Abstract: Graphene was dispersed using a tip sonicator and the
effect of surfactants were analysed. Sodium Dodecyl Sulphate (SDS)
and Polyvinyl Alcohol (PVA) were compared to observe whether or
not they had any effect on any de-wrinkling, and secondly whether
they aided to achieve better dispersions. There is a huge demand for
wrinkle free graphene as this will greatly increase its usefulness in
various engineering applications. A comprehensive literature on dewrinkling
graphene has been discussed. Low magnification Scanning
Electronic Microscopy (SEM) was conducted to assess the quality of
graphene de-wrinkling. The utilization of the PVA has significant
effect on de-wrinkling whereas SDS had minimal effect on the dewrinkling
of graphene.
Abstract: In this research, thorium dioxide mesoporous
nanocrystalline powder was synthesized through the sol-gel method
using hydrated thorium nitrate and ammonium hydroxide as starting
materials and Triton X100 as surfactant. ThO2 gel was characterized
by thermogravimetric (TGA), and prepared ThO2 powder was
subjected to scanning electron microscopy (SEM), X-ray diffraction
(XRD), and Brunauer-Emett-Teller (BET) analyses studies. Detailed
analyses show that prepared powder consisted of phase with the
space group Fm3m of thoria and its crystalline size was 12.6 nm. The
thoria possesses 16.7 m2/g surface area and the pore volume and size
calculated to be 0.0423 cc/g and 1.947 nm, respectively.
Abstract: The use of titanium fluoride and iron fluoride
(TiF3/FeF3) catalysts in combination with polutetrafluoroethylene
(PTFE) in plain zinc- dialkyldithiophosphate (ZDDP) oil is important
for the study of engine tribocomponents and is increasingly a strategy
to improve the formation of tribofilm and provide low friction and
excellent wear protection in reduced phosphorus plain ZDDP oil. The
influence of surface roughness and the concentration of
TiF3/FeF3/PTFE were investigated using bearing steel samples
dipped in lubricant solution at 100°C for two different heating time
durations. This paper addresses the effects of water drop contact
angle using different surface; finishes after treating them with
different lubricant combination. The calculated water drop contact
angles were analyzed using Design of Experiment software (DOE)
and it was determined that a 0.05 μm Ra surface roughness would
provide an excellent TiF3/FeF3/PTFE coating for antiwear resistance
as reflected in the Scanning electron microscopy (SEM) images and
the tribological testing under extreme pressure conditions. Both
friction and wear performance depend greatly on the PTFE/and
catalysts in plain ZDDP oil with 0.05 % phosphorous and on the
surface finish of bearing steel. The friction and wear reducing effects,
which was observed in the tribological tests, indicated a better micro
lubrication effect of the 0.05 μm Ra surface roughness treated at
100°C for 24 hours when compared to the 0.1 μm Ra surface
roughness with the same treatment.
Abstract: A novel chromium-free protective coating films based
on a zeolite coating was growing onto a FeCrAlloy metal using in –
situ hydrothermal method. The zeolite film was obtained using in-situ
crystallization process that is capable of coating large surfaces with
complex shape and in confined spaces has been developed. The
zeolite coating offers an advantage of a high mechanical stability and
thermal stability. The physicochemical properties were investigated
using X-ray diffraction (XRD), Electron Microscopy (SEM), Energy
Dispersive X–ray Analysis (EDX) and Thermogravimetric Analysis
(TGA). The transition from oxide-on-alloy wires to hydrothermally
synthesised uniformly zeolite coated surfaces was followed using
SEM and XRD. In addition, the robustness of the prepared coating
was confirmed by subjecting these to thermal cycling (ambient to
550oC).
Abstract: The synthesis of CuFe2O4 spinel powders by an
optimized combustion-like process followed by calcination is
described herein. The samples were characterized using X-ray
diffraction (XRD), differential thermal analysis (TG/DTA), scanning
electron microscopy (SEM), dilatometry and 4-probe DC methods.
Different glycine to nitrate (G/N) ratios of 1 (fuel-deficient), 1.48
(stoichiometric) and 2 (fuel-rich) were employed. Calcining the asprepared
powders at 800 and 1000°C for 5 hours showed that the G/N
ratio of 2 results in the formation of the desired copper spinel single
phase at both calcination temperatures. For G/N=1, formation of
CuFe2O4 takes place in three steps. First, iron and copper nitrates
decompose to iron oxide and pure copper. Then, copper transforms to
copper oxide and finally, copper and iron oxides react with each other
to form a copper ferrite spinel phase. The electrical conductivity and
the coefficient of thermal expansion of the sintered pelletized
samples were 2 S.cm-1 (800°C) and 11×10-6 °C-1 (25-800°C),
respectively.
Abstract: Processing of Al-19.4Si alloy by high intensive
electron beam has been carried out and multiple increases in fatigue
life of the material have been revealed. Investigations of structure and
surface modified layer destruction of Al-19.4Si alloy subjected to
multicycle fatigue tests to fracture have been carried out by methods
of scanning electron microscopy. The factors responsible for the
increase of fatigue life of Al-19.4Si alloy have been revealed and
analyzed.
Abstract: The future and the development of science is therefore
seen in interdisciplinary areas such as biomedical engineering. Selfassembled
structures, similar to stem cell niches would inhibit fast
division process and subsequently capture the stem cells from the
blood flow. By means of surface topography and the stiffness as well
as microstructure progenitor cells should be differentiated towards
the formation of endothelial cells monolayer which effectively will
inhibit activation of the coagulation cascade. The idea of the material
surface development met the interest of the clinical institutions,
which support the development of science in this area and are waiting
for scientific solutions that could contribute to the development of
heart assist systems. This would improve the efficiency of the
treatment of patients with myocardial failure, supported with artificial
heart assist systems. Innovative materials would enable the redesign,
in the post project activity, construction of ventricular heart assist.
Abstract: The nanoindentation behaviour and phase
transformation of annealed single-crystal silicon wafers are examined.
The silicon specimens are annealed at temperatures of 250, 350 and
450ºC, respectively, for 15 minutes and are then indented to maximum
loads of 30, 50 and 70 mN. The phase changes induced in the indented
specimens are observed using transmission electron microscopy
(TEM) and micro-Raman scattering spectroscopy (RSS). For all
annealing temperatures, an elbow feature is observed in the unloading
curve following indentation to a maximum load of 30 mN. Under
higher loads of 50 mN and 70 mN, respectively, the elbow feature is
replaced by a pop-out event. The elbow feature reveals a complete
amorphous phase transformation within the indented zone, whereas
the pop-out event indicates the formation of Si XII and Si III phases.
The experimental results show that the formation of these crystalline
silicon phases increases with an increasing annealing temperature and
indentation load. The hardness and Young’s modulus both decrease as
the annealing temperature and indentation load are increased.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: The aim of this study is to investigate formability of
Al based closed cell metallic foams at high temperature. The foam
specimens with rectangular section were produced from
AlMg1Si0.6TiH20.8 alloy preform material. Bending and free
bending tests based on gravity effect were applied to foam specimens
at high temperatures. During the tests, the time-angular deformation
relationships with various temperatures were determined.
Deformation types formed in cell walls were investigated by means
of Scanning Electron Microscopy (SEM) and optical microscopy.
Bending deformation about 90° was achieved without any defect at
high temperatures. The importance of a critical temperature and
deformation rate was emphasized in maintaining the deformation.
Significant slip lines on surface of cell walls at tensile zones of
bending specimen were observed. At high strain rates, the microcrack
formation in boundaries of elongated grains was determined.
Abstract: The secondary alloy A226 is used for many
automotive casting produced by mould casting and high pressure die
casting. This alloy has excellent castability, good mechanical
properties and cost-effectiveness. Production of primary aluminium
alloys belong to heavy source fouling of life environs. The European
Union calls for the emission reduction and reduction in energy
consumption therefore increase production of recycled (secondary)
aluminium cast alloys. The contribution is deal with influence of
recycling on the quality of the casting made from A226 in automotive
industry. The properties of the casting made from secondary
aluminium alloys were compared with the required properties of
primary aluminium alloys. The effect of recycling on microstructure
was observed using combination different analytical techniques (light
microscopy upon black-white etching, scanning electron microscopy
- SEM upon deep etching and energy dispersive X-ray analysis -
EDX). These techniques were used for the identification of the
various structure parameters, which was used to compare secondary
alloy microstructure with primary alloy microstructure.
Abstract: A chromium-loaded ash originating from incineration of tannery sludge under anoxic conditions was mixed with low grade soda-lime glass powder coming from commercial glass bottles. The relative weight proportions of ash over glass powder tested were 30/70, 40/60 and 50/50. The solid mixtures, formed in green state compacts, were sintered at the temperature range of 800o C up to 1200o C. The resulting products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDXS) and micro-indentation. The above methods were employed to characterize the various phases, microstructure and hardness of the produced materials. Thermal treatment at 800o C and 1000o C produced opaque ceramic products composed of a variety of chromium-containing and chromium-free crystalline phases. Thermal treatment at 1200o C gave rise to composite products, where only chromium-containing crystalline phases were detected. Hardness results suggest that specific products are serious candidates for structural applications.
Abstract: Dental porcelain composites reinforced and toughened
by 20 wt.% tetragonal zirconia (3Y-TZP) were processed by hot
pressing at 1000°C. Two types of particles were tested: yttriastabilized
zirconia (ZrO2–3%Y2O3) agglomerates and pre-sintered
yttria-stabilized zirconia (ZrO2–3%Y2O3) particles. The composites
as well as the reinforcing particles were analyzed by the means of
optical and Scanning Electron Microscopy (SEM), Energy Dispersion
Spectroscopy (EDS) and X-Ray Diffraction (XRD). The mechanical
properties were obtained by the transverse rupture strength test. Wear
tests were also performed on the composites and monolithic
porcelain. The best mechanical results were displayed by the
porcelain reinforced with the pre-sintered ZrO2–3%Y2O3
agglomerates.
Abstract: In this study, polycaprolactone (PCL) was dissolved
in chloroform:ethanol solvent system at a concentration of 18 w/v %.
1, 2, 4, and 6 droplets of formic acid were added to the prepared 10ml
PCL-chloroform:ethanol solutions separately. Fibrous webs were
produced by electrospinning technique based on the horizontal
working principle. Morphology of the webs was investigated by
using scanning electron microscopy (SEM) whereas fiber diameters
were measured by Image J Software System. The effect of formic
acid addition to the mostly used chloroform solvent on fiber
morphology was examined.
Results indicate that there is a distinct fall in fiber diameter with
the addition of formic acid drops. The average fiber diameter was
measured as 2.22μm in PCL /chloroform:ethanol solution system. On
the other hand, 328nm and 256 nm average fiber diameters were
measured for the samples of 4 drops and 6 drops formic acid added.
This study offers alternative solvent systems to produce nanoscaled,
nontoxic PCL fibrous webs by electrospinning technique.
Abstract: Morphological interaction of porcine cumulus-oocyte
complexes (pCOCs) was investigated on in vitro condition using
electron microscope (SEM and TEM). The totals of 1,923 oocytes
were round in shape, surrounded by Zona pellucida with layer of
cumulus cells ranging between 59.29-202.14 μm in size. They were
classified into intact-, multi-, partial cumulus cell layer oocyte, and
completely denuded oocyte, at the percentage composition of 22.80%
32.70%, 18.60%, and 25.90 % respectively. The pCOCs classified as
intact- and multi cumulus cell layer oocytes were further culturing at
37°C with 5% CO2, 95% air atmosphere and high humidity for 44 h
in M199 with Earle’s salts supplemented with 10% HTFCS, 2.2
mg/mL NaHCO3, 1 M Hepes, 0.25 mM pyruvate, 15 μg/mL porcine
follicle-stimulating hormone, 1 μg/mL LH, 1μg/mL estradiol with
ethanol, and 50 μg/mL gentamycin sulfate. On electron microscope
study, cumulus cells were found to stick their processes to secrete
substance from the sac-shape end into Zona pellucida of the oocyte
and also communicated with the neighboring cells through their
microvilli on the beginning of incubation period. It is believed that
the cumulus cells communicate with the oocyte by inserting the
microvilli through this gap and embedded in the oocyte cytoplasm
before secreting substance, through the sac-shape end of the
microvilli, to inhibit primary oocyte development at the prophase I.
Morphological changes of the complexes were observed after
culturing for 24-44 h. One hundred percentages of the cumulus layers
were expanded and cumulus cells were peeling off from the oocyte
surface. In addition, the round-shape cumulus cells transformed
themselves into either an elongate shape or a columnar shape, and no
communication between cumulus neighboring cells. After 44 h of
incubation time, diameter of oocytes surrounded by cumulus cells
was larger than 0 h incubation. The effect of hormones in culture
medium is exerted by their receptors present in porcine oocyte. It is
likely that all morphological changes of the complexes after hormone
treatment were to allow maturation of the oocyte. This study
demonstrated that the association of hormones in M199 could
promote porcine follicle activation in 44 h in vitro condition. This
culture system should be useful for studying the regulation of early
follicular growth and development, especially because these follicles represent a large source of oocytes that could be used in vitro for cell
technology.
Abstract: Over the past four decades, the fatigue behavior of
nickel-based alloys has been widely studied. However, in recent
years, significant advances in the fabrication process leading to grain
size reduction have been made in order to improve fatigue properties
of aircraft turbine discs. Indeed, a change in particle size affects the
initiation mode of fatigue cracks as well as the fatigue life of the
material. The present study aims to investigate the fatigue behavior of
a newly developed nickel-based superalloy under biaxial-planar
loading. Low Cycle Fatigue (LCF) tests are performed at different
stress ratios so as to study the influence of the multiaxial stress state
on the fatigue life of the material. Full-field displacement and strain
measurements as well as crack initiation detection are obtained using
Digital Image Correlation (DIC) techniques. The aim of this
presentation is first to provide an in-depth description of both the
experimental set-up and protocol: the multiaxial testing machine, the
specific design of the cruciform specimen and performances of the
DIC code are introduced. Second, results for sixteen specimens
related to different load ratios are presented. Crack detection, strain
amplitude and number of cycles to crack initiation vs. triaxial stress
ratio for each loading case are given. Third, from fractographic
investigations by scanning electron microscopy it is found that the
mechanism of fatigue crack initiation does not depend on the triaxial
stress ratio and that most fatigue cracks initiate from subsurface
carbides.
Abstract: Poly vinyl acetate (PVA)-based titania (TiO2)–carbon
nanotube composite nanofibers (PVA-TCCNs) with various
PVA-to-solvent ratios and PVA-based TiO2 composite nanofibers
(PVA-TN) were synthesized using an electrospinning process,
followed by thermal treatment. The photocatalytic activities of these
nanofibers in the degradation of airborne monocyclic aromatics under
visible-light irradiation were examined. This study focuses on the
application of these photocatalysts to the degradation of the target
compounds at sub-part-per-million indoor air concentrations. The
characteristics of the photocatalysts were examined using scanning
electron microscopy, X-ray diffraction, ultraviolet-visible
spectroscopy, and Fourier-transform infrared spectroscopy. For all the
target compounds, the PVA-TCCNs showed photocatalytic
degradation efficiencies superior to those of the reference PVA-TN.
Specifically, the average photocatalytic degradation efficiencies for
benzene, toluene, ethyl benzene, and o-xylene (BTEX) obtained using
the PVA-TCCNs with a PVA-to-solvent ratio of 0.3 (PVA-TCCN-0.3)
were 11%, 59%, 89%, and 92%, respectively, whereas those observed
using PVA-TNs were 5%, 9%, 28%, and 32%, respectively.
PVA-TCCN-0.3 displayed the highest photocatalytic degradation
efficiency for BTEX, suggesting the presence of an optimal
PVA-to-solvent ratio for the synthesis of PVA-TCCNs. The average
photocatalytic efficiencies for BTEX decreased from 11% to 4%, 59%
to 18%, 89% to 37%, and 92% to 53%, respectively, when the flow
rate was increased from 1.0 to 4.0 L min1. In addition, the average
photocatalytic efficiencies for BTEX increased 11% to ~0%, 59% to
3%, 89% to 7%, and 92% to 13%, respectively, when the input
concentration increased from 0.1 to 1.0 ppm. The prepared
PVA-TCCNs were effective for the purification of airborne aromatics
at indoor concentration levels, particularly when the operating
conditions were optimized.
Abstract: In this research (using induction furnace process)
nodular iron with three different percentages of copper (residual,
0.5% and 1,2%) was obtained. Chemical analysis was performed by
mass spectrometry and microstructures were characterized by Optical
Microscopy (ASTM E3) and Scanning Electron Microscopy (SEM).
The study of mechanical behavior was carried out in a mechanical
test machine (ASTM E8) and a Pin on disk tribometer (ASTM G99)
was used to assess wear resistance. It is observed that the dissolution
of copper in crystal lattice increases the pearlite structure improving
the wear and hardness behavior, but producing a contrary effect on
the energy absorption.
Abstract: Thin ZnO films are deposited on glass substrates via
sol–gel method and dip-coating. The films are prepared from zinc
acetate dehydrate as a starting reagent. After that the as-prepared
ZnO sol is aged for different periods (0, 1, 3, 5, 10, 15 and 30 days).
Nanocrystalline thin films are deposited from various sols. The
effect ZnO sols aging time on the structural and photocatalytic
properties of the films is studied. The films surface is studied by
Scanning Electron Microscopy. The effect of the aging time of the
starting solution is studied in the photocatalytic degradation of
Reactive Black 5 (RB5) by UV-vis spectroscopy. The experiments
are conducted upon UV-light illumination and in complete darkness.
The variation of the absorption spectra shows the degradation of RB5
dissolved in water, as a result of the reaction, occurring on the surface
of the films and promoted by UV irradiation. The initial
concentrations of dye (5, 10 and 20 ppm) and the effect of the aging
time are varied during the experiments. The results show, that the
increasing aging time of starting solution with respect to ZnO
generally promotes photocatalytic activity. The thin films obtained
from ZnO sol, which is aged 30 days have best photocatalytic
degradation of the dye (97,22%) in comparison with the freshly
prepared ones (65,92%). The samples and photocatalytic
experimental results are reproducible. Nevertheless, all films exhibit
a substantial activity in both UV light and darkness, which is
promising for the development of new ZnO photocatalysts by sol-gel
method.
Abstract: Bio-composites derived from plant fiber and/or bioderived
polymer, are likely more ecofriendly and demonstrate
competitive performance with petroleum based composites. In this
research, the bio phenol-formaldehyde (bio-PF) was used as a matrix
and oil palm empty fruit bunch fiber (EFB) as reinforcement. The
matrix was synthesized via liquefaction and condensation to enhance
the combination of phenol and formaldehyde, during the process.
Then, the bio-PF was mixed with different percentage of EFB (5%,
10%, 15% and 20%) and molded at 180oC. The samples that viewed
under scanning electron microscopy (SEM) showed an excellent
wettability and interaction between EFB and matrix. Samples of 10%
EFB gave the optimum properties of impact and hardness meanwhile
sample 15% of EFB gave the highest reading of flexural modulus
(MOE) and flexural strength (MOR). For thermal stability analysis, it
was found that the weight loss and the activation energy (Ea) of the
bio-composites samples were decreased as the filler content
increased.