Multiaxial Fatigue Analysis of a High Performance Nickel-Based Superalloy

Over the past four decades, the fatigue behavior of
nickel-based alloys has been widely studied. However, in recent
years, significant advances in the fabrication process leading to grain
size reduction have been made in order to improve fatigue properties
of aircraft turbine discs. Indeed, a change in particle size affects the
initiation mode of fatigue cracks as well as the fatigue life of the
material. The present study aims to investigate the fatigue behavior of
a newly developed nickel-based superalloy under biaxial-planar
loading. Low Cycle Fatigue (LCF) tests are performed at different
stress ratios so as to study the influence of the multiaxial stress state
on the fatigue life of the material. Full-field displacement and strain
measurements as well as crack initiation detection are obtained using
Digital Image Correlation (DIC) techniques. The aim of this
presentation is first to provide an in-depth description of both the
experimental set-up and protocol: the multiaxial testing machine, the
specific design of the cruciform specimen and performances of the
DIC code are introduced. Second, results for sixteen specimens
related to different load ratios are presented. Crack detection, strain
amplitude and number of cycles to crack initiation vs. triaxial stress
ratio for each loading case are given. Third, from fractographic
investigations by scanning electron microscopy it is found that the
mechanism of fatigue crack initiation does not depend on the triaxial
stress ratio and that most fatigue cracks initiate from subsurface
carbides.





References:
[1] D. Fournier, A. Pineau, “Low cycle fatigue behavior of Inconel 718 at
298K and 823K”, Metallurgical Transactions A, vol. 8A, pp. 1095-1105,
1977.
[2] F. Alexandre, S. Deyber, A. Pineau, “Modelling the optimum grain size
on the low cycle fatigue life of a Ni based superalloy in the presence of
two possible crack initiation sites”, Scripta Materialia, vol. 50, pp. 25-
30, 2004.
[3] X.F. Ma, Z. Duan, H.J. Shi, R. Murai, E. Yanagisawa, “Fatigue and
fracture behavior of nickel-based superalloy Inconel 718 up to the very
high cycle regime”, Journal of Zhejiang Univ-Sci – Applied Physics &
Engineering, vol. 10, pp. 727-737, 2010.
[4] V. Zerrouki, “Inconel 718 et tenue en fatigue oligocyclique. Influence de
la microstructure et prédiction de la durée de vie”, Mémoire de DRT
Génie des Matériaux, Université EVE, 2000.
[5] Y. Ohtake, S. Rokugawa, H. Masumoto, “Geometry determination of
cruciform type specimen and biaxial tensile test of C/C composites”,
Key Eng. Mater., vol. 3, pp. 151-154, 1999.
[6] S.B. Lin, J.L. Ding, H.M. Zbib, “Characterization of yield surfaces using
balanced biaxial tests of cruciform plate specimens”, Scripta Metall.
Mater., vol. 28, pp. 617-622, 1993.
[7] J.S. Welsh, D.F. Adams, “An experimental investigation of the biaxial
strength of IM6/3501-6 carbon /epoxy cross-ply laminates using
cruciform specimens”, Composites: Part A 33, vol. 6, pp. 829-839, 2002.
[8] M. Poncelet, G. Barbier, B. Raka, S. Courtin, R. Desmorat, J.C. Le-
Roux, L. Vincent, “Biaxial high cycle fatigue of a type 304L stainless
steel: cyclic strains end crack initiation detection by digital image
correlation”, European Journal of Mechanics / A Solids, vol. 5, 2010.
[9] P. Terriault, K. Settouane, V. Brailovski, “Biaxial testing at different
temperatures of cruciform Ti-Ni samples. In: Shape Memory and
Superelastic Technologies”, California, 2003.
[10] A. Makinde, L. Thibodeau, K.W. Neale, “Development of an apparatus
for biaxial testing for cruciform specimens”, Experimental mechanics,
vol. 32, pp. 132-137, 1992.
[11] A. Scholz, C. Berger, A. Samir, R. Bardenheier, “Biaxiale TMFSimulation
mit Kreuzproben zur Untersuchung des
Kriechermüdungsverhaltens von hochtemperaturewerkstoffen.
Weinheim”, Wiley, pp. 280-285, 2007.
[12] Abaqus Analysis User’s Manual v6.10.
[13] Aramis software. Gom Optical Measuring Techniques.
http://www.gom.com/EN/index.html, 2006.
[14] S.P. Lynch, “Progression markings, striations, and crack-arrest markings
on fracture surfaces”, Materials Sciences and Engineering A, 468-470,
pp. 74-80, 2007.