Abstract: Lightweight and efficient structures have the aim to
enhance the efficiency of the components in various industries.
Toward this end, composites are one of the most widely used
materials because of durability, high strength and modulus, and low
weight. One type of the advanced composites is grid-stiffened
composite (GSC) structures, which have been extensively considered
in aerospace, automotive, and aircraft industries. They are one of the
top candidates for replacing some of the traditional components,
which are used here. Although there are a good number of published
surveys on the design aspects and fabrication of GSC structures, little
systematic work has been reported on their material modification to
improve their properties, to our knowledge. Matrix modification
using nanoparticles is an effective method to enhance the flexural
properties of the fibrous composites. In the present study, a silanecoupling
agent (3-glycidoxypropyltrimethoxysilane/3-GPTS) was
introduced onto the silica (SiO2) nanoparticle surface and its effects
on the three-point flexural response of isogrid E-glass/epoxy
composites were assessed. Based on the Fourier Transform Infrared
Spectrometer (FTIR) spectra, it was inferred that the 3-GPTS
coupling agent was successfully grafted onto the surface of SiO2
nanoparticles after modification. Flexural test revealed an
improvement of 16%, 14%, and 36% in stiffness, maximum load and
energy absorption of the isogrid specimen filled with 3 wt.% 3-
GPTS/SiO2 compared to the neat one. It would be worth mentioning
that in these structures, considerable energy absorption was observed
after the primary failure related to the load peak. In addition, 3-
GPTMS functionalization had a positive effect on the flexural
behavior of the multiscale isogrid composites. In conclusion, this
study suggests that the addition of modified silica nanoparticles is a
promising method to improve the flexural properties of the gridstiffened
fibrous composite structures.
Abstract: In this study, the evaluation of thermal stability of the
micrometer-sized silica particle reinforced epoxy composite was
carried out through the measurement of thermal expansion coefficient
and Young’s modulus of the specimens. For all the specimens in this
study from the baseline to those containing 50 wt% silica filler, the
thermal expansion coefficients and the Young’s moduli were
gradually decreased down to 20% and increased up to 41%,
respectively. The experimental results were compared with fillervolume-
based simple empirical relations. The experimental results of
thermal expansion coefficients correspond with those of Thomas’s
model which is modified from the rule of mixture. However, the
measured result for Young’s modulus tends to be increased slightly.
The differences in increments of the moduli between experimental and
numerical model data are quite large.
Abstract: Repairing of the cracks by fiber metal laminates
(FMLs) was first done by some aeronautical laboratories in early
1970s. In this study, experimental investigations were done on the
effect of repairing the center-cracked aluminum plates using the FML
patches. The repairing processes were conducted to characterize the
response of the repaired structures to tensile tests. The composite
patches were made of one aluminum layer and two woven glassepoxy
composite layers. Three different crack lengths in three crack
angles and different patch lay-ups were examined. It was observed
for the lengthen cracks, the effect of increasing the crack angle on
ultimate tensile load in the structure was increase. It was indicated
that the situation of metal layer in the FML patches had an important
effect on the tensile response of the tested specimens. It was found
when the aluminum layer is farther, the ultimate tensile load has the
highest amount.