Abstract: Spherical shaped magnetite (Fe3O4) and Au@Fe3O4
nanoparticles were successfully synthesized from Fe electrodes
immersed in water with CTAB surfactant and HAuCl4 solution using
simple method-pulsed plasma in liquid, without the use of dopants or
special conditions for stabilization. Vibrating sample magnetometer
indicated ferromagnetic behavior of particles at room temperature with
coercivity and saturation magnetization of (Hc=105 Oe, Ms=6.83
emu/g) for Fe3O4 and (Hc=175, Ms=3.56emu/g) for Au@Fe3O4
nanoparticles. Structure and morphology of nanoparticles were
characterized by X-ray Diffraction analysis and HR-TEM
measurements. The cytotoxicity of nanoparticles was indicated using a
XTT assay to be very low (cell viability: 98-89% with Fe3O4 and
99-91% for Au@Fe3O4 NPs).
Abstract: Copper sulfide nanoparticles (CuS) were successfully synthesized by the pulsed plasma in liquid method, using two copper rod electrodes submerged in molten sulfur. Low electrical energy and no high temperature were applied for synthesis. Obtained CuS nanoparticles were then analyzed by means of X-ray diffraction, Low and High Resolution Transmission Electron Microscopy, Electron Diffraction, X-ray Photoelectron, Raman Spectroscopies and Field Emission Scanning Electron Microscopy. XRD analysis revealed peaks for CuS with hexagonal phase composition. TEM and HRTEM studies showed that sizes of CuS nanoparticles ranged between 10-60 nm, with the average size of about 20 nm. Copper sulfide nanoparticles have short nanorod-like structure. Raman spectroscopy found peak for CuS at 474.2cm-1of Raman region.