Abstract: Poly vinyl acetate (PVA)-based titania (TiO2)–carbon
nanotube composite nanofibers (PVA-TCCNs) with various
PVA-to-solvent ratios and PVA-based TiO2 composite nanofibers
(PVA-TN) were synthesized using an electrospinning process,
followed by thermal treatment. The photocatalytic activities of these
nanofibers in the degradation of airborne monocyclic aromatics under
visible-light irradiation were examined. This study focuses on the
application of these photocatalysts to the degradation of the target
compounds at sub-part-per-million indoor air concentrations. The
characteristics of the photocatalysts were examined using scanning
electron microscopy, X-ray diffraction, ultraviolet-visible
spectroscopy, and Fourier-transform infrared spectroscopy. For all the
target compounds, the PVA-TCCNs showed photocatalytic
degradation efficiencies superior to those of the reference PVA-TN.
Specifically, the average photocatalytic degradation efficiencies for
benzene, toluene, ethyl benzene, and o-xylene (BTEX) obtained using
the PVA-TCCNs with a PVA-to-solvent ratio of 0.3 (PVA-TCCN-0.3)
were 11%, 59%, 89%, and 92%, respectively, whereas those observed
using PVA-TNs were 5%, 9%, 28%, and 32%, respectively.
PVA-TCCN-0.3 displayed the highest photocatalytic degradation
efficiency for BTEX, suggesting the presence of an optimal
PVA-to-solvent ratio for the synthesis of PVA-TCCNs. The average
photocatalytic efficiencies for BTEX decreased from 11% to 4%, 59%
to 18%, 89% to 37%, and 92% to 53%, respectively, when the flow
rate was increased from 1.0 to 4.0 L min1. In addition, the average
photocatalytic efficiencies for BTEX increased 11% to ~0%, 59% to
3%, 89% to 7%, and 92% to 13%, respectively, when the input
concentration increased from 0.1 to 1.0 ppm. The prepared
PVA-TCCNs were effective for the purification of airborne aromatics
at indoor concentration levels, particularly when the operating
conditions were optimized.