Abstract: The synthesis of CuFe2O4 spinel powders by an
optimized combustion-like process followed by calcination is
described herein. The samples were characterized using X-ray
diffraction (XRD), differential thermal analysis (TG/DTA), scanning
electron microscopy (SEM), dilatometry and 4-probe DC methods.
Different glycine to nitrate (G/N) ratios of 1 (fuel-deficient), 1.48
(stoichiometric) and 2 (fuel-rich) were employed. Calcining the asprepared
powders at 800 and 1000°C for 5 hours showed that the G/N
ratio of 2 results in the formation of the desired copper spinel single
phase at both calcination temperatures. For G/N=1, formation of
CuFe2O4 takes place in three steps. First, iron and copper nitrates
decompose to iron oxide and pure copper. Then, copper transforms to
copper oxide and finally, copper and iron oxides react with each other
to form a copper ferrite spinel phase. The electrical conductivity and
the coefficient of thermal expansion of the sintered pelletized
samples were 2 S.cm-1 (800°C) and 11×10-6 °C-1 (25-800°C),
respectively.
Abstract: A new conserving approach in the context of Immersed Boundary Method (IBM) is presented to simulate one dimensional, incompressible flow in a moving boundary problem. The method employs control volume scheme to simulate the flow field. The concept of ghost node is used at the boundaries to conserve the mass and momentum equations. The Present method implements the conservation laws in all cells including boundary control volumes. Application of the method is studied in a test case with moving boundary. Comparison between the results of this new method and a sharp interface (Image Point Method) IBM algorithm shows a well distinguished improvement in both pressure and velocity fields of the present method. Fluctuations in pressure field are fully resolved in this proposed method. This approach expands the IBM capability to simulate flow field for variety of problems by implementing conservation laws in a fully Cartesian grid compared to other conserving methods.