Abstract: Particles are the most common and cheapest
reinforcement producing discontinuous reinforced composites with
isotropic properties. Conventional fabrication methods can be used to
produce a wide range of product forms, making them relatively
inexpensive. Optimising composite development must include
consideration of all the fundamental aspect of particles including
their size, shape, volume fraction, distribution and mechanical
properties. Research has shown that the challenges of low fracture
toughness, poor crack growth resistance and low thermal stability can
be overcome by reinforcement with particles. The unique properties
exhibited by micro particles reinforced ceramic composites have
made them to be highly attractive in a vast array of applications.
Abstract: Sand cast samples of the as-received 66/34Mg-Al alloy were first homogenized at 4900C and then divided into three groups on which annealing, normalising and artificial ageing were respectively carried out. Thermal ageing of the samples involved treatment at 5000C, soaked for 4 hours and quenched in water at ambient temperature followed by tempering at 2000C for 2 hours. Test specimens were subjected to microstructure and mechanical analyses and the results compared. Precipitation of significant volume of stable Mg17Al12 crystals in the aged specimen’s matrix conferred superior mechanical characteristics compared with the annealed, normalized and as-cast specimens. The ultimate tensile strength was 93.4MPa with micro-hardness of 64.9HRC and impact energy (toughness) of 4.05J. In particular, its Young modulus was 10.4GPa which compared well with that of cortical (trabecule) bone’s modulus that varies from 12-17GPa.