Abstract: Zinc borate is an important inorganic hydrate borate
material, which can be used as a flame retardant agent and corrosion
resistance material. This compound can loss its structural water
content at higher than 290°C. Due to thermal stability; Zinc Borate
can be used as flame retardant at high temperature process of plastic
and gum. In this study, the ultrasonic reaction of zinc borates were
studied using hydrozincite (Zn5(CO3)2·(OH)6) and boric acid
(H3BO3) raw materials. Before the synthesis raw materials were
characterized by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). Ultrasonic method is a new
application on the zinc borate synthesis. The synthesis parameters
were set to 90°C reaction temperature and 55 minutes of reaction
time, with 1:1, 1:2, 1:3, 1:4 and 1:5 molar ratio of starting materials
(Zn5(CO3)2·(OH)6 : H3BO3). After the zinc borate synthesis, the
products were analyzed by XRD and FT-IR. As a result, optimum
molar ratio of 1:5 is determined for the synthesis of zinc borates with
ultrasonic method.
Abstract: The effect of carbon nanofibers (CNFs) on the
electrical properties of Poly(vinylidene fluoride-hexafluoropropylene)
(P(VdF-HFP)) based gel polymer electrolytes has been investigated
in the present work. The length and diameter ranges of CNFs used in
the present work are 5-50 μm and 200-600 nm respectively. The
nanocomposite gel polymer electrolytes have been synthesized by
solution casting technique with varying CNFs content in terms of
weight percentage. Electrochemical impedance analysis demonstrates
that the reinforcement of carbon nanofibers significantly enhances the
ionic conductivity of the polymer electrolyte. The decrease of
crystallinity of P(VdF-HFP) due the addition of CNFs has been
confirmed by X-ray diffraction (XRD). The interaction of CNFs with
various constituents of nanocomposite gel polymer electrolytes has
been assessed by Fourier Transform Infrared (FTIR) spectroscopy.
Moreover CNFs added gel polymer electrolytes offer superior
thermal stability as compared to that of CNFs free electrolytes as
confirmed by Thermogravimetric analysis (TGA).
Abstract: A novel chromium-free protective coating films based
on a zeolite coating was growing onto a FeCrAlloy metal using in –
situ hydrothermal method. The zeolite film was obtained using in-situ
crystallization process that is capable of coating large surfaces with
complex shape and in confined spaces has been developed. The
zeolite coating offers an advantage of a high mechanical stability and
thermal stability. The physicochemical properties were investigated
using X-ray diffraction (XRD), Electron Microscopy (SEM), Energy
Dispersive X–ray Analysis (EDX) and Thermogravimetric Analysis
(TGA). The transition from oxide-on-alloy wires to hydrothermally
synthesised uniformly zeolite coated surfaces was followed using
SEM and XRD. In addition, the robustness of the prepared coating
was confirmed by subjecting these to thermal cycling (ambient to
550oC).
Abstract: Catalytic combustion of methane is imperative due to
stability of methane at low temperature. Methane (CH4), therefore,
remains unconverted in vehicle exhausts thereby causing greenhouse
gas GHG emission problem. In this study, heterogeneous catalysts of
palladium with bio-char (2 wt% Pd/Bc) and Al2O3 (2wt% Pd/ Al2O3)
supports were prepared by incipient wetness impregnation and then
subsequently tested for catalytic combustion of CH4. Support-porous
heterogeneous catalytic combustion (HCC) material were selected
based on factors such as surface area, porosity, thermal stability,
thermal conductivity, reactivity with reactants or products, chemical
stability, catalytic activity, and catalyst life. Sustainable and
renewable support-material of bio-mass char derived from palm shell
waste material was compared with those from the conventional
support-porous materials. Kinetic rate of reaction was determined for
combustion of methane on Palladium (Pd) based catalyst with Al2O3
support and bio-char (Bc). Material characterization was done using
TGA, SEM, and BET surface area. The performance test was
accomplished using tubular quartz reactor with gas mixture ratio of
3% methane and 97% air. The methane porous-HCC conversion was
carried out using online gas analyzer connected to the reactor that
performed porous-HCC. BET surface area for prepared 2 wt% Pd/Bc
is smaller than prepared 2wt% Pd/ Al2O3 due to its low porosity
between particles. The order of catalyst activity based on kinetic rate
on reaction of catalysts in low temperature was 2wt%
Pd/Bc>calcined 2wt% Pd/ Al2O3> 2wt% Pd/ Al2O3>calcined 2wt%
Pd/Bc. Hence agro waste material can successfully be utilized as an
inexpensive catalyst support material for enhanced CH4 catalytic
combustion.
Abstract: Bio-composites derived from plant fiber and/or bioderived
polymer, are likely more ecofriendly and demonstrate
competitive performance with petroleum based composites. In this
research, the bio phenol-formaldehyde (bio-PF) was used as a matrix
and oil palm empty fruit bunch fiber (EFB) as reinforcement. The
matrix was synthesized via liquefaction and condensation to enhance
the combination of phenol and formaldehyde, during the process.
Then, the bio-PF was mixed with different percentage of EFB (5%,
10%, 15% and 20%) and molded at 180oC. The samples that viewed
under scanning electron microscopy (SEM) showed an excellent
wettability and interaction between EFB and matrix. Samples of 10%
EFB gave the optimum properties of impact and hardness meanwhile
sample 15% of EFB gave the highest reading of flexural modulus
(MOE) and flexural strength (MOR). For thermal stability analysis, it
was found that the weight loss and the activation energy (Ea) of the
bio-composites samples were decreased as the filler content
increased.
Abstract: The current study investigated the influence of milling
time and ball-to-powder (BPR) weight ratio on the microstructural
constituents and mechanical properties of bulk nanocrystalline Al;
Al-10%Cu; and Al-10%Cu-5%Ti alloys. Powder consolidation was
carried out using a high frequency induction heat sintering where the
processed metal powders were sintered into a dense and strong bulk
material. The powders and the bulk samples were characterized using
XRD and FEGSEM techniques. The mechanical properties were
evaluated at various temperatures of 25°C, 100°C, 200°C, 300°C and
400°C to study the thermal stability of the processed alloys. The
processed bulk nanocrystalline alloys displayed extremely high
hardness values even at elevated temperatures. The Al-10%Cu-5%Ti
alloy displayed the highest hardness values at room and elevated
temperatures which are related to the presence of Ti-containing
phases such as Al3Ti and AlCu2Ti. These phases are thermally stable
and retain the high hardness values at elevated temperatures up to
400ºC.
Abstract: Particles are the most common and cheapest
reinforcement producing discontinuous reinforced composites with
isotropic properties. Conventional fabrication methods can be used to
produce a wide range of product forms, making them relatively
inexpensive. Optimising composite development must include
consideration of all the fundamental aspect of particles including
their size, shape, volume fraction, distribution and mechanical
properties. Research has shown that the challenges of low fracture
toughness, poor crack growth resistance and low thermal stability can
be overcome by reinforcement with particles. The unique properties
exhibited by micro particles reinforced ceramic composites have
made them to be highly attractive in a vast array of applications.
Abstract: In this study, the evaluation of thermal stability of the
micrometer-sized silica particle reinforced epoxy composite was
carried out through the measurement of thermal expansion coefficient
and Young’s modulus of the specimens. For all the specimens in this
study from the baseline to those containing 50 wt% silica filler, the
thermal expansion coefficients and the Young’s moduli were
gradually decreased down to 20% and increased up to 41%,
respectively. The experimental results were compared with fillervolume-
based simple empirical relations. The experimental results of
thermal expansion coefficients correspond with those of Thomas’s
model which is modified from the rule of mixture. However, the
measured result for Young’s modulus tends to be increased slightly.
The differences in increments of the moduli between experimental and
numerical model data are quite large.
Abstract: A novel new vanadium (IV) complexes incorporating the chelating diamido cyclopentadienyl {ArN(CH2)3NAr)}2-((ηn-Cp)Cp)} (Ar = 2,6-Pri2C6H3)(Cp = C5H5 and n = 1,2,3,4 and 5) have been studied with calculation of the properties of species involved in various of cyclopentadienyl reaction. These were carried out under investigation of density functional theory (DFT) calculation, and comparing together. Other methods, explicitly including electron correlation, are necessary for more accurate calculations; MB3LYP (Becke) (Lee–Yang–Parr) level of theory often being used to obtain more exact results. These complexes were estimated of electronic energy for molecular system, because it accounts for all electron correlation interactions.
The optimised of [V(ArN(CH2)3NAr)2Cl(η5-Cp)] (Ar = 2,6-Pri2C6H3 and Cp= C5H5) was found to be thermally more stable than others of vanadium cyclopentadienyl. In the meantime the complex [V(ArN(CH2)3NAr)2Cl(η1-Cp)] (Ar = 2,6-Pri2C6H3 and Cp= C5H5) which is showed a low thermal stability in case of the just one carbon of cyclopentadienyl can be insertion with vanadium metal centre. By using Dewar-Chatt-Duncanson model, as a basis of the molecular orbital (MO) analysis and showed the highest occupied molecular orbital (HOMO) and lowest occupied molecular orbital LUMO.
Abstract: Collagen was isolated from chicken feet by using papain and pepsin enzymes in acetic acid solution at 4°C for 24h with a yield of 18.16% and 22.94% by dry weight, respectively. Chemical composition and characteristics of chicken feet collagen such as amino acid composition, SDS-PAGE patterns, FTIR spectra and thermal properties were evaluated. The chicken feet collagen is rich in the amino acids glycine, glutamic acid, proline and hydroxyproline. Electrophoresis pattern demonstrated two distinct α-chains (α1 and α2) and β chain, indicating that type I collagen is a major component of chicken feet collagen. The thermal stability of collagen isolated by papain and pepsin revealed stable denaturation temperatures of 48.40 and 53.35°C, respectively. The FTIR spectra of both collagens were similar with amide regions in A, B, I, II and III. The study demonstrated that chicken feet collagen using papain isolation method is possible as commercial alternative ingredient.
Abstract: In this experiment Polystyrene/Zinc-oxide (PS/ZnO) nanocomposite fibers were produced by electrospinning technique using limonene as a green solvent. First, the morphology of electrospun pure polystyrene (PS) and PS/ZnO nanocomposite fibers investigated by SEM. Results showed the PS fiber diameter decreased by increasing concentration of Zinc Oxide nanoparticles (ZnO NPs). Thermo Gravimetric Analysis (TGA) results showed thermal stability of nanocomposites increased by increasing ZnO NPs in PS electrospun fibers. Considering Differential Scanning Calorimeter (DSC) thermograms for electrospun PS fibers indicated that introduction of ZnO NPs into fibers affects the glass transition temperature (Tg) by reducing it. Also, UV protection properties of nanocomposite fibers were increased by increasing ZnO concentration. Evaluating the effect of metal oxide NPs amount on mechanical properties of electrospun layer showed that tensile strength and elasticity modulus of the electrospun layer of PS increased by addition of ZnO NPs. X-ray diffraction (XRD) pattern of nanopcomposite fibers confirmed the presence of NPs in the samples.
Abstract: This study explains the influence of secondary filler on the dispersion of carbon nanotube (CNT) reinforced high density polyethylene (HDPE) nanocomposites (CNT/HDPE). In order to understand the mixed-fillers system, Montmorillonite (MMT) was added to CNT/HDPE nanocomposites. It was followed by investigating their effect on the thermal, mechanical and morphological properties of the aforesaid nanocomposite. Incorporation of 3 wt% each of MMT into CNT/HDPE nanocomposite resulted to the increased values for the tensile and flexural strength, as compared to the pure HDPE matrix. The thermal analysis result showed improved thermal stability of the formulated nanocomposites. Transmission electron microscopy (TEM) images revealed that larger aggregates of CNTs were disappeared upon addition of these two components leading to the enhancement of thermo-mechanical properties for such composites.
Abstract: A vertical SOI-based MOSFET with trench body
structure operated as 1T DRAM cell at various temperatures has been
studied and investigated. Different operation temperatures are
assigned for the device for its performance comparison, thus the
thermal stability is carefully evaluated for the future memory device
applications. Based on the simulation, the vertical SOI-based
MOSFET with trench body structure demonstrates the electrical
characteristics properly and possess conspicuous kink effect at
various operation temperatures. Transient characteristics were also
performed to prove that its programming window values and
retention time behaviors are acceptable when the new 1T DRAM cell
is operated at high operation temperature.
Abstract: Carbon fibers have specific characteristics in
comparison with industrial and structural materials used in different
applications. Special properties of carbon fibers make them attractive
for reinforcing and fabrication of composites. These fibers have been
utilized for composites of metals, ceramics and plastics. However,
it-s mainly used in different forms to reinforce lightweight polymer
materials such as epoxy resin, polyesters or polyamides. The
composites of carbon fiber are stronger than steel, stiffer than
titanium, and lighter than aluminum and nowadays they are used in a
variety of applications. This study explains applications of carbon
fibers in different fields such as space, aviation, transportation,
medical, construction, energy, sporting goods, electronics, and the
other commercial/industrial applications. The last findings of
composites with polymer, metal and ceramic matrices containing
carbon fibers and their applications in the world investigated.
Researches show that carbon fibers-reinforced composites due to
unique properties (including high specific strength and specific
modulus, low thermal expansion coefficient, high fatigue strength,
and high thermal stability) can be replaced with common industrial
and structural materials.
Abstract: In this study, it is investigated the stability boundary of
Functionally Graded (FG) panel under the heats and supersonic
airflows. Material properties are assumed to be temperature
dependent, and a simple power law distribution is taken. First-order
shear deformation theory (FSDT) of plate is applied to model the
panel, and the von-Karman strain- displacement relations are
adopted to consider the geometric nonlinearity due to large
deformation. Further, the first-order piston theory is used to model the
supersonic aerodynamic load acting on a panel and Rayleigh damping
coefficient is used to present the structural damping. In order to find a
critical value of the speed, linear flutter analysis of FG panels is
performed. Numerical results are compared with the previous works,
and present results for the temperature dependent material are
discussed in detail for stability boundary of the panel with various
volume fractions, and aerodynamic pressures.
Abstract: In this study, we sought to investigate the mercury
removal efficiency of manganese oxides from natural gas. The
fundamental studies on mercury removal with manganese oxides
sorbents were carried out in a laboratory scale fixed bed reactor at 30
°C with a mixture of methane (20%) and nitrogen gas laden with 4.8
ppb of elemental mercury. Manganese oxides with varying surface
area and crystalline phase were prepared by conventional precipitation
method in this study. The effects of surface area, crystallinity and
other metal oxides on mercury removal efficiency were investigated.
Effect of Ag impregnation on mercury removal efficiency was also
investigated. Ag supported on metal oxide such titania and zirconia as
reference materials were also used in this study for comparison. The
characteristics of mercury removal reaction with manganese oxide
was investigated using a temperature programmed desorption (TPD)
technique.
Manganese oxides showed very high Hg removal activity (about
73-93% Hg removal) for first time use. Surface area of the manganese
oxide samples decreased after heat-treatment and resulted in complete
loss of Hg removal ability for repeated use after Hg desorption in the
case of amorphous MnO2, and 75% loss of the initial Hg removal
activity for the crystalline MnO2. Mercury desorption efficiency of
crystalline MnO2 was very low (37%) for first time use and high (98%)
after second time use. Residual potassium content in MnO2 may have
some effect on the thermal stability of the adsorbed Hg species.
Desorption of Hg from manganese oxides occurs at much higher
temperatures (with a peak at 400 °C) than Ag/TiO2 or Ag/ZrO2.
Mercury may be captured on manganese oxides in the form of mercury
manganese oxide.
Abstract: Platinum oxide nanoparticles were prepared by a
simple hydrothermal route and chemical reduction using
carbohydrates (Fructose and sucrose) as the reducing and
stabilizing agents. The crystallite size of these nanoparticles was
evaluated from X-ray diffraction (XRD), atomic force microscopy
(AFM) and transmission electron microscopy (TEM) and was
found to be 10 nm as shown in figure 1, which is the
demonstration of EM bright field and transmission electron
microscopy. The effect of carbohydrates on the morphology of the
nanoparticles was studied using TEM (Figure 1). The
nanoparticles (100 μg/ml) were administered to the Pseudomonas
Stutzeri and Lactobacillus cultures and the incubation was done at
35 oC for 24 hours. The nanocomposites exhibited interesting
inhibitory as well as bactericidal activity against P. Stutzeri and
and Lactobacillus species. Incorporation of nanoparticles also
increased the thermal stability of the carbohydrates.
Abstract: In the present study, the incorporation of graphene
into blends of acrylonitrile-butadiene-styrene terpolymer with
polypropylene (ABS/PP) was investigated focusing on the
improvement of their thermomechanical characteristics and the effect
on their rheological behavior. The blends were prepared by melt
mixing in a twin-screw extruder and were characterized by measuring
the MFI as well as by performing DSC, TGA and mechanical tests.
The addition of graphene to ABS/PP blends tends to increase their
melt viscosity, due to the confinement of polymer chains motion.
Also, graphene causes an increment of the crystallization temperature
(Tc), especially in blends with higher PP content, because of the
reduction of surface energy of PP nucleation, which is a consequence
of the attachment of PP chains to the surface of graphene through the
intermolecular CH-π interaction. Moreover, the above nanofiller
improves the thermal stability of PP and increases the residue of
thermal degradation at all the investigated compositions of blends,
due to the thermal isolation effect and the mass transport barrier
effect. Regarding the mechanical properties, the addition of graphene
improves the elastic modulus, because of its intrinsic mechanical
characteristics and its rigidity, and this effect is particularly strong in
the case of pure PP.
Abstract: Extraction of laccase produced by L. polychrous in an
aqueous two-phase system, composed of polyethylene glycol and
phosphate salt at pH 7.0 and 250C was investigated. The effect of
PEG molecular weight, PEG concentration and phosphate
concentration was determined. Laccase preferentially partitioned to
the top phase. Good extraction of laccase to the top phase was
observed with PEG 4000. The optimum system was found in the
system containing 12% w/w PEG 4000 and 16% w/w phosphate salt
with KE of 88.3, purification factor of 3.0-fold and 99.1% yield.
Some properties of the enzyme such as thermal stability, effect of
heavy metal ions and kinetic constants were also presented in this
work. The thermal stability decreased sharply with high temperature
above 60 0C. The enzyme was inhibited by Cd2+, Pb2+, Zn2+ and
Cu2+. The Vmax and Km values of the enzyme were 74.70
μmol/min/ml and 9.066 mM respectively.
Abstract: In this research work, poly (acrylonitrile-butadienestyrene)/
polypropylene (ABS/PP) blends were processed by melt
compounding in a twin-screw extruder. Upgrading of the thermal
characteristics of the obtained materials was attempted by the
incorporation of organically modified montmorillonite (OMMT), as
well as, by the addition of two types of compatibilizers;
polypropylene grafted with maleic anhydride (PP-g-MAH) and ABS
grafted with maleic anhydride (ABS-g-MAH). The effect of the
above treatments was investigated separately and in combination.
Increasing the PP content in ABS matrix seems to increase the
thermal stability of their blend and the glass transition temperature
(Tg) of SAN phase of ABS. From the other part, the addition of ABS
to PP promotes the formation of its β-phase, which is maximum at 30
wt% ABS concentration, and increases the crystallization temperature
(Tc) of PP. In addition, it increases the crystallization rate of PP.The
β-phase of PP in ABS/PP blends is reduced by the addition of
compatibilizers or/and organoclay reinforcement. The incorporation
of compatibilizers increases the thermal stability of PP and reduces
its melting (ΔΗm) and crystallization (ΔΗc) enthalpies. Furthermore it
decreases slightly the Tgs of PP and SAN phases of ABS/PP blends.
Regarding the storage modulus of the ABS/PP blends, it presents a
change in their behavior at about 10°C and return to their initial
behavior at ~110°C. The incorporation of OMMT to no compatibilized
and compatibilized ABS/PP blends enhances their storage modulus.