Abstract: A controlled cutting fluid impinging supply system (CUT-LIST) was developed to deliver an accurate amount of cutting fluid into the machining zone via well-positioned coherent nozzles based on a calculation of the heat generated. The performance of the CUT-LIST was evaluated against a conventional flood cutting fluid supply system during step shoulder milling of Ti-6Al-4V using vegetable oil-based cutting fluid. In this paper, the micro-hardness of the machined surface was used as the main criterion to compare the two systems. CUT-LIST provided significant reductions in cutting fluid consumption (up to 42%). Both systems caused increased micro-hardness value at 100 µm from the machined surface, whereas a slight reduction in micro-hardness of 4.5% was measured when using CUL-LIST. It was noted that the first 50 µm is the soft sub-surface promoted by thermal softening, whereas down to 100 µm is the hard sub-surface caused by the cyclic internal work hardening and then gradually decreased until it reached the base material nominal hardness. It can be concluded that the CUT-LIST has always given lower micro-hardness values near the machined surfaces in all conditions investigated.
Abstract: This study aimed to investigate the effect of aggressive environment on the flexural properties of halloysite nanotubes-polyester nanocomposites. Results showed that the addition of halloysite nanotubes into polyester matrix was found to improve flexural properties of the nanocomposites in dry condition and after water-methanol exposure. Significant increase in surface roughness was also observed and measured by Alicona Infinite Focus optical microscope.
Abstract: Graphene was dispersed using a tip sonicator and the
effect of surfactants were analysed. Sodium Dodecyl Sulphate (SDS)
and Polyvinyl Alcohol (PVA) were compared to observe whether or
not they had any effect on any de-wrinkling, and secondly whether
they aided to achieve better dispersions. There is a huge demand for
wrinkle free graphene as this will greatly increase its usefulness in
various engineering applications. A comprehensive literature on dewrinkling
graphene has been discussed. Low magnification Scanning
Electronic Microscopy (SEM) was conducted to assess the quality of
graphene de-wrinkling. The utilization of the PVA has significant
effect on de-wrinkling whereas SDS had minimal effect on the dewrinkling
of graphene.