphous alloys using the single-roller melt-spinning technique. Ribbon width varied from 142 mm to 213 mm and, with a thickness of approximately 22 μm 2 μm. The microstructure and magnetic properties of the ribbons were characterized by differential scanning calorimeter (DSC), X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and electrical resistivity measurements (ERM). The amorphous material properties dependence of the cooling rate and nozzle pressure have uneven surface in ribbon thicknesses are investigated. Magnetic measurement results indicate that some region of the ribbon exhibits good magnetic properties, higher saturation induction and lower coercivity. However, due to the uneven surface of 213 mm wide ribbon, the magnetic responses are not uniformly distributed. To understand the transformer magnetic performances, this study analyzes the measurements of a three-phase 2 MVA amorphous-cored transformer. Experimental results confirm that the transformer with a ribbon width of 142 mm has better magnetic properties in terms of lower core loss, exciting power, and audible noise.
Abstract: This paper presents a comparative study on
Vanadyl Phthalocyanine (VOPc) thin films deposited by thermal
evaporation and spin coating techniques. The samples
were prepared on cleaned glass substrates and annealed at
various temperatures ranging form 95oC to 155oC. To obtain
the morphological and structural properties of VOPc thin
films, X-ray diffraction (XRD) technique and atomic force
microscopy (AFM) have been implied. The AFM topographic
images show a very slight difference in the thermally grown
films, before and after annealing, however best results are
achieved for the spin-cast film annealed at 125oC. The XRD
spectra show no existence of the sharp peaks, suggesting the
material to be amorphous. The humps in the XRD patterns
indicate the presence of some crystallites.
Abstract: In this paper we report the technique of optical
induction of 2 and 3-dimensional (2D and 3D) photonic lattices in
photorefractive materials based on diffraction grating self replication
-Talbot effect. 1D and 2D different rotational symmery diffraction
masks with the periods of few tens micrometers and 532 nm cw laser
beam were used in the experiments to form an intensity modulated
light beam profile. A few hundred micrometric scale replications of
mask generated intensity structures along the beam propagation axis
were observed. Up to 20 high contrast replications were detected for
1D annular mask with 30
Abstract: The paper reports the preparation and photocatalytic
activity of ZnO/SnO2 and SnO2 nanoparticles. These nanoparticles
were synthesized by hydrothermal method. The products were
characterized by X-ray diffraction (XRD) and scanning electron
microscopy (SEM). Their grain sizes are about 50-100 nm. The
photocatalytic activities of these materials were investigated for
congo red removal from aqueous solution under UV light irradiation.
It was shown that the use of ZnO/SnO2 as photocatalyst have better
photocatalytic activity for degradation of congo red than SnO2 or
TiO2 (anatase, particle size: 30nm) alone.
Abstract: In this paper, an analysis of a target location estimation
system using the best linear unbiased estimator (BLUE) for high
performance radar systems is presented. In synthetic environments,
we are here concerned with three key elements of radar system
modeling, which makes radar systems operates accurately in strategic
situation in virtual ground. Radar Cross Section (RCS) modeling
is used to determine the actual amount of electromagnetic waves
that are reflected from a tactical object. Pattern Propagation Factor
(PPF) is an attenuation coefficient of the radar equation that contains
the reflection from the surface of the earth, the diffraction, the
refraction and scattering by the atmospheric environment. Clutter is
the unwanted echoes of electronic systems. For the data fusion of
output results from radar detection in synthetic environment, BLUE
is used and compared with the mean values of each simulation results.
Simulation results demonstrate the performance of the radar system.
Abstract: Contamination of aromatic compounds in water can
cause severe long-lasting effects not only for biotic organism but also
on human health. Several alternative technologies for remediation of
polluted water have been attempted. One of these is adsorption
process of aromatic compounds by using organic modified clay
mineral. Porous structure of clay is potential properties for molecular
adsorptivity and it can be increased by immobilizing hydrophobic
structure to attract organic compounds. In this work natural
montmorillonite were modified with cetyltrimethylammonium
(CTMA+) and was evaluated for use as adsorbents of aromatic
compounds: benzene, toluene, and 2-chloro phenol in its single and
multicomponent solution by ethanol:water solvent. Preparation of
CTMA-montmorillonite was conducted by simple ion exchange
procedure and characterization was conducted by using x-day
diffraction (XRD), Fourier-transform infra red (FTIR) and gas
sorption analysis. The influence of structural modification of
montmorillonite on its adsorption capacity and adsorption affinity of
organic compound were studied. It was shown that adsorptivity of
montmorillonite was increased by modification associated with
arrangements of CTMA+ in the structure even the specific surface
area of modified montmorillonite was lower than raw
montmorillonite. Adsorption rate indicated that material has affinity
to adsorb compound by following order: benzene> toluene > 2-chloro
phenol. The adsorption isotherms of benzene and toluene showed 1st
order adsorption kinetic indicating a partition phenomenon of
compounds between the aqueous and organophilic CTMAmontmorillonite.
Abstract: Performance of a cobalt doped sol-gel derived silica (Co/SiO2) catalyst for Fischer–Tropsch synthesis (FTS) in slurryphase reactor was studied using paraffin wax as initial liquid media. The reactive mixed gas, hydrogen (H2) and carbon monoxide (CO) in a molar ratio of 2:1, was flowed at 50 ml/min. Braunauer-Emmett- Teller (BET) surface area and X-ray diffraction (XRD) techniques were employed to characterize both the specific surface area and crystallinity of the catalyst, respectively. The reduction behavior of Co/SiO2 catalyst was investigated using the Temperature Programmmed Reduction (TPR) method. Operating temperatures were varied from 493 to 533K to find the optimum conditions to maximize liquid fuels production, gasoline and diesel.